Manufacturing method for environmental-friendly fire-retardant fiber board
A flame-retardant fiber and environment-friendly technology, which is applied in the manufacturing field of environment-friendly flame-retardant fiberboard, can solve problems such as low utilization rate, and achieve the effect of reducing production cost and increasing added value.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0009] 8mm thick medium density fiberboard is manufactured from wood fiber produced from forest residues and wood waste. Treat the wood fiber at a drying temperature of 60°C to a moisture content of 10%, and then add 12% ammonium lignosulfonate, 6% urea, 10% ammonium dihydrogen phosphate, and 1% paraffin wax emulsion to the raw material Mixing is carried out, the mixed material is paved and pre-pressed into a slab, and then hot-pressed. The hot-pressing temperature is 190°C, the hot-pressing pressure is 2MPa, and the hot-pressing time is 10 minutes. Finally, the finished product is aged and cut into storage.
Embodiment 2
[0011] The 4mm thick high-density fiberboard is manufactured from wood fiber produced from forest residues and wood waste. Treat the wood fiber at a drying temperature of 60°C to a moisture content of 13%, and then add 12% ammonium lignosulfonate, 8% urea, 8% ammonium dihydrogen phosphate, and 1% paraffin wax emulsion to the raw material Mixing, pre-pressing the mixed material into a slab, and then hot-pressing, the hot-pressing temperature is 180 ° C, the hot-pressing pressure is 3 MPa, and the hot-pressing time is 6 minutes. Finally, the finished product is put into storage after aging.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com