Urethane elastomer combined material for automobile foot pad and preparation thereof

A technology of polyurethane elastomer and automobile, which is applied in the special position of the vehicle, vehicle parts, transportation and packaging, etc., and can solve the problems of high mold requirements, long production cycle, and single appearance

Active Publication Date: 2009-01-28
SHANDONG INOV POLYURETHANE
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to use the polyurethane composite material on the car floor mat, which solves the problems of long production cycle, single appearance and high requirements on the mold of the conventional rubber products, thereby providing a car floor mat Polyurethane elastomer composite material used and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Prepare 207 grams of component A material, weighing respectively: 90 grams of polyether polyol (MN3050), 17 grams of expansion agent (ethylene glycol), 75 grams of filler (400 mesh talcum powder), plasticizer (phthalate Dioctyl formate) 20 grams, flame retardant (TCPP) 1 gram, catalyst (zinc naphthenate) 0.5 grams, antioxidant 2,6-di-tert-butyl p-cresol: 2.5 grams, color paste (carbon black) 1 gram, first put the weighed polyether polyol into the beaker and stir, then add the weighed crosslinking agent, filler, plasticizer, flame retardant, anti-aging agent, catalyst, color paste (wherein the catalyst , The color paste can be added separately in proportion to the production), the temperature is controlled at 70°C-90°C, and the vacuum (-0.096Mpa) is dehydrated until the moisture content is qualified (≤0.05%).

[0028] Prepare 165 grams of component B material, add 100 grams of polyether polyol DL-4000 (2 functionality, molecular weight 4000) into a three-necked bottle at...

Embodiment 2

[0031] Prepare 215 grams of component A material, weigh respectively: 100 grams of polyether polyol (330N), 15 grams of linking agent (1,4-butanediol), 85 grams of filler (325 mesh light calcium carbonate), add Plasticizer (dioctyl phthalate) 10 grams, flame retardant (TCPP) 1 gram, catalyst (zinc naphthenate) 0.5 grams, anti-aging agent (2,6-di-tert-butyl p-cresol) 2.5 grams , 1 gram of color paste (carbon black), first put the weighed polyether polyol into the beaker and stir, then add the weighed crosslinking agent, filler, plasticizer, flame retardant, antioxidant ( 2,6-di-tert-butyl-p-cresol), catalyst, color paste (the catalyst and color paste can be added separately in proportion to production), vacuum dehydration at 70-90 degrees, and the water content is qualified (≤0.05%).

[0032] Prepare 165 grams of component B material, add 100 grams of polyether polyol DL-3000 (2 functionality, molecular weight 3000) into a three-necked bottle at room temperature, stir at 80°C-1...

Embodiment 3

[0035] Prepare 310 grams of component A material, weighing respectively: polyether polyol (MN-3050) 80 grams, crosslinking agent (propylene glycol) 20 grams, filler (400 mesh clay) 185 grams, plasticizer (chlorinated paraffin) 20 grams, 1 gram of flame retardant (TCEP), 0.5 grams of catalyst (zinc naphthenate), 2,6-di-tert-butyl-p-cresol: 2.5 grams of anti-aging agent, 1 gram of color paste (iron oxide red), will First put the weighed polyether polyol into the beaker and stir, then add the weighed crosslinking agent, filler, plasticizer, flame retardant, auxiliary agent, catalyst, color paste (wherein the catalyst, color paste can be It is added separately in proportion during production), vacuum dehydrated at 70-90 degrees, and the moisture is qualified (≤0.05%).

[0036] Prepare 170 grams of component B material, add 100 grams of polyether polyol (2 functionality, molecular weight 4000) into a three-necked bottle at room temperature, stir at 80°C-100°C, vacuum dehydrate and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a combined material of a PU elastomer used for a vehicle foot pad and a preparation method thereof. The combined material of a PU elastomer consists of a component A and a component B, wherein, the component A consists of PPG, a chain extender, fillings, a plasticizer, a flame retardant, an age inhibitor, a catalyst and color paste; the component B is the reaction product of PPG and isocyanate. When in use, the component A and the component B are mixed according to a weight ratio that A: B is equal to 100: 30 to 65, thus being capable of manufacturing the PU elastomer used for a vehicle foot pad. The combined material of the PU elastomer used for the vehicle foot pad and the preparation method thereof have the advantages that the technique flow is simple, the period is short, the cost value is high and the color of the product can be randomly adjusted when the product is manufactured, thus being completely capable of meeting each performance demand on the vehicle foot pad.

Description

Technical field: [0001] The invention belongs to the technical field of the preparation method of polyurethane elastomer composite material. Background technique: [0002] At present, with the rapid development of the automobile manufacturing industry, the demand for automobile floor mats is also rising rapidly, and the requirements for comfort, wear resistance, and economy are also getting higher and higher. With its superior performance, the production and application range of polyurethane materials are rapidly expanding and popularizing, and they have played an increasingly important role in various fields of the national economy. In recent years, many automobile manufacturers and parts manufacturers have higher requirements for the comfort of the floor mats, especially the appearance. The original automobile floor mats are mostly rubber products. The production of rubber products requires high pressure, cumbersome processes, and long cycles. Its color is not easy to adj...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G18/66C08G18/10C08L75/08C08K13/02B60N3/06
Inventor 李健孙清峰鞠伟坦栾森于鹏程
Owner SHANDONG INOV POLYURETHANE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com