Method for making ceramic selenium drum development magnetic roller aluminum sleeve

A technology for developing a magnetic roller and a manufacturing method, which is applied to the plating of superimposed layers, the electrical recording process applying charge patterns, and the equipment for applying the electrical recording process of charge patterns, etc. The degree of oxidation and wear resistance need to be further improved to achieve the effect of improving various properties, improving wear resistance and electrical conductivity, and good bonding force

Inactive Publication Date: 2012-04-04
郑杰 +1
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in actual use, the conductivity, easy oxidation and wear resistance of the adsorption layer on the surface of the aluminum sleeve still need to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The present invention comprises following steps in order:

[0018] (1) The surface of the aluminum casing is directly sandblasted for roughening treatment, including the following steps:

[0019] A. Perform routine chemical degreasing, water washing, and light cleaning on the aluminum casing;

[0020] B. Cover both ends of the cleaned aluminum casing with silica gel-processed protective sleeves, put them into the sandblasting machine, and use the sandblasting machine to spray the glass beads sieved by the 180-mesh sampling sieve on the aluminum casing For sand, the sandblasting pressure is 0.2MP, the sandblasting distance is 10CM, and it is sprayed back and forth twice at a constant speed of 30 seconds / time.

[0021] C. Insert the sandblasted aluminum casing into the jig and put it into the air shower to remove the remaining glass beads for use.

[0022] (2) The process of plating an electroless nickel-phosphorus alloy protective layer with a total thickness of <5 μm ...

Embodiment 2

[0032] Repeat Example 1 according to the same steps described, but in the process (1) step B, the white corundum sieved by the 280-mesh sampling sieve is used to sandblast the aluminum casing, and the sandblasting pressure of the sandblasting machine is 0.25MP, the sandblasting distance is 12CM, spray back and forth twice at a constant speed of 35 seconds / time. Operation (2) step G with Teflon 90g / L, nickel sulfate 220g / L, sodium acetate 60g / L, sodium citrate 40g / L, sodium hypophosphite 180g / L, pH is 4.6~4.8, treatment temperature The temperature is 95°C, the processing time is 12 minutes, and washed with pure water.

Embodiment 3

[0034] Repeat Example 1 according to the same steps as described, but in the process (1) step B, the white corundum sieved by the 80-purpose sampling sieve is used to sandblast the aluminum casing, and the sandblasting pressure of the sandblasting machine is 0.15MP, the sandblasting distance is 8CM, spray back and forth twice at a constant speed of 25 seconds / time. Operation (2) step G with Teflon 110g / L, nickel sulfate 180g / L, sodium acetate 40g / L, sodium citrate 60g / L, sodium hypophosphite 220g / L, pH is 4.6~4.8, treatment temperature The temperature is 85°C, the processing time is 12 minutes, and washed with pure water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Resistivityaaaaaaaaaa
Durabilityaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for making a ceramic selenium drum development magnetic roller aluminum sleeve. The method is used for preventing oxidation of an adsorption layer on the surface of the aluminum sleeve, improving the abrasion resistance of the aluminum sleeve and improving the conductivity of the aluminum sleeve at the same time. The method comprises the following processes of: directly blasting sand to the surface of the aluminum sleeve to perform roughening treatment; and coating a chemically plated nickel-phosphorus alloy protective layer with the total thickness of less than 5 microns and a chemically plated ceramic and nickel-phosphorus alloy protective layer on the aluminum sleeve with a frosting layer. On the basis of keeping high particle fineness and uniformity of the adsorption layer on the surface of the aluminum sleeve, the service life of the aluminum sleeve can be greatly prolonged by the coated nickel-phosphorus alloy protective layer and the ceramic and nickel-phosphorus alloy protective layer; and meanwhile, because the chemically plated nickel-phosphorus alloy protective layer, the chemically plated ceramic and nickel-phosphorus alloy protective layer, the sand blasting method and the secondary zinc galvanizing technology are combined, the conductivity and the abrasion resistance of the adsorption layer on the surface of the aluminum sleeve are improved, the oxidation property of the adsorption layer is reduced, and various properties of common development magnetic rollers are obviously improved.

Description

technical field [0001] The invention relates to a method for chemically treating metal surfaces, in particular to a method for manufacturing an aluminum sleeve of a developing magnetic roller of a ceramic toner cartridge. Background technique [0002] The magnetic stick in the toner cartridge is an important accessory for laser printers, copiers or fax machines. The magnetic stick is usually composed of an aluminum sleeve with an adsorption layer, a magnetic core inserted in it, a conductive contact head tightly fitted on the aluminum sleeve, and two ends. Composed of plastic isolation sleeves, under the action of the magnetic field of the magnetic core, the carbon powder is adsorbed on the surface of the adsorption layer of the aluminum sleeve. After the toner drum is powered on, the aluminum sleeve arranges and transfers the carbon powder to the surface of the photosensitive drum. It can be seen that the quality of the carbon powder adsorption layer on the surface of the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C18/32C23C18/18C23C18/36C23C18/00C23C10/20C23C28/00B24C1/00G03G15/09
Inventor 郑杰龚晓剑
Owner 郑杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products