Metallic nano cluster/silicon dioxide hollow nuclear shell structured nanoparticles and preparation method thereof

A metal nanocluster and core-shell structure technology, applied in the preparation of microspheres, microcapsule preparations, etc., can solve the problems of limiting the application performance of hollow metals with nanostructures, and the inability to control and adjust synchronously, so as to achieve controllable size and shape, Easy to operate, high output effect

Active Publication Date: 2011-04-20
DALIAN UNIV OF TECH
View PDF6 Cites 93 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the above method can be made of nanostructured solid metal @SiO 2 Get Nanostructured Hollow Metal@SiO 2 , but the metal coated in the silica shell is only nanoparticles, not metal nanoclusters; at the same time, the shape and size of the cavity depend on

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metallic nano cluster/silicon dioxide hollow nuclear shell structured nanoparticles and preparation method thereof
  • Metallic nano cluster/silicon dioxide hollow nuclear shell structured nanoparticles and preparation method thereof
  • Metallic nano cluster/silicon dioxide hollow nuclear shell structured nanoparticles and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0045] Example 1

[0046] 10g Dissolve in 50mL cyclohexane, stir and heat to 50℃, after complete dissolution, add dropwise 1M cobalt chloride solution 1.5mL, stir for 1h, add 2mL 80% hydrazine hydrate solution, stir and react for 5-50 minutes, adjust the reaction with ammonia The pH value of the solution is 10.5-11, 10 g of ethyl orthosilicate is added dropwise, and the reaction is stirred for 2 hours. After centrifugation, washing, drying, roasting, reduction, electron microscope observation, such as figure 1 As shown, the product particles are uniform, the particle size is 40-50nm, the nanometal particle size is less than 4nm, and the cavity diameter is 8-10nm.

Example Embodiment

[0047] Example 2

[0048] 10g Dissolve in 50mL cyclohexane, stir and heat to 50℃, after complete dissolution, add 1.5mL 1M cobalt chloride solution dropwise, stir for 1h, then add 1.5mL 1M ethylenediamine (or triethanolamine / diethylenetriamine / tetra Ethylene pentamine) solution, after being evenly dispersed, add 1.0 g of NaBH 4 / LiAlH 4 , The reaction is stirred for 5-50 minutes, the pH of the reaction solution is adjusted to 10.5-11 with ammonia water, 10 g of ethyl orthosilicate is added dropwise, and the reaction is stirred for 2 hours. After centrifugation, washing, drying, roasting, reduction, electron microscope observation, such as figure 2 As shown, the product particles are uniform, the particle size is 40-50nm, the nanometal particle size is less than 4nm, and the cavity diameter is 8-10nm.

Example Embodiment

[0049] Example 3

[0050] 10g Dissolve in 50mL cyclohexane, stir and heat to 50℃, after complete dissolution, add 1.5mL 1M nickel nitrate solution dropwise, stir for 1h, add 2mL 80% hydrazine hydrate solution, stir and react for 5-50 minutes, adjust the reaction solution with ammonia The pH value is 10.5-11, 10 g of ethyl orthosilicate is added dropwise, and the reaction is stirred for 2 hours. After centrifugation, washing, drying, roasting, reduction, electron microscope observation, such as image 3 As shown, the product particles are uniform, the particle size is 20-30nm, the nanometal particle size is less than 4nm, and the cavity diameter is 8-10nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Cavity diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of nanoparticle preparation, in particular to metallic nano cluster/silicon dioxide hollow nuclear shell structured nanoparticles and a one-step controllable preparation method thereof. The used surfactant is a nonionic surfactant, the organic phase is cyclohexane, toluene and other organic hydrocarbons, and a metal saline solution and a metal complexing agent are added to form a reversed micelle system. Meanwhile, the complexed metal saline solution in the reversed micelle system is reduced to obtain metallic nanoparticles and then ammonia water and ammoniawater are added directly in the solution to obtain size and shape controllable hollow silicon dioxide nuclear shell material with metallic nano clusters distributed uniformly on the inner wall of thecavity. The method has the advantages of simple process, easy operation and great yield and can obtain size and shape controllable metallic nano cluster/silicon dioxide hollow nuclear shell structured nanoparticles.

Description

technical field [0001] The invention belongs to the field of nanoparticle preparation, and in particular relates to a metal nanocluster@silica hollow core-shell nanoparticle and a one-step controllable preparation method thereof. Background technique [0002] Nano-sized core-shell materials have great application potential in chemistry, physics, electronics, biotechnology, and material science, and have received extensive attention. The hollow core-shell material has low density, high surface area, good thermal and mechanical stability, especially the nano-sized hollow metal core-silica shell material with controllable structure, composition and performance in catalytic nanoreactors, sensors. And energy storage media and other aspects have shown outstanding advantages, so it has become a hot spot of interdisciplinary research. [0003] Synthesis of nanostructured metal@SiO by conventional methods 2 Only solid structures can be obtained. At present, nanostructured hollow me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F9/24B22F1/02B01J13/02
Inventor 吕荣文邹伟
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap