A kind of method for preparing organic pervaporation membrane

A pervaporation membrane and organic technology, applied in chemical instruments and methods, semi-permeable membrane separation, membrane technology, etc., can solve the problem that the pervaporation membrane cannot realize the microscopic chemical structure and microstructural structure of the separation layer and the interface of the support layer. , to achieve the effect of increasing the permeation flux and separation factor, improving the permeation flux and selectivity, and simplifying the preparation steps

Active Publication Date: 2011-12-14
JIANGSU JIUMO HIGH TECH CO LTD
View PDF4 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that the current pervaporation membrane cannot realize the microchemical structure and microstructure an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1: Using (v / v) 7:3 concentrated sulfuric acid and hydrogen peroxide solution to soak the mullite support overnight for hydroxylation pretreatment, and then wash it with deionized water. Get 4 grams of polydimethylsiloxane (PDMS) and 72g of n-hexane, stir and mix at 800rpm for 1h, then add 0.75g of vinyltrimethoxysilane as a crosslinking agent, 0.6g of n-octyltrichlorosilane and 0.1g of anilinomethyltriethoxysilane was used as a dual-functional modifier, stirred at 800rpm for 2h, then added 0.08g of dibutyltin dilaurate catalyst, stirred at 400rpm for 8h to obtain a uniform PDMS membrane coating solution, Finally, the impregnation-pulling method is used to coat the tubular mullite support to obtain a PDMS composite pervaporation membrane with improved permeability and selectivity.

Embodiment 2

[0029] Example 2: The polyethersulfone support was soaked in deionized water for 12 hours to carry out hydroxylation pretreatment. Take 5 g of polyoctylmethylsiloxane (POMS) and 55 g of toluene, stir at 650 rpm for 2 h, then add 0.05 g of vinyltriethoxysilane as a crosslinking agent, 0.03 g of γ-aminopropyltriethoxy Base silane and 0.12g hexadecyltriethoxysilane are used as dual-functional regulators, stir at 650rpm for 2h, add 0.1g of oxalic acid catalyst, stir at 450rpm for 4h to get a uniform PDMS membrane coating solution, and finally use A PDMS composite pervaporation membrane with improved permeability and selectivity can be obtained by coating the polyethersulfone support with a casting method.

Embodiment 3

[0032] Example 3: Soak the cellulose acetate support in 5 wt% dilute sulfuric acid solution overnight for hydroxylation pretreatment. Take 5 grams of polyvinyl alcohol (PVA) and 75g of xylene and mix them, stir at 300rpm for 10h, then add 0.04g of ethyl silicate as a crosslinking agent, 0.03g of hexadecyltrichlorosilane and 0.05g of N-β (Aminoethyl)-γ-aminopropyltriethoxysilane was used as a dual-functional modifier, after stirring at 300rpm for 8h, 0.04g of platinum catalyst was added, and stirring at 700rpm for 10h to obtain uniformly dispersed and stable PDMS composites Finally, the scrap coating method is used to coat the cellulose acetate support to obtain a PDMS composite membrane with microphase separation and equilibrium.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing a composite pervaporation membrane. The method comprises the following steps of: dissolving an organic matter in a solvent to prepare a homogeneous phase membrane forming solution; adding a crosslinking agent and a difunctional conditioning agent into the membrane forming solution, uniformly mixing and adding a catalyst; coating the prepared membrane forming solution containing the difunctional conditioning agent on a supporting body; and finally performing aftertreatment on the composite membrane to prepare the composite pervaporation membrane.By the method, the permeability and selectivity of the pervaporation membrane can be improved simultaneously, and the stability of the composite membrane is also improved.

Description

technical field [0001] The invention relates to a technology for preparing and regulating organic pervaporation membranes, specifically refers to regulating the microchemical structure and microstructure of organic pervaporation membranes as well as the organic separation layer and support by utilizing the synergistic effect of "reaction inhibition and interface wetting" Interfacial bond strength between layers. Background technique [0002] The pervaporation process is a good method for separating liquid mixtures, including dehydration of aqueous solutions of organic matter, separation of organic matter in water, separation of binary organic mixtures, etc. Organic membrane materials are widely used in pervaporation processes. Organic pervaporation membranes have become the preferred materials for the preparation of pervaporation membranes because of their low price and good film-forming properties. However, there is still a lack of effective means to achieve the controlla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D69/10B01D67/00B01D61/36
Inventor 金万勤卫旺赵旭红徐南平
Owner JIANGSU JIUMO HIGH TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap