Permanent antistatic polyphenylene sulfite (PPS)/poly-p-phenylene oxide (PPO) alloy and production method thereof

An antistatic masterbatch and alloy technology, which is applied in the field of permanent antistatic masterbatch and its preparation, can solve the problems of low conductivity, etc., and achieve the effects of low cost, improved comprehensive performance and small addition amount.

Inactive Publication Date: 2012-04-18
SHANGHAI SUNNY
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PPS / PPO alloy has good electrical insulation like most polymer materials, and its surface resistivity is generally 10 13 -10 15 Ω.m, the conductivity is much smaller than that of metal materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permanent antistatic polyphenylene sulfite (PPS)/poly-p-phenylene oxide (PPO) alloy and production method thereof
  • Permanent antistatic polyphenylene sulfite (PPS)/poly-p-phenylene oxide (PPO) alloy and production method thereof
  • Permanent antistatic polyphenylene sulfite (PPS)/poly-p-phenylene oxide (PPO) alloy and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0023] The raw material formula of the antistatic masterbatch of Examples 1-5 is as follows:

[0024]

[0025] In the above embodiment, the alkali metal salt is M + X - , Where M + Li + , Na + , K + ; X - For Cl - , Br - , I - , CLO 4 - , Preferably LiCLO 4 .

[0026] In the above embodiment, the antioxidant is a 1:1 compound of phenothiazine and phosphite (s9228) in weight ratio;

[0027] In the above embodiment, the heat stabilizer is a compound of organotin heat stabilizer, calcium stearate, and zinc stearate in a weight ratio of 2:1:1;

[0028] In the foregoing embodiment, the auxiliary antistatic agent is silica;

[0029] In the above embodiment, the polymer material containing polyether block is a compound of polyethylene oxide and polyethylene glycol methacrylic acid copolymer at a weight ratio of 5:1; the molecular weight of the two polymers is preferably Between 6-16 million.

[0030] Put the above components into a high-mixer in proportion to mix for 2-5 minutes, discharge the...

Embodiment 5

[0036] Example 5 has the lowest surface resistivity and the highest cost performance.

Embodiment 6

[0053] Weigh the raw materials according to the weight ratio: 1% of the above-mentioned antistatic masterbatch, PPS 40%, PPO 58%, and 1% of the compatibilizer. Weigh the raw materials according to the weight ratio and put them in the high mixer for 2-5 minutes. , Discharge the material, and then extrude and pelletize with a twin-screw extruder, the processing temperature is 285-325℃, and the screw rotation speed is 40Hz. The surface resistivity of the prepared material is 10 14 Ω.m.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a permanent antistatic polyphenylene sulfite (PPS) / poly-p-phenylene oxide (PPO) alloy and a production method thereof, wherein the material comprises the following component in percentage by weight: 3-8% of antistatic masterbatch, 40-45% of PPS, 40-50% of PPO and 1-5% of compatilizer, raw materials are placed into a high speed mixer according to the weight percentage to mix for 2-5 min, are discharged, and are extruded and granulated through a double-screw extruder, the processing temperature is between 285-325 DEG C, and the rotational frequencies of screws are 35-40Hz. Compared with the prior art, the invention has the advantages of permanent antistatic effect, realization of permanent antistatic effect, good antistatic effect and higher comprehensive mechanical property; and being approximate to the performance of the pure PPS / PPO alloy, having light color, being capable of being made up into other colors, and having low cost, good heat-resistant quality and the like. The surface resistivity of the PPS / PPO alloy can reach 106-108 omega.m.

Description

Technical field [0001] The invention relates to a permanent antistatic masterbatch and a preparation method, in particular to a permanent antistatic PPS / PPO alloy preparation method. Background technique [0002] PPO has the advantages of high rigidity, high heat resistance, good water resistance, flame resistance, high strength, and excellent electrical properties. It also has the advantages of wear resistance, non-toxicity, and pollution resistance. Its dielectric constant and dielectric loss are in the engineering It is one of the smallest varieties of plastics, and it is hardly affected by temperature and humidity, and can be used in low, medium and high frequency electric fields. The load deformation temperature of PPO can reach above 190℃, and the embrittlement temperature is -170℃. PPS has the advantages of high mechanical strength, high temperature resistance, high flame retardancy, and strong chemical resistance; it has the advantages of hard and brittle, high crystalli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L81/02C08L71/12C08L71/02C08K13/02C08K3/24C08K3/16C08K5/524C08K5/46C08K5/098C08K3/36C08J3/22B29C47/92B29B9/06B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 郭建鹏杨涛孟成铭蔡爽
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com