Cleaning type low-pressure low-temperature burning solid fuel
A solid fuel, low temperature combustion technology, applied in the direction of solid fuel, fuel, waste fuel, etc., can solve the problem of no public information on solid fuel.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0011] Example 1: Get 15g of potassium nitrate, 280g of ammonium nitrate, and 580g of nitrocellulose in a kneader, mix and stir evenly, and dissolve 110g of glyceryl triacetate, 4g of dimethyldiphenylurea, and diethyldiphenylurea with 220g of ethyl ether, respectively. 6g of phenylurea and 5g of rose essence are mixed uniformly, then mixed with the aforementioned mixture and stirred for 1 hour; the uniformly stirred material is packed into a pressure extruder, and a solid strip with a diameter of 0.8mm is extruded; the strip is aired for 2 Hours later, use a cutting machine to cut the strips into 1-2 mm long granules; then dry the granules in an oven at 55±2°C to obtain nitrocellulose-based solid granules for use.
[0012] Take 12g of hydroxyl-terminated polybutadiene, 3g of ammonium perchlorate, 35g of ammonium nitrate, 50g of nitrocellulose-based solid particles, and 0.45g of toluene diisocyanate, mix and stir evenly; pressurize the mixed material and pour it into a cylindric...
example 2
[0013] Example 2: Get 150g of potassium nitrate, 260g of ammonium nitrate, and 500g of nitrocellulose in a kneader, mix and stir evenly, and dissolve 50g of dibutyl phthalate, 25g of diethyl phthalate, and diethyl phthalate with 220g of ethanol and 220g of acetone. 10 g of methyl diphenylurea and 5 g of essential oil and mix evenly, then mix with the aforementioned mixture and stir for 2 hours; put the uniformly stirred material into a pressure extruder, and extrude a solid strip with a diameter of 1.5 mm; After drying for 3 hours, use a cutting machine to cut the strips into 2-3 mm long particles; then dry the particles in an oven at 57±2°C to obtain nitrocellulose-based solid particles for use.
[0014] Take 16g of hydroxyl-terminated polybutadiene, 50g of ammonium perchlorate, 2g of strontium nitrate, 14g of ammonium nitrate, 20g of nitrocellulose-based solid particles, and 0.8g of toluene diisocyanate, mix and stir evenly; In the forming mold, it is cured at 70±2°C for 4 d...
example 3
[0015] Example 3: Get 60g of potassium nitrate, 280g of ammonium nitrate, and 550g of nitrocellulose in a kneader, mix and stir evenly, and dissolve 100g of dinitrotoluene, 10g of diphenylamine and 4g of lily essence with ether 200g and acetone 210g and mix evenly, then mix with The aforementioned mixture is mixed and stirred for 2 hours; the uniformly stirred material is put into a pressure extruder, and a solid strip with a diameter of 1mm is extruded; after the strip is aired for 2 hours, the strip is cut into a length of 2-3mm by a cutting machine granules; then dry the granules and transfer them to an oven for drying at 56±2°C to obtain nitrocellulose-based solid granules for use.
[0016] Take 10g of hydroxyl-terminated polybutadiene, 10g of ammonium perchlorate, 1g of strontium nitrate, 1g of rosin, 40g of ammonium nitrate, 40g of nitrocellulose-based solid particles, and 0.5 toluene diisocyanate, mix and stir evenly; pressurize the mixture and pour it into a cylinder S...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com