Meteorologic balloon and production method thereof

A technology of weather balloons and production methods, applied to balloon aircraft, other household appliances, applications, etc., to achieve the effects of improving overall processing performance, increasing uniformity, and increasing explosion diameter

Active Publication Date: 2011-05-18
CHEMCHINA ZHUZHOU RUBBER RES & DESIGN INST
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The prior art balloons have been using the old formula and old technology of the 1970s. The original weather balloon formula is: 100 parts of centrifugally concentrated natural latex, 0.30 parts of potassium hydroxide, 0.15 parts of casein, 1.00 parts of sulfur, 1.00 parts of anti-D, 4010NA1 .00 parts, pro-PX 1.50 parts, zinc oxide 0.20 parts, machine oil 7.00 parts, not adjusted according to changes in raw materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The production method of above-mentioned weather balloon, its raw material is made up of solid raw material, oily raw material, colloidal raw material, and the composition and weight ratio of described solid raw material are: 100 parts of centrifugal concentrated natural latex, 0.30 part of potassium hydroxide, 0.15 part of casein 0.10 parts, flat plus O 0.10 parts, 3 parts of sulfur, 2 parts of anti-D, 2 parts of 4010NA, 3 parts of PX, 5 parts of zinc oxide, the oily raw material is mechanical oil, and the weight ratio is 10.0 parts, and the colloidal raw material is chloroprene latex , The addition of chloroprene latex is 1: 10 to add by the mixture of solid raw material and oily raw material and neoprene latex mixing weight ratio.

[0023] The raw material preparation method is as follows: firstly, various water-insoluble solid powder raw materials are made into water dispersions, water-soluble solid powder raw materials are prepared into solutions, oily raw materials...

Embodiment 2

[0026] A kind of production method of weather balloon, its raw material is made up of solid raw material, oily raw material, colloidal raw material, and the composition and weight ratio of described solid raw material are: the composition of solid raw material and weight ratio are: 100 parts of centrifugally concentrated natural rubber latex , 0.20 parts of potassium hydroxide, 0.15 parts of casein, 0.05 parts of Pingpingjiao, 1.00 parts of sulfur, 2.00 parts of anti-D, 2 parts of 4010NA, 2.50 parts of PX, 0.5 parts of zinc oxide, oily raw materials are machine oils, weight ratio For 7.00 parts, the colloidal raw material is neoprene latex, and the addition of neoprene latex is 1: 10 to add by the mixture of solid raw material and oily raw material and neoprene latex mixing weight ratio. The raw material preparation method is as follows: firstly, various water-insoluble solid powder raw materials are made into water dispersions, water-soluble solid powder raw materials are prep...

Embodiment 3

[0030] A kind of production method of weather balloon, its raw material is made up of solid raw material, oily raw material, colloidal raw material, and the composition and weight ratio of described solid raw material are: 100 parts of centrifugal concentrated natural latex, 0~0.10 part of Pingpingjiao, 1.0 parts of sulfur, 1.00 parts of anti-D, 1.00 parts of 4010NA, 1.50 parts of PX, 0.20 parts of zinc oxide, the oily raw material is mechanical oil, and the weight ratio is 7.00 parts, and the rubbery raw material is neoprene latex. The addition amount is added according to the mixture weight ratio of solid raw material and oily raw material and neoprene latex as 1:10.

[0031]The raw material preparation method is as follows: firstly, various water-insoluble solid powder raw materials are made into water dispersions, water-soluble solid powder raw materials are prepared into solutions, oily raw materials are prepared into emulsions, and then the obtained water dispersions and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
massaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a meteorological balloon and a production method thereof. The meteorological balloon has the quality of 700g to 800g, the length of a balloon body is 205 cm to 255 cm, and a balloon handle has a width of 9 cm to 10 cm and a length of 10 cm to 14 cm. The meteorological balloon comprises a solid raw material, an oil raw material and a colloid raw material, wherein the solid raw material comprises the ingredients by weight ratio: 100 parts of centrifugal concentrated natural latex, 0 part to 0.30 part of potassium hydroxide, 0 part to 0.15 part of casein, 0 part to 0.10 part of leveling agent O, 1.00 part to 3 parts of sulfur, 1.00 part to 2 parts of antioxidant D, 1.00 part to 2 parts of 4010NA, 1.50 parts to 3 parts of rubber accelerator PX and 0.20 part to 5 parts of zinc oxide; the oil raw material comprises 7.00 parts to 10.0 parts of mechanical oil by weight ratio; and the colloid raw material comprises neoprene latex which is added by the mixed weight ratio of the mixture of the solid raw material and the oil raw material to the neoprene latex, namely 1 to 10. The neoprene latex is added in a raw material formulation so as to improve the anti-aging performance and the whole processing performance of the meteorological balloon, ensure the streamlined appearance of the meteorological balloon, improve the evenness degree of a balloon surface and enable the balloon surface to swell evenly in the discharge process.

Description

technical field [0001] The invention relates to a vehicle for detecting air weather and a production method thereof, in particular to a weather balloon and a production method thereof. Background technique [0002] Meteorological balloons are a vehicle commonly used to detect meteorological elements in the air. It is not only used by meteorological departments to detect meteorological elements and provide meteorological support conditions, but also is an indispensable meteorological test method for troops to perform national defense scientific research and military operations such as aerospace, aviation, navigation, and combat. In recent years, due to the rapid development of industry, great changes in the geographical environment, and global warming, many changes have taken place in meteorological elements in various places. Weather balloons should adapt to the changing and complex meteorological elements in the atmosphere. With the development of science and technology, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29D22/02B64B1/40C08L7/02C08L11/02B29K7/00B29K409/00
Inventor 肖迪娥
Owner CHEMCHINA ZHUZHOU RUBBER RES & DESIGN INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com