Abrasion-resistant rubber and plastic composite material

A composite material, rubber and plastic technology, applied in the field of rubber and plastic composite materials, can solve the problems of poor strength, poor softness and elasticity, unsatisfactory wear resistance, etc., to improve strength and wear resistance, anti-skid and wear-resistant. wear resistance, the effect of excellent wear resistance

Active Publication Date: 2011-05-04
JINJIANG CHENGCHANG SHOES
View PDF0 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing EVA composition modified by POE (polyethylene hydrocarbon elastomer) is light in weight and easy to shape, but the softness and elasticity of the material are not good, and even if the softness partially meets the requirements, its strength is still poor , especially wear resistance is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0026] A wear-resistant rubber-plastic composite material, which is composed of rubber particle raw materials, fillers, coupling agents, metal oxides, lubricants, foaming agents, and bridging agents. The ratio of each component is:

[0027] Colloidal raw material: 100kg, the ratio is: 90kgEVA (ethylene vinyl acetate), 5kgPOE (polyolefin elastomer), 5kg EPDM rubber;

[0028] Filler: use 20kg of talcum powder;

[0029] Coupling agent: use 0.1kg of silane coupling agent;

[0030] Metal oxide: 0.6kg of ZnO is used as foaming aid and active agent;

[0031] Lubricant: use 0.2kg of stearic acid and 0.3kg of zinc stearate;

[0032] Foaming agent: 4kg of AC azo foaming agent is used;

[0033] Bridging agent: use 1kg dicumyl peroxide;

[0034] Its production process is as follows:

[0035] 1. Fully mix 100kg of colloidal raw materials with 20kg of talcum powder, 0.6kg of ZnO, 0.2kg of stearic acid, 0.3kg of zinc stearate, and 0.1kg of silane coupling agent in an internal mixer;

...

specific Embodiment 2

[0040] A wear-resistant rubber-plastic composite material, which is composed of rubber particle raw materials, fillers, coupling agents, metal oxides, lubricants, foaming agents, and bridging agents. The ratio of each component is:

[0041] Colloid material: 100kg, the ratio is: 50kg EVA (ethylene vinyl acetate), 30kg POE (polyolefin elastomer), 20kg EPDM rubber;

[0042] Filler: use 2kg of calcium carbonate;

[0043] Coupling agent: use 15kg of titanate coupling agent;

[0044] Metal oxide: 2kg of ZnO is used as foaming aid and active agent;

[0045] Lubricant: use 1kg of stearic acid and 1kg of zinc stearate;

[0046] Foaming agent: 0.5kg of AC azo foaming agent is used;

[0047] Bridging agent: use 0.4kg dicumyl peroxide;

[0048] Its production process is as follows:

[0049] 1. Fully mix 100kg of colloidal raw materials with 2kg of calcium carbonate, 2kg of ZnO, 1kg of stearic acid, 1kg of zinc stearate, and 15kg of titanate coupling agent in an internal mixer;

[0...

specific Embodiment 3

[0054] A wear-resistant rubber-plastic composite material, which is composed of rubber particle raw materials, fillers, coupling agents, metal oxides, lubricants, foaming agents, and bridging agents. The ratio of each component is:

[0055] Colloidal raw material: 100kg, the ratio is: 50kg EVA (ethylene vinyl acetate), 20kg POE (polyolefin elastomer), 30kg EPDM rubber;

[0056] Filler: use 15kg of talcum powder or calcium carbonate;

[0057] Coupling agent: use 10kg of silane coupling agent or titanate coupling agent;

[0058] Metal oxide: 1kg of ZnO is used as foaming aid and active agent;

[0059] Lubricant: use 0.7kg of stearic acid and 0.8kg of zinc stearate;

[0060] Foaming agent: use 2kg of AC azo foaming agent;

[0061] Bridging agent: use 0.6kg dicumyl peroxide;

[0062] Its production process is as follows:

[0063] 1. Put 100kg of colloidal raw materials, 15kg of talcum powder or calcium carbonate, 1kg of ZnO, 0.7kg of stearic acid, 0.8kg of zinc stearate, 10kg...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a composite material, in particular to a rubber and plastic composite material which is specially used for the components of shoe materials, sports goods, leather and the like. The composite material is mainly prepared by mixing a colloidal particle raw material, a bulking agent, a coupling agent, metal oxides, a lubricating agent, a foaming agent and a bridging agent according to a certain ratio, wherein the colloidal particle raw material is prepared by mixing EVA (Ethylene Vinyl Acetate), POE (Polyolefin Elastomer) and ethylene propylene rubber. The composite material provided by the invention improves the compatibility and associativity of each component material by adding the ethylene propylene rubber and the coupling agent into the formula so as to enhance the strength and abrasion resistance of the rubber and plastic blended material, thus the obtained rubber and plastic composite material maintains the plasticity of the EVA material and has the advantages of flexibility, elasticity, skid resistance and excellent abrasion resistance of a rubber material.

Description

【Technical field】 [0001] The invention relates to a composite material, especially a rubber-plastic composite material specially used for shoe materials, sporting goods, leather and other components. 【Background technique】 [0002] Most of the existing EVA adopts the production method of POE modified materials. The modified materials are suitable for injection molding and compression molding. They can be widely used in shoe outsoles, sporting goods and other light industrial products. The ingredients are composed of 50-95% EVA, 5 -40% POE (Polyolefin Elastomer), 5-20% Talc or CaCO 3 , 1-2% of metal oxides, 0.1-1% of lubricants, 0.4-1% of peroxides (bridging agents), 1-4% of azo foaming agents and appropriate amount of pigments are mixed by internal mixer, and the kneading Machine-assisted mixing, pelletizing, injection molding or compression molding. The existing EVA composition modified by POE (polyethylene hydrocarbon elastomer) is light in weight and easy to shape, but ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/16C08K13/02C08K5/54C08K5/10
Inventor 李灿升
Owner JINJIANG CHENGCHANG SHOES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap