Calcium sulphate crystal whisker preparation method with sea water bittern as raw material

A technology of calcium sulfate whiskers and brine, applied in chemical instruments and methods, calcium/strontium/barium sulfate, single crystal growth, etc., can solve the problems of not forming a more suitable preparation method and process technology, and achieve easy industrialization , increase added value, reduce consumption effect

Active Publication Date: 2008-12-10
TIANJIN SEA WATER DESALINATION & COMPLEX UTILIZATION INST STATE OCEANOGRAPHI
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main component of salt gypsum is calcium sulfate dihydrate (CaSO4 2H2O), which can be used as a raw material for producing calcium sulfate whiskers. For this reason, the research and experiment of using salt gypsum to produce calcium sulfate whiskers are in progress, but still There is no more suitable preparation method and process technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Take 10 liters of concentrated seawater with a specific gravity of 6.50Be', containing Ca2+0.63 g / L, Mg2+2.38 g / L, SO42-4.49 g / L and Cl-34.41 g / L, and put it into an evaporative crystallizer for evaporation and concentration. The feed liquid was concentrated to 230Be' to stop evaporation. There are 22 grams of calcium sulfate dihydrate and 2200 milliliters of mother liquor in the evaporation and crystallization completion liquid.

[0028] Transfer 22 grams of calcium sulfate dihydrate and 300 milliliters of mother liquor in the evaporated and crystallized liquid into a pressure reactor by means of precipitation separation. While stirring at a speed of 80 rpm, heat and maintain a temperature of 120°C and a pressure of 0.2 MPa, the reaction time is 2 hours.

[0029] After the reaction is completed, the reaction completed liquid is filtered, and the filtered solid-phase calcium sulfate hemihydrate whiskers are separated from the mother liquor. Then the calcium sulfate he...

Embodiment 2

[0032] Take 10 liters of concentrated seawater with a specific gravity of 6.50Be', containing Ca2+0.63 g / L, Mg2+2.38 g / L, SO42-4.49 g / L and Cl-34.41 g / L, and put it into an evaporative crystallizer for evaporation and concentration. The feed liquid was concentrated to 230Be' to stop evaporation. There are 21 grams of calcium sulfate dihydrate and 2230 milliliters of mother liquor in the evaporation and crystallization completion liquid.

[0033] Transfer 21 grams of calcium sulfate dihydrate and 380 milliliters of mother liquor in the evaporated and crystallized liquid into a pressure reactor by means of precipitation separation. While stirring at a speed of 200 rpm, heat and keep the temperature at 200°C and the pressure is 0.5MPa, and the reaction time is 0.5 hours.

[0034] After the reaction is completed, the reaction completed liquid is filtered, and the filtered solid-phase calcium sulfate hemihydrate whiskers are separated from the mother liquor. Then the calcium sulf...

Embodiment 3

[0037] Take 10 liters of seawater brine with a specific gravity of 9.80Be', containing Ca2+0.95 g / L, Mg2+3.60 g / L, SO42-6.75 g / L and Cl-51.85 g / L, put it into an evaporative crystallizer for evaporation and concentration, The feed liquid was concentrated to 220Be' to stop evaporation. There are 33 grams of calcium sulfate dihydrate and 3350 milliliters of mother liquor in the evaporation and crystallization completion liquid.

[0038] Transfer 33 grams of calcium sulfate dihydrate and 450 milliliters of mother liquor in the evaporated and crystallized liquid into a pressure reactor by means of precipitation separation. While stirring at a speed of 100 rpm, heat and maintain a temperature of 120°C and a pressure of 0.5MPa, the reaction time is 0.5 hours.

[0039] After the reaction is completed, the reaction completed liquid is filtered, and the filtered solid-phase calcium sulfate hemihydrate whiskers are separated from the mother liquor, then the solid-phase calcium sulfate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing calcium sulphate crystal whisker. The method takes sea water and bittern as raw materials, combines the comprehensive utilization of the sea water, lowers the cost, simplifies the process and is easy to realize the industrialization. The method comprises the following processes of evaporating crystallization, crystal whisker conversion, filtration and washing and salting-out evaporation. The concentrated sea water after desalted or the moderate bittern in the salt manufacturing process is put in an evaporated crystallizer to be evaporated and concentrated so that the granular calcium sulphate crystal is separated out; the calcium sulphate crystal and a feed liquid prepared by the mother solution after the evaporation according to the solid / liquid mixture ratio of between 5 and 10 percent are put in a reaction kettle to translate into the calcium sulphate crystal whisker, the reaction temperature is between 100 and 200 DEG C, the reaction pressure is between 0.1 and 0.5 MPa, and the reaction time lasts for 0.5 to 2 hours; the calcium sulphate crystal whisker is filtered, washed and dried so that the calcium sulphate crystal whisker product is prepared; and the remaining mother solution obtained by filtering the crystal whisker converting reaction liquid is evaporated and concentrated further to separate out the sodium chloride crystal.

Description

technical field [0001] The invention relates to the production technology of inorganic salt whiskers, in particular to the production technology of calcium sulfate whisker materials. Background technique [0002] Calcium sulfate whisker refers to anhydrous calcium sulfate (CaSO4) fibrous single crystal, with an average aspect ratio of 50-80, complete crystal structure, stable size, specific cross-section, strength and modulus close to the theoretical value of crystal materials. Calcium sulfate whiskers have excellent physical, chemical and mechanical properties such as high temperature resistance, acid and alkali resistance, chemical corrosion resistance, good electrical insulation, high strength, good toughness and compatibility, and easy surface treatment. The material is widely used in the manufacture of plastics, rubber, adhesives, friction materials, coatings, paints, heat insulation materials, lightweight building materials, etc., and is a low-cost green environmental ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C30B29/22C30B29/62C01F11/46
Inventor 张家凯张雨山曹冬梅王玉琪刘骆峰
Owner TIANJIN SEA WATER DESALINATION & COMPLEX UTILIZATION INST STATE OCEANOGRAPHI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com