Heavy metal-polluted soil masonry and preparation method thereof

A technology that pollutes soil and heavy metals, applied in building components, buildings, building structures, etc., to achieve the effects of simple mechanical equipment, low price, and easy transportation

Inactive Publication Date: 2012-05-02
HANGZHOU DIANZI UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a masonry technology for heavy metal contaminated soil and a preparation method for the masonry, aiming at the deficiencies in the existing restoration and utilization technology of heavy metal heavily polluted soil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Take 2kg of polluted soil (0-20cm topsoil, soil pH value 5.51, organic matter content 21.8g / kg, total lead 19592mg / kg, total zinc 647mg / kg, total cadmium 14.65mg / kg, Total copper 287mg / kg), air-dried, passed through a 2mm sieve, picked out non-soil impurities, mixed and took 700g of soil for later use. Will 779.8g 325 # Portland cement is thoroughly mixed with 700g of soil as the base material. Weigh 0.2g of calcium dihydrogen phosphate, dissolve it in 420ml of water, pour 520g of sodium bentonite into the phosphate mixture, stir evenly, and use it as an additive. Then mix the base material and additives, add 430ml of water, stir well and pour it into the test mold to make two test pieces, adopt the standard curing method for 24 hours, remove the mold, and then cure in the curing room for 28 days. The indoor temperature was 17° C. and the humidity was 90%. The measured compressive strength of the finished masonry products is 7.84MPa and 7.19MPa, and the contaminated ...

Embodiment 2

[0021] Take 2kg of polluted soil (0-20cm topsoil, soil pH value 5.51, organic matter content 21.8g / kg, total lead 19592mg / kg, total zinc 647mg / kg, total cadmium 14.65mg / kg, Total copper 287mg / kg), air-dried, passed through a 2mm sieve, sorted out non-soil impurities, mixed and got 1200g soil for later use. Will 560g 325 # Portland cement is thoroughly mixed with 1200g soil as the base material. Weigh 1g of calcium dihydrogen phosphate, dissolve it in 420ml of water, pour 239g of sodium bentonite into the phosphate mixture, stir well, and use it as an additive. Then mix the base material and additives, add 450ml of water, stir well and pour it into the test mold to make two test pieces, adopt the standard curing method for 24 hours, remove the mold, and then cure in the curing room for 28 days. The indoor temperature was 19° C. and the humidity was 92%. The measured compressive strength of the finished masonry products is 9.85MPa and 9.91MPa, and the contaminated soil, 325 ...

Embodiment 3

[0024] Take 2kg of polluted soil (0-20cm topsoil, soil pH value 5.51, organic matter content 21.8g / kg, total lead 19592mg / kg, total zinc 647mg / kg, total cadmium 14.65mg / kg, Total copper 287mg / kg), air-dried, passed through a 2mm sieve, picked out non-soil impurities, mixed and took 1000g of soil for later use. Will 978g 325 # Portland cement is fully mixed with 1000g soil as the base material. Weigh 2g of calcium dihydrogen phosphate, dissolve it in 420ml of water, pour 20g of sodium bentonite into the phosphate mixture, stir well, and use it as an additive. Then mix the base material and additives, add 430ml of water, stir well and pour it into the test mold to make two test pieces, adopt the standard curing method for 24 hours, remove the mold, and then cure in the curing room for 28 days. The indoor temperature was 21° C. and the humidity was 93%. The measured compressive strength of the finished masonry products is 11.98MPa and 12.52MPa, and the contaminated soil, 325 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a heavy metal-polluted soil masonry and a preparation method thereof. The prior method is not suitable for the remediation of heavily polluted soil. Polluted soil is mixed with No.325 Portland cement, sodium bentonite and monocalcium phosphate according to the weight ratio of (35 to 60):(28 to 62):(1 to 26):(0.01 to 0.2) to form the masonry. The specific preparation process is as follows: after impurities are removed, the polluted soil is proportionally mixed with the No.325 Portland cement, so that base material is produced; the sodium bentonite and the monocalcium phosphate are added into water, so that additive is produced; the additive is added into the base material, water is also added, and after uniform mixing, the mixture is poured into a testing mould, sothat a test piece is produced; the test piece is kept still for 24 hours by adopting a standard curing method; and the demoulded test piece is cured in a curing room for 28 days, so that the masonry product is produced. When in use, the masonry cannot generate secondary pollution on the environment, the materials needed by the preparation method are cheap, the mechanical equipment and the preparation method are simple, and the masonry can be operated on the site and easily transported.

Description

technical field [0001] The invention relates to a method for making masonry by using soil polluted by mine tailings heavy metals, in particular to a method for preparing masonry for structures at normal temperature by adding a hardener to soil heavily polluted by heavy metals. Background technique [0002] Soil pollution by heavy metals is one of the most serious environmental problems in China. Soil heavy metal pollution has the characteristics of poor mobility of pollutants in the soil, long residence time, high toxicity, etc., and can eventually affect human health through media such as water and plants. In particular, heavy metal ions in polluted soil pose a potential threat to crop growth, agricultural product safety, and human health due to their cumulative effect and their biodegradability characteristics. The sources of heavy metals in the soil mainly come from metal tailings, industrial combustion, sewage irrigation, vehicle exhaust emissions, battery production an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): E04C1/00C04B28/04B28B1/14
Inventor 陈建军谢正苗
Owner HANGZHOU DIANZI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka