A kind of zirconia ceramic matrix composite material and its preparation method

A technology for zirconia ceramics and composite materials, which is applied in the field of zirconia ceramic matrix composites and their preparation, can solve the problems of reducing the high temperature performance and chemical stability of ceramics, high cost, and low toughness of ceramic materials, and achieves low oxidation resistance. , Broaden the scope of application, excellent effect of high temperature mechanics

Inactive Publication Date: 2011-12-14
UNIV OF JINAN
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still many shortcomings in various toughening and reinforcing methods at present. For example, metal reinforcement will reduce the high-temperature performance and chemical stability of ceramics; fiber and whisker toughening have problems such as difficult dispersion, high cost, and unstable performance.
In addition to the low toughness of ceramic materials, the disadvantages of difficult processing and high cost are also the reasons that restrict the large-scale application of structural ceramics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of zirconia ceramic matrix composite material and its preparation method
  • A kind of zirconia ceramic matrix composite material and its preparation method
  • A kind of zirconia ceramic matrix composite material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Nb powder, Ti powder, and Cr powder with a particle size of 2000 to 8000nm and a purity of ≥99.0% are mixed according to the ratio of Nb:Ti:Cr=50:37:23, and ball milled under a nitrogen atmosphere. The ball milling time is 20 ~60h, the mill speed is 360r / min, after ball milling, the toughening phase powder with a particle size of 200~500nm is obtained;

[0031] (2) ZrO with a particle size of 10-40nm 2 (3Y) powder and toughening phase powder are mixed according to the volume ratio of 30:70, using QM-1SP2 planetary high-energy ball mill, nickel-chromium stainless steel vacuum ball milling tank and carbide balls, and ball milling under nitrogen atmosphere , the ball milling time is 1h, and the mill speed is 100r / min;

[0032] (3) The mixed powder is hot-pressed and sintered in a multifunctional sintering furnace with a heating rate of 50°C / min and a vacuum degree of 3×10 -3 Pa. The sample was degassed at 500°C for 30 minutes. The sintering temperature is 1250-1450...

Embodiment 2

[0034] (1) Nb powder, Ti powder, and Cr powder with a particle size of 2000 to 8000nm and a purity of ≥99.0% are mixed according to the ratio of Nb:Ti:Cr=50:37:23, and ball milled under a nitrogen atmosphere. The ball milling time is 20 ~60h, the mill speed is 360r / min, after ball milling, the toughening phase powder with a particle size of 200~500nm is obtained;

[0035] (2) ZrO 2 (3Y) powder and toughening phase powder are mixed according to the volume ratio of 40:60, using QM-1SP2 planetary high-energy ball mill, nickel-chromium stainless steel vacuum ball milling tank and carbide balls, and ball milling under nitrogen atmosphere , the ball milling time is 0.5h, and the mill speed is 100r / min;

[0036] (3) The mixed powder is hot-pressed and sintered in a multifunctional sintering furnace with a heating rate of 25°C / min and a vacuum of 3×10 -3 Pa. The sample was degassed at 500°C for 30 minutes. The sintering temperature is 1250-1450° C., the holding time is 60 minutes,...

Embodiment 3

[0038] ZrO 2 (3Y) The powder is mixed with the toughening phase powder at a volume ratio of 50:50, and the other operations are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a zirconia ceramic matrix composite material and a preparation method thereof. The composite material is made of tetragonal zirconia as a matrix, and the Nb-Ti-Cr phase is used as a toughening phase; the volume fractions of the matrix and the toughening phase are respectively 20 to 80%, and the sum of the two volume fractions is 100%. %. The Nb powder, Ti powder and Cr powder are mixed according to the ratio of the amount of Nb, Ti and Cr atoms being 50:37:23. The preparation method is that the base body and the toughening phase are mixed after ball milling, and then sintered by vacuum hot pressing. The composite material of the present invention has more excellent high-temperature mechanics, oxidation resistance and low cost; compared with fiber whisker toughened ceramics, the toughening effect is close, but the preparation process is simple, the cost is low, and the electrical conductivity is far superior to the former .

Description

technical field [0001] The invention relates to a zirconia ceramic-based composite material and a preparation method thereof, belonging to the technical field of zirconia-based ceramic materials. Background technique [0002] Tetragonal zirconia (TZP) ceramics is a material with the highest room temperature mechanical properties among ceramic materials. In addition to the inherent brittleness of ceramic materials, the strength and toughness of TZP materials decrease sharply with the increase of temperature. In addition, the disadvantages of low-temperature aging and poor thermal shock resistance have greatly weakened its competitive advantage and limited its scale development and application. The intrinsic brittleness of ceramics determines that the toughening of ceramic materials has become a core issue in ceramic research. At present, the toughening methods of ceramics mainly include phase transformation toughening, fiber (whisker) toughening, particle toughening and compo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/48C04B35/71C04B35/622
Inventor 李嘉温雨师瑞霞孙富升张宗见
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More