Waterborne anti-rust heat insulating coating

A heat-insulating coating, water-based technology, applied in the direction of anti-corrosion coatings, fire-proof coatings, coatings, etc., can solve the problems of less dense film-forming material structure, poor light and heat resistance of inorganic substances, high content of organic solvents, etc., to achieve rust prevention Good heat insulation effect, low cost, easy coating effect

Inactive Publication Date: 2008-11-05
胡月祖
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main reason is that the content of organic solvent is high; or the structure of the film-forming material is not too dense, and the aging resistance is poor; or the light and heat resistance of inorganic substances is poor, the heat insulation method is single, and the heat insulation effect is poor, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1 (unit: kilogram; Total amount: 100 kilograms)

[0011] Soft water: balance, hydroxyethyl cellulose 0.2, preservative 0.1, antifungal agent 0.4, amine salt dispersant 0.43, low foam wetting agent 0.05, defoamer 0.26, ethylene glycol 2, heavy calcium 5, talcum powder 3 , titanium dioxide 18, organic amine: appropriate amount, calcined kaolin 4, silicon acrylic emulsion above Tg35°C 35, lauryl alcohol ester 1.8, hollow sodium silicate particles with an average particle size of about 10-30um 5, thickener: appropriate amount, Wollastonite powder 6, adjust PH10-PH11.

Embodiment 2

[0012] Embodiment 2 (unit: kilogram; Total amount: 100 kilograms)

[0013] Soft water: balance, hydroxyethyl cellulose 0.18, preservative 0.13, antifungal agent 0.35, amine salt dispersant 0.46, low foam wetting agent 0.05, defoamer 0.28, ethylene glycol 3, heavy calcium 6, talc 3 , titanium dioxide 20, organic amine: appropriate amount, calcined kaolin 3, silicon acrylic emulsion with Tg above 35°C 38, lauryl alcohol ester 2, hollow sodium silicate particles with an average particle size of about 10-30um 6, thickener: appropriate amount, Wollastonite powder 7, adjust PH10-PH11.

Embodiment 3

[0014] Embodiment 3 (unit: kilogram; Total amount: 100 kilograms)

[0015] Soft water: balance, hydroxyethyl cellulose 0.23, preservative 0.13, antifungal agent 0.48, amine salt dispersant 0.47, low foam wetting agent 0.04, defoamer 0.3, ethylene glycol 1.8, heavy calcium 3, talcum powder 3 , titanium dioxide 18, organic amine: appropriate amount, calcined kaolin 3, silicon acrylic emulsion above Tg35°C 40, lauryl alcohol ester 2, hollow sodium silicate particles with an average particle size of about 10-30um 7, thickener: appropriate amount, Wollastonite powder 5, adjust PH10-PH11.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based anti-rust and heat insulation coating which is characterized in that the coating mainly consists of materials with following weight percentage: 10-30 percent of soft water, 0.1-0.3 percent of hydroxyethyl cellulose, 0.1-0.2 percent of preservative, 0.2-0.4 percent of anti-mildew agent, 0.2-0.5 percent of amine salt dispersant, 0.02-0.1 percent of low foam wetting agent, 0.1-0.3 percent of defoamer, 1-4 percent of glycol, 3-13 percent of coarse whiting, 3-20 percent of saponite, 18-25 percent of titanium pigment, 0.1-0.6 percent of organic amine, 3-6 percent of calcined kaolin, 28-43 percent of silicone-acrylate emulsion above Tg 35 DEG C, 1.3-2.8 percent of lauryl alcohol ester, 3-13 percent of hollow sodium silicate particle with the average grain size of about 10 to 30 Mum, 0.1-0.6 percent of thickener, 3-12 percent of wollastonite powder, and adjusting pH 10-pH 11. The invention is used for iron roofs and exterior walls etc., and has the advantages of good anti-rust and heat insulation effect, good durability, being easy for storage and coating, low cost and water environmental protection.

Description

technical field [0001] The invention relates to a water-based coating, in particular to a water-based anti-rust and heat-insulating coating with good anti-rust and heat-insulating effect, good durability, easy storage and easy coating for iron roofs and exterior walls. Background technique [0002] At present, the coatings used for iron roofs and exterior walls are oil-based coatings or ordinary water-based architectural coatings. Oil-based coatings are not environmentally friendly, difficult to coat, high in cost, and not very good in heat insulation; while ordinary water-based architectural coatings are anti-rust and heat-insulating The effect is not very good, and the durability is not very good. Generally speaking, lack a kind of coating that is used for coating such as iron sheet roof, exterior wall better comprehensive performance. The main reason is that the content of organic solvent is high; or the structure of the film-forming material is not too dense, and the ag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D5/02C09D5/08C09D5/18C09D101/26
Inventor 胡月祖
Owner 胡月祖
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products