Method for producing basalt fiber rope net

A technology of basalt fiber and production method, applied in the field of rope nets, can solve the problems of no patents or reports on basalt fiber rope nets, and achieve the effects of superior performance, reduced friction, and reduced yarn friction

Active Publication Date: 2010-09-22
TAIAN ROPE NET PLASTIC
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are no related patents or reports on basalt fiber rope nets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing basalt fiber rope net
  • Method for producing basalt fiber rope net

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1: The composition of the hot dip solution is 2% by weight of anionic surfactant, 5% of sodium alginate, 3% of other additives, and 90% of water; the composition of the fireproof and wear-resistant solution is 12% by weight of PTFE, neutral Salt 6%, other active agents 2%, water 80%; steaming treatment temperature 110°C, pressure 1.8 atmospheres, steaming time 30min.

Embodiment 2

[0019] Embodiment 2: The composition of hot soaking solution is 4% by weight of anionic surfactant, 4% of sodium alginate, 1% of other additives, 91% of water; the composition of fireproof and wear-resistant solution is 14% by weight of PTFE, neutral Salt 4%, other active agents 4%, water 78%; steaming treatment temperature 130°C, pressure 1.2 atmospheres, steaming time 90min.

Embodiment 3

[0020] Embodiment 3: The composition of hot soaking solution is 4% by weight of anionic surfactant, 5% of sodium alginate, 3% of other additives, 88% of water; the composition of fireproof and wear-resistant solution is 14% by weight of PTFE, neutral Salt 6%, other active agents 4%, water 76%; steaming treatment temperature 110°C, pressure 1.6 atmospheres, steaming time 45min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing basalt fiber rope nets, which comprises the following processes of: heat soaking treatment, hot-pressing treatment, weaving ropes, fireproof and wear-resistant treatment, steaming treatment, and the like. The heat soaking treatment solution contains an anionic surfactant, sodium alga acid and other aids; a tension regulation device is arranged on a high-speed braiding machine; and the fireproof and wear-resistant treatment solution contains PTFE, neutral salts, and other active agents. The method has reasonable process and advanced treatment technology and method, and the produced rope nets have the advantages of high temperature resistance, corrosion resistance, high intensity, high safety, and high cost performance.

Description

technical field [0001] The invention relates to a rope net, in particular to a production method of a basalt fiber rope net. Background technique [0002] Basalt fiber is a continuous fiber drawn by high-speed platinum-rhodium alloy wire drawing bushing after basalt rock is melted at 1450 ° C ~ 1500 ° C. It is similar to glass fiber, and its performance is between high-strength S glass fiber and alkali-free E glass fiber. between. Compared with high-tech fibers such as carbon fiber, aramid fiber, and ultra-high molecular weight polyethylene fiber, basalt fiber not only has the characteristics of high-strength and high-modulus high-tech fibers, but also has good high temperature resistance, oxidation resistance, and radiation resistance. , heat insulation and sound insulation, good filterability, high compressive strength and shear strength, suitable for use in various environments and other excellent performances, and good cost performance. New basic materials and high-tec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04C1/02D04C1/12C03C25/26D06B15/02D06B1/00
CPCD07B1/142D07B2401/2035D07B2205/30D07B2205/2071D07B1/02D07B2401/2025C03C25/42
Inventor 宋维广王存涛许秀萍王立家张功明刘兆新许文强
Owner TAIAN ROPE NET PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com