Method for preparing peacock blue crystal bead embryo

A technology of crystal beads and blue, applied in glass pressing, glass manufacturing equipment, manufacturing tools, etc., can solve the problems of poor coloring reproducibility, low production efficiency, unstable product quality, etc., achieve stable lead silicate, improve Efficiency and productivity, good reproducible results

Inactive Publication Date: 2012-05-09
ZHEJIANG WEIXING CRYSTAL
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a method for the disadvantages of poor coloring reproducibility, unstable product quality, low production efficiency, and unsuitability for continuous tank kiln production operations in the existing technology for preparing peacock blue crystal bead embryos. A method for preparing peacock blue crystal bead embryos with good coloring reproducibility, stable product quality, high production efficiency, and suitable for continuous tank kiln production operations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of preparation method of peacock blue crystal bead embryo, the preparation method of peacock blue crystal bead embryo comprises the following steps:

[0020] (1) The raw materials of peacock blue crystal bead embryos are weighed out according to the weight ratio and mixed evenly, wherein, the raw material formula (weight ratio) of peacock blue crystal bead embryos is: 55 parts of quartz sand, 12 parts of soda ash, potassium nitrate 2 parts, 2 parts of boric acid, 1 part of lead silicate, 1 part of aluminum hydroxide, 2 parts of calcium carbonate, 1 part of lithium carbonate, 2 parts of barium carbonate, 2 parts of titanium dioxide, 1 part of magnesium carbonate, 2 parts of copper oxide;

[0021] (2) the evenly mixed peacock blue crystal bead embryo raw material is granulated by a granulator;

[0022] (3) Put the granular peacock blue crystal bead embryo raw material into a glass crystal pool furnace for melting. During melting, the temperature is controlled at 13...

Embodiment 2

[0025] A kind of preparation method of peacock blue crystal bead embryo, the preparation method of peacock blue crystal bead embryo comprises the following steps:

[0026] (1) The raw materials of peacock blue crystal bead embryos are weighed out according to the weight ratio and mixed evenly, wherein, the raw material formula (weight ratio) of peacock blue crystal bead embryos is: 70 parts of quartz sand, 15 parts of soda ash, potassium nitrate 14 parts, 7 parts of boric acid, 8 parts of lead silicate, 3 parts of aluminum hydroxide, 3 parts of calcium carbonate, 1.5 parts of lithium carbonate, 5 parts of barium carbonate, 7 parts of titanium dioxide, 3 parts of magnesium carbonate, 3 parts of copper oxide;

[0027] (2) the evenly mixed peacock blue crystal bead embryo raw material is granulated by a granulator;

[0028] (3) Put the granular peacock blue crystal bead embryo raw material into a glass crystal pool furnace for melting. During melting, the temperature is controlle...

Embodiment 3

[0031] A kind of preparation method of peacock blue crystal bead embryo, the preparation method of peacock blue crystal bead embryo comprises the following steps:

[0032] (1) The raw materials of peacock blue crystal bead embryos are weighed out according to the weight ratio and mixed evenly, wherein, the raw material formula (weight ratio) of peacock blue crystal bead embryos is: 60 parts of quartz sand, 13 parts of soda ash, potassium nitrate 7 parts, 4 parts of boric acid, 5 parts of lead silicate, 2 parts of aluminum hydroxide, 1 part of calcium carbonate, 0.5 parts of lithium carbonate, 2 parts of barium carbonate, 3 parts of titanium dioxide, 1 part of magnesium carbonate, 3 parts of copper oxide;

[0033] (2) the evenly mixed peacock blue crystal bead embryo raw material is granulated by a granulator;

[0034] (3) Put the granular peacock blue crystal bead embryo raw material into a glass crystal pool furnace for melting. During melting, the temperature is controlled a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing a peacock blue crystal bead embryo, aiming at the defects of poor coloring reproducibility, unstable product quality, low production efficiency and unsuitability of production work of a continuous tank furnace in the conventional process for preparing the peacock blue crystal bead embryo, and providing the method for preparing the peacock blue crystal bead embryo with good coloring reproducibility, stable product quality, high production efficiency and suitability of production work of the continuous tank furnace. In the method for preparing the peacock blue crystal bead embryo, the peacock blue crystal bead embryo comprises the raw materials in proportions by weight: 50-70 parts of quartz sand, 5-15 parts of soda ash, 2-14 parts of potassium nitrate, 2-8 parts of boracic acid, not more than 10 parts of lead silicate, not more than 3 parts of aluminum hydroxide, not more than 5 parts of calcium carbonate, not more than 1.5 parts of lithium carbonate, not more than 5 parts of barium carbonate, not more than 7 parts of titanium white, not more than 3 parts of magnesium carbonate and not more than 6 parts of copper oxide.

Description

technical field [0001] The invention relates to the field of artificial crystal products, in particular to a method for preparing peacock blue crystal bead embryos. Background technique [0002] Peacock blue crystal bead embryos are semi-finished products used to prepare peacock blue crystal products. The existing technology for preparing peacock blue crystal bead embryos has poor coloring reproducibility, unstable product quality, and low production efficiency. It is not suitable for continuous tank kilns. Inadequacies in production operations. In addition, in the existing process for preparing peacock blue crystal bead embryos, there is red lead component in the raw material formula of peacock blue crystal bead embryos, and red lead is volatile and will cause environmental pollution. Contents of the invention [0003] The purpose of the present invention is to provide a method for the disadvantages of poor coloring reproducibility, unstable product quality, low producti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C6/04C03B11/00
CPCC03C10/0054C03C1/10
Inventor 杨鑫法
Owner ZHEJIANG WEIXING CRYSTAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com