Method for preparing starch grafted hyperbranched amide polymer

An amide polymer, starch grafting technology, applied in the direction of flocculation/sedimentation water/sewage treatment, etc., can solve the problem of not getting branched polymers, and achieve the effects of easy control of polymerization reaction and remarkable turbidity removal effect.

Active Publication Date: 2011-11-02
ZHEJIANG UNIV
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, WO 99/46301 discloses the use of polyene monomers and appropriate proportions of mercaptans as chain transfer agents to obtain branched polymethyl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1

[0023] (1) Add 1.0 parts of carboxymethyl starch (CMS), 100 parts of acetic acid-sodium acetate buffer solution (pH=5), and 0.0453 parts of 3-benzylmercaptothiocarbonylpropionic acid (BCPA) into a 250ml three-necked bottle. Stir, pass nitrogen and deoxygenate, heat up to 60°C, and gelatinize for 0.5 hours;

[0024] (2) 7.1 parts of acrylamide were added to the above-mentioned starch aqueous solution;

[0025] (3) Dissolve 0.59 parts of N,N'-methylenebisacrylamide in 50 parts of water and install it on a micro-injection pump;

[0026] (4) Weigh 0.020 part of ammonium persulfate (APS), dissolve it in a small amount of water and add it to a mixed solution of starch and acrylamide to initiate polymerization;

[0027] (5) Start the micro-injection pump, set the dripping acceleration rate, and complete the dripping of the N,N'-methylenebisacrylamide aqueous solution within 3 hours, and then continue the reaction for 0.5 hours to obtain hyperbranched polyacrylami...

Example Embodiment

[0035] Example 2

[0036] (1) Add 0.6 parts of carboxymethyl starch (CMS), 100 parts of acetic acid-sodium acetate buffer solution (pH=5), and 0.0272 parts of 3-benzylmercaptothiocarbonylpropionic acid (BCPA) into a 250ml three-necked bottle. Stir, pass nitrogen and deoxygenate, then heat up to 60°C, and gelatinize for 30 minutes;

[0037] (2) 7.1 parts of acrylamide were added to the above-mentioned starch aqueous solution;

[0038] (3) Dissolve 0.45 part of N,N'-methylenebisacrylamide in 50 parts of water and install it on a micro-injection pump;

[0039] (4) Weigh 0.020 part of ammonium persulfate (APS), dissolve it in a small amount of water and add it to a mixed solution of starch and acrylamide to initiate polymerization;

[0040] (5) Start the micro-injection pump, set the dripping acceleration rate, and complete the dripping of the N,N'-methylenebisacrylamide aqueous solution within 3 hours, and then continue to react for 1 hour to obtain hyperbranched polyacrylamide...

Example Embodiment

[0042] Example 3

[0043] (1) Add 1.0 parts of corn starch (Maize), 100 parts of acetic acid-sodium acetate buffer solution (pH=5), and 0.0453 parts of 3-benzylmercaptothiocarbonylpropionic acid (BCPA) into a 250ml three-necked bottle, stir mechanically, After nitrogen and oxygen removal, the temperature was raised to 95°C and gelatinized for 30 minutes;

[0044] (2) 7.1 parts of acrylamide were added to the above-mentioned starch aqueous solution;

[0045] (3) Dissolve 0.45 part of N,N'-methylenebisacrylamide in 50 parts of water and install it on a micro-injection pump;

[0046] (4) Weigh 0.020 part of ammonium persulfate (APS), dissolve it in a small amount of water and add it to a mixed solution of starch and acrylamide to initiate polymerization;

[0047] (5) Start the micro-syringe pump, set the dripping acceleration rate, and complete the dripping of the N,N'-methylenebisacrylamide aqueous solution within 3 hours, and then continue to react for 1 hour to obtain hyperb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a starch grafted hyperbranched amide polymer. The method is characterized by: preparing a mixed phase and a branching reagent phase, gelatinizing the mixed phase for 0.1-1 hour at a temperature of 25-95 DEG C, then adjusting the temperature to 40-80 DEG C, adding a RAFT chain transfer agent to the gelatinized mixed phase, then adding a initiator to initiate a polymerization; during the polymerization, adding the branching reagent phase to the mixed phase in a dropwise manner within 1-10 hours, and sequentially carrying out the reaction for 0.5-4 hours after completing the adding, finally, carrying out a high-conversion preparation to prepare the starch grafted hyperbranched amide polymer. With the present invention, diene monomers and the chain transfer agent with low ratio are provided for high-polymerization rate and high- conversion preparation of the starch grafted hyperbranched amide polymer in a polar solvent system by using a semi-continuous polymerization process through a reversible addition and fragmentation chain transfer polymerization; the polymerization is easy to be controlled and turbidity removal effect of the productis significant.

Description

technical field [0001] The invention relates to a preparation method of a flocculant, in particular to a preparation method of a starch-grafted hyperbranched vinyl or acrylamide polymer suitable for dispersion, adhesion, flocculation and rheology control. Background technique [0002] Vinyl or acrylamide polymers are widely used in major fields such as water treatment, papermaking, printing and dyeing, mining, oil extraction, and building materials. Vinyl or acrylamide polymers widely used at present, such as polyacrylamide and its copolymers, mainly have a linear structure, but branched vinyl or acrylamide polymers are widely used in water treatment and the like. uncommon. As a natural polymer compound with abundant resources and low price, starch is widely used in many fields, and water treatment is one of them. CN1196334A discloses a method for preparing cationic amphoteric grafted polyacrylamide flocculants by using potassium permanganate to initiate starch or microcry...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F251/00C08F220/56C08F222/38C08F2/38C02F1/56
Inventor 王文俊王敦明李伯耿朱世平
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap