Plastic nail

A technology of plastics and raw materials, applied in the direction of nails, staples, connecting components, etc., can solve the problems of not mentioning plastic row nails, the performance of plastic nails cannot meet the requirements of row nails, and plastics are incompetent, and achieve light weight. , high strength, simple molding effect

Inactive Publication Date: 2010-07-21
NANJING HONGRUI PLASTIC PROD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent application number 95113087.0 discloses a plastic alloy nail and a plastic bolt, which are used to replace ordinary iron nails, but the above-mentioned patents do not mention the production of plastic row nails, and the performance of the plastic nails cannot reach that of row nails. Require
Rack nails have higher requirements on the strength and rigidity of the material than ordinary nails, and ordinary plastics are not up to the task

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Component parts by weight ratio:

[0016] Nylon 650

[0017] Fiberglass 47

[0018] Talc powder 3

[0019] Y-(2,3-epoxypropoxy)propyltrimethoxysilane 0.4

[0020] Isopropyl tris (dioctyl pyrophosphate acyloxy) titanate 0.1

[0021] Tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester 0.2

[0022] Tris(2,4-di-tert-butylphenyl)phosphite 0.2

[0023] Silicone powder 1

[0024] 1) taking the above-mentioned various raw materials according to the ratio in parts by weight;

[0025] 2) Mix the above-mentioned raw materials in a mixer for 10 minutes;

[0026] 3) Put the mixed material into the twin-screw extruder, the glass fiber is added from the glass fiber inlet on the extruder, and then melted and extruded to granulate. The production process conditions are: temperature in zone 1-2 of the twin-screw extruder 240°C, 250°C for zone 3-4, 250°C for zone 5-6, 255°C for zone 7-8, 230°C for the head, and 300 rpm for the screw;

[0027] 4) Aft...

Embodiment 2

[0029] Component parts by weight ratio:

[0030] Nylon 66 60

[0031] Fiberglass 30

[0032] calcium carbonate 10

[0033] Y-(2,3-epoxypropoxy)propyltrimethoxysilane 0.2

[0034] Isopropyl tris (dioctyl pyrophosphate acyloxy) titanate 0.2

[0035] N,N'-hexamethylenebis(3,5-di-tert-butyl-4-hydroxyphenylpropanamide) 0.3

[0036] Tris(2,4-di-tert-butylphenyl)phosphite 0.3

[0037] Calcium stearate 1.5

[0038] 1) taking the above-mentioned various raw materials according to the ratio in parts by weight;

[0039] 2) Mix the above-mentioned raw materials in a mixer for 10 minutes;

[0040] 3) Put the mixed material into the twin-screw extruder, the glass fiber is added from the glass fiber inlet on the extruder, and then melted and extruded to granulate. The production process conditions are: temperature in zone 1-2 of the twin-screw extruder The temperature is 240°C, the temperature in zone 3-4 is 255°C, the temperature in zone 5-6 is 265°C, the temperature in zone 7-8 is ...

Embodiment 3

[0043] Component parts by weight ratio:

[0044] Nylon 610 60

[0045] Fiberglass 35

[0046] mica 5

[0047] Y-(2,3-epoxypropoxy)propyltrimethoxysilane 0.3

[0048] Isopropyl tris (dioctyl pyrophosphate acyloxy) titanate 0.1

[0049] Tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester 0.3

[0050] Tris(2,4-di-tert-butylphenyl)phosphite 0.3

[0051] N,N'-Ethylenebisstearamide 1

[0052] Operation process is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a plastic chain riveting, the raw materials of which are calculated by weight: 40-60 portions of nylon, 40-60 portions of glass fiber, 0-10 portions of mineral powder, 0.1-0.5 portion of coupling agent, 0.1-0.5 portion of antioxidant, and 0.3-2 portions of lubricant. The plastic chain riveting made by the invention is characterized by long service life without treatment and comparatively long-term high strength and high rigidity maintenance, which is applicable to common electrical or air staple guns, with good comprehensive mechanical property, strong corrosion resistance, light mass and simple forming of products, and grinding and shaving can be done during usage, thus various components with complex shapes can be easily machined.

Description

technical field [0001] The invention relates to a nail row, in particular to a plastic nail row used by an electric or pneumatic nail gun. Background technique [0002] In modern construction and manufacturing, a large number of nails are required for fastening. In order to meet the requirements of high-speed development and automation, electric or pneumatic tools are used in more and more places, and row nails have gradually replaced traditional nails. But most of the row nails used at present are to adopt galvanized iron nails, which have many defects such as easy to get rusty, short life, and troublesome manufacture. Replacing steel with plastic is a trend in the future development of fasteners. Chinese Patent Application No. 93112495.6 discloses a method for making plastic nails from glass fiber-reinforced thermoplastic resin materials. Chinese patent application number 95113087.0 discloses a plastic alloy nail and a plastic bolt, which are used to replace ordinary iro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/00C08K13/04C08K7/14F16B15/08
Inventor 张明张静志李志嘉
Owner NANJING HONGRUI PLASTIC PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap