Polyamide resin composition

A technology of polyamide resin and composition, which is applied in the field of polyamide resin composition and fuel parts, which can solve the problem of insufficient bonding strength of the main body of the fuel tank, poor adhesion between HDPE resin and polyamide resin, reduction in weight, etc. problems, achieve excellent adhesive strength, fuel gas barrier properties, and excellent fuel permeation resistance

Inactive Publication Date: 2011-02-16
UBE IND LTD
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, even if the amount of permeation of the fuel from the main body of the fuel tank can be reduced by the above methods, the amount of permeation from various parts (such as valves, etc.) attached to the fuel tank is large, so the volatilization from the entire fuel part is hindered. Quantity reduction
[0005] The reason is that in order to obtain sufficient bonding strength with the fuel tank, various parts attached to the fuel tank are made of the same material as the fuel tank, that is, high-density polyethylene, which has poor fuel permeation resistance.
[0006] Therefore, it has been studied to use polyamide resin with excellent fuel permeation resistance to manufacture various parts attached to the fuel tank, but because the adhesion between HDPE resin and polyamide resin is poor, there is a problem with the use of HDPE resin. The problem that sufficient bonding strength cannot be obtained for the main body of the formed fuel tank

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyamide resin composition
  • Polyamide resin composition
  • Polyamide resin composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0091] Hereinafter, although an Example and a comparative example are shown and this invention is demonstrated concretely, this invention is not limited to this. In addition, the physical property measurement of the molded article in the Example and the comparative example was performed as follows.

[0092] (1) Determination of the terminal amino group concentration of polyamide resin

[0093] Add 1 g of polyamide resin to an Erlenmeyer flask with a stopcock, add 40 ml of a pre-adjusted solvent (phenol / methanol (volume ratio)=9 / 1), then stir and dissolve with a magnetic stirrer, using thymol blue as an indicator reagent, titrated with 0.02N hydrochloric acid, and then the concentration of the terminal amino group was determined.

[0094] (2) Determination of the terminal carboxyl group concentration of polyamide resin

[0095] 1 g of polyamide resin and 40 ml of benzyl alcohol were added to a three-neck pear-shaped flask, and then immersed in an oil bath set at 180° C. under...

Embodiment I-1

[0107] (1) Manufacture of aliphatic polyamide resin I-1

[0108] In a 70-liter autoclave, add 0.5 kg of water, 200 g, and 70 g of hexamethylenediamine to 20 kg of ε-caprolactam as a polymerizable monomer, replace the tank with nitrogen, heat to 100°C, and stir to make the tank become uniform within. Then, the inside of the tank was stirred for 1 hour under the conditions of 260° C. and 1.7 MPa. Thereafter, the pressure was released, and polymerization was performed under normal pressure for 3 hours while evaporating moisture from the reaction vessel. After the reaction, the polymer taken out from the lower nozzle of the reaction vessel in the form of strands is cooled and cut to obtain pellets formed of polyamide resin. The obtained pellets were extracted in hot water at 100° C. to extract unreacted monomers, and vacuum-dried to obtain samples.

[0109] The obtained polyamide 6 had a terminal amino group concentration of 100 meq / kg and a terminal carboxyl group concentratio...

Embodiment I-2

[0115] In Example I-1(2), Harima Chemicals Co., Ltd. granulated talc "HT-7050" (powder talc with an average particle diameter of 1.8 μm (aspect ratio: 10) 95.0% by weight + rosin-based resin (modified rosin) 5.0% by weight) 0.7% by weight and resin I-1 99.3% by weight, the same operation as Example I-1 was carried out to obtain a polyamide resin composition. As a result of electron microscope observation, talc was uniformly dispersed in the polyamide resin composition. The results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

Disclosed are: [1] a polyamide resin composition which is characterized by comprising 85 wt% or more of an aliphatic polyamide resin (A-1) in which the concentration of the terminal amino group is higher than that of the terminal carboxy group, 0.01 to 10 wt% of talc (B) which is dispersed in the aliphatic polyamide resin (A-1), and 0.0001 to 1 wt% of a dispersing agent (C); [2] a polyamide resin composition which is characterized by comprising 75 to 95 wt% of the aliphatic polyamide resin (A-1), 1 to 15 wt% of an aromatic polyamide resin (A-2), 0.01 to 10 wt% of talc (B) which is dispersed in the polyamide resins (A-1) and (A-2), and 0.0001 to 1 wt% of a dispersing agent (C); [3] a process for producing each of the above-mentioned polyamide resin compositions; and [4] a fuel component comprising any one of the above-mentioned polyamide resin compositions. The polyamide resin compositions are not deteriorated in the properties inherent in polyamide resins and has excellent adhesion strength to a polyolefin resin and the like and excellent fuel gas barrier properties.

Description

technical field [0001] The present invention relates to a polyamide resin composition excellent in fuel permeation resistance for use in welded portions of fuel tanks and the like, a method for producing the same, and fuel parts using the polyamide resin composition. Background technique [0002] Conventionally, in consideration of safety and environmental measures, it has been required to reduce the amount of volatilization of fuel from the walls and connecting parts of fuel tanks and their accessories. For example, in the automotive field, fuel tanks made of single-layer high-density polyethylene (HDPE) resin manufactured by blow molding are popular. When using this HDPE resin fuel tank, in order to reduce the amount of permeation of the fuel from the tank main body, a method of sulfonating the HDPE resin (see Patent Document 1), a method of fluorine treatment, and the formation of a gas-barrier resin have been proposed. A method of forming a hollow molded body with a mul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L93/04C08L77/00B29C45/16C08L77/10
CPCB29C66/71B29C65/20B60K15/03177C08L2205/02B29C66/91411B29C65/06B29K2035/00B29L2031/7172B60K2015/03046B29C65/0672B29K2023/00B29C65/16B29K2077/00B29C65/14B29C66/919C08K3/14B29C65/8215B29C65/08C08L77/06C08L93/04B29C65/02B29C66/712C08K2201/008C08L2666/02Y10T428/31725B29C65/00
Inventor 坂本直树野中裕文儿玉齐