Colored profiled polyester multifilament fiber with stable dimension and preparation method thereof

A dimensionally stable, polyester multifilament technology, applied in the fiber field, can solve the problems of no fiber preparation, poor surface gloss, low coverage, etc., and achieve small creep and relaxation phenomenon, clean surface, and low boiling water shrinkage. Effect

Active Publication Date: 2011-11-16
ZHEJIANG JINXIA NEW MATERIAL TECH CO LTD
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN1211204C discloses a production method of PET / PEN blended or copolymerized film but does not involve the preparation of fibers
At present, the more common fibers in the market generally have a circular cross-sectional shape, poor surface gloss, waxy feel, and there are disadvantages such as easy to dirty, easy to pilling, non-absorbent, and small coverage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colored profiled polyester multifilament fiber with stable dimension and preparation method thereof
  • Colored profiled polyester multifilament fiber with stable dimension and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The selected ratio is 91.7 parts of polyethylene terephthalate (PET) spinning chips, Jinshan Petrochemical provides molecular weight of 20000, 1 part of color masterbatch, Tongxiang Masterbatch Factory HC800, 7 parts of poly 2,6-naphthalene dicarboxylic acid dicarboxylate Ethyl ester (PEN) chips DuPont PENQ3000, and 0.3 parts of barium sulfate powder, Yufeng Powder Material Co., Ltd. ultrafine barium sulfate YF ~ 10000. Spinning slices of polyethylene terephthalate and polyethylene 2,6-diethyl naphthalate are sliced ​​in a VC358 rotary pan, first vacuumed to within 30 Pa and then heated to 120°C for 8 hours to dry and dehydrate. Keep the water content below 35PPM for 8 hours. Polyester chips and color masterbatch are extruded, blended and melted by a screw machine in a VC406 spinning machine to form a melt, and then spun through a spinneret assembly. The extruded temperature of the screw machine is: 275°C in the first zone, The second zone is 285°C, the third zone is 2...

Embodiment 2

[0041] The selected proportion is 93.9 parts of polyethylene terephthalate (PET) spinning chip, Jinshan Petrochemical provides molecular weight 20000, color masterbatch 0.6 part, Changzhou TR27. 5 parts of polyethylene 2,6-diethyl naphthalate ( PEN) sliced ​​DuPont PENQ3000, and 0.5 parts of barium sulfate powder, ultrafine barium sulfate YF~10000 from Yufeng Powder Materials Co., Ltd. Spinning slices of polyethylene terephthalate and polyethylene 2,6-diethyl naphthalate slices are placed in a VC358 rotary pan, first vacuumed to within 30 Pa, then heated to 140°C for 10 hours to dry and dehydrate, and keep warm 8 hours water content below 35PPM. Polyester chips and color masterbatch are extruded, blended and melted by a screw machine in a VC406 spinning machine to form a melt, and then spun through a spinneret assembly. The extruded temperature of the screw machine is: 280°C in the first zone The second zone is 285°C, the third zone is 285°C, the fourth zone is 290°C, the fif...

Embodiment 3

[0043] The selected ratio is 95.8 parts of polyethylene terephthalate (PET) spinning chip, Jinshan Petrochemical provides molecular weight of 20000, 4 parts of color masterbatch, Lihe Lihe Chemical Fiber Plastic Factory T1614. 0 parts of poly-2,6-naphthalene Diethyl diformate (PEN) chips and 0.2 parts of barium sulfate powder, Yufeng Powder Material Co., Ltd. ultrafine barium sulfate YF ~ 10000. Spinning chip polyethylene terephthalate chips are placed in a VC358 rotary pot, first vacuumed to within 30 Pa, then heated to 140°C for 9 hours for drying and dehydration, and kept for 10 hours to keep the water content below 35PPM. The water content is below 35PPM; the polyester chip and the color masterbatch are extruded, blended and melted by the screw machine in the VC406 spinning machine to form a melt, which is spun through the spinneret assembly, and the temperature extruded by the screw machine is : Zone 1 270°C, Zone 2 280°C, Zone 3 285°C, Zone 4 280°C, Zone 5 280°C, Zone 6 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water contentaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a colored profiled polyester multifilament fiber with stable dimension and a preparation method thereof. The preparation method comprises the following steps: adjusting contents of polyester, pigment masterbatch and an additive in a fusant according to a certain proportion, drying and dehydrating, forming after melting, extrusion, spinning and cooling, and obtaining finished filament after oiling, coiling, heating, tensioning, heat setting, inspection and grading. The fiber can be prepared with conventional spinning equipment, has even multifilament bundle yarn and even color distribution, can be widely applied to fields of clothing, decoration and industry. Fabric is smooth, is characterized by soft luster, high breaking strength and low breaking elongation, can ensure stable geometric dimension of the fabric without easy deformation; and the fiber has the advantages of good fabric elastic resilience, less creep and relaxation and low boiling water shrinkage,and can improve the stability due to hard deformation at high temperature.

Description

【Technical field】 [0001] The invention relates to the field of fiber technology, in particular to a non-colored and dimensionally stable polyester multifilament fiber applied to civilian textiles and a preparation method thereof. 【Background technique】 [0002] Since the advent of polyester in the 1950s, great progress has been made in the development of industrial applications. Due to its low heat shrinkage, polyester industrial yarn is widely used in the field of narrow-width fabrics such as filter cloth, sunshade cloth, tarpaulin, etc. The dry heat shrinkage of traditional low-shrinkage polyester industrial yarn is about 2 % or so, the polyester industrial yarn with this level of dry heat shrinkage is woven into cloth. After the coating heat treatment, the cloth surface shrinkage rate is large, the shrinkage is uneven, and the cloth surface is easy to cause unevenness, so it can only be used for narrow fabrics. Weaving. In recent years, due to the rapid development of m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F8/14D01D5/08D01D5/088D01D5/096D01D5/253
Inventor 张志明陈龙
Owner ZHEJIANG JINXIA NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com