Negative ion bath mat and preparation method thereof

A technology of negative ions and bath mats, applied in bathtubs, showers, sanitary equipment, etc., can solve the problems of not being able to bring comfort to users, not being able to play a role in medical care, and poor physical and mechanical properties, achieving soft texture, The effect of smooth surface and high physical and mechanical properties

Active Publication Date: 2011-10-05
GUANGDONG GUANGHAIDA IND
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current bath mats mainly play an anti-skid role, and most of them are hard in texture and have poor physical and mechanical properties, which cannot bring comfortable feeling to users, let alone play a role in medical care.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] A kind of negative ion bath pad, by weight, is made up of following raw material:

[0083] 60 parts of natural rubber

[0084] 20 parts of styrene-butadiene rubber

[0085] 10 parts isoprene rubber

[0086] EPDM rubber 5 parts

[0087] Zinc oxide 4 parts

[0088] 2 parts stearic acid

[0089] Light calcium carbonate 90 parts

[0090] Talcum powder 26 parts

[0091] Naphthenic oil 20 parts

[0092] Anti-aging agent 1 part

[0093] Microcrystalline wax 0.3 parts

[0094] Negative ion powder 4 parts

[0095] Accelerator 2 parts

[0096] Sulfur powder 2 parts

[0097] 1 part of M plastic rubber.

[0098] The negative ion powder is tourmaline negative ion powder with a particle size of 1500 mesh.

[0099] M plasticate rubber is made from natural rubber with a weight ratio of 100:2 and accelerator M at a temperature of 110°C for 8 minutes in a tipping bucket mixer.

[0100] The anti-aging agent includes anti-aging agent PA and anti-aging agent 264 with a mass ra...

Embodiment 2

[0111] A kind of negative ion bath pad, by weight, is made up of following raw material:

[0112] 60 parts of natural rubber

[0113] 30 parts of styrene-butadiene rubber

[0114] 10 parts isoprene rubber

[0115] EPDM rubber 10 parts

[0116] Zinc oxide 5 parts

[0117] 2 parts stearic acid

[0118] Light calcium carbonate 90 parts

[0119] Talcum powder 30 parts

[0120] Naphthenic oil 22 parts

[0121] Anti-aging agent 1 part

[0122] Microcrystalline wax 0.5 parts

[0123] Negative ion powder 6 parts

[0124] Accelerator 3 parts

[0125] Sulfur powder 2 parts

[0126] 5 parts of M plastic rubber.

[0127] The negative ion powder is tourmaline negative ion powder with a particle size of 2000 mesh.

[0128] M plasticate rubber is made from natural rubber with a weight ratio of 100:2 and accelerator M at a temperature of 115°C for 9 minutes in a tilting bucket mixer.

[0129] The anti-aging agent includes anti-aging agent PA and anti-aging agent 264 with a mass ...

Embodiment 3

[0140] A kind of negative ion bath pad, by weight, is made up of following raw material:

[0141] 65 parts of natural rubber

[0142] 25 parts of styrene-butadiene rubber

[0143] 15 parts isoprene rubber

[0144] EPDM rubber 6 parts

[0145] Zinc oxide 5 parts

[0146] 3 parts stearic acid

[0147] Light calcium carbonate 93 parts

[0148] Talc powder 28 parts

[0149] Naphthenic oil 22 parts

[0150] Anti-aging agent 2 parts

[0151] Microcrystalline wax 0.4 parts

[0152] Negative ion powder 5 parts

[0153] Accelerator 3 parts

[0154] 3 parts sulfur powder

[0155] 6 parts of M plastic rubber.

[0156] The negative ion powder is tourmaline negative ion powder with a particle size of 3000 mesh.

[0157] M mlastane rubber is prepared by masticating natural rubber and accelerator M at a temperature of 120°C for 10 minutes at a temperature of 120°C with a ratio of parts by weight of 100:2.

[0158] The anti-aging agent includes anti-aging agent PA and anti-aging...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of bath mats, in particular to a negative ion bath mat and a preparation method thereof. The negative ion bath mat comprises the following raw materials in part by weight: 60 to 70 parts of natural rubber, 20 to 30 parts of butadiene styrene rubber, 10 to 20 parts of isoprene rubber, 5 to 10 parts of ethylene propylene diene monomer (EPDM) rubber, 4 to5 parts of zinc oxide, 2 to 3 parts of stearic acid, 90 to 100 parts of light calcium carbonate, 26 to 36 parts of talcpowder, 20 to 24 parts of naphthenic oil, 1 to 3 parts of anti-aging agent, 0.3 to 0.5 part of microcrystalline wax, 4 to 6 parts of negative ion powder, 2 to 4 parts of accelerant, 2 to 3 parts of sulphur powder and 1 to 10 parts of M plasticated rubber. In the invention, raw materials such as various rubber compositions, the negative ion powder, the anti-aging agent and the like are used for preparing the negative ion bath mat which has a soft texture, a smooth and neat surface and high physical and mechanical properties such as high tensile strength, high elongation at rupture, high tearing strength and the like, has a better health-care effect on a human body and can increase human metabolism and blood circulation.

Description

technical field [0001] The invention relates to the technical field of bath mats, in particular to an anion bath mat and a preparation method thereof. Background technique [0002] According to research, negative ions can strengthen the function of the cerebral cortex and mental activity, boost the spirit, improve work efficiency, and improve the quality of sleep; negative ions can strengthen the oxidation process of brain tissue, so that the brain tissue can obtain more oxygen; negative ions have The effect of obviously dilating blood vessels can relieve arterial vasospasm and achieve the purpose of lowering blood pressure. Negative ions are also beneficial for improving heart function and myocardial nutrition, and are beneficial to the recovery of patients with hypertension and cardiovascular and cerebrovascular diseases; negative ions can make the blood The effect of slowing down and prolonging the coagulation time can increase the oxygen content in the blood, which is be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08L9/06C08L23/16C08K13/02C08K3/22C08K3/26C08K3/34C08K3/36C08K3/38C08K3/32A47G27/02A47K3/00
Inventor 蔡业林
Owner GUANGDONG GUANGHAIDA IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More