Optical film, polarizing plate, image display device, and method for manufacturing optical film

An optical film and transparent substrate technology, applied in the field of optical films, can solve problems such as unfavorable display image visibility or image quality, and achieve the effects of suppressing interference unevenness, suppressing bending, and suppressing film bending

Inactive Publication Date: 2012-05-09
FUJIFILM CORP
View PDF47 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This interference unevenness is detrimental to the visibility or image quality of the displayed image of the image display device, and thus needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optical film, polarizing plate, image display device, and method for manufacturing optical film
  • Optical film, polarizing plate, image display device, and method for manufacturing optical film
  • Optical film, polarizing plate, image display device, and method for manufacturing optical film

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0268] One example of the production method of the esterified compound is as follows.

[0269] Acetic anhydride (200 mL) was added dropwise to a solution of glucose (29.8 g, 166 mmol) to which pyridine (100 mL) had been added, and the mixture was allowed to react for 24 hours. Thereafter, the resulting solution was concentrated by evaporation and poured into ice water. After allowing the resulting solution to stand for 1 hour, solids were separated from water by filtration with a glass filter. The solid on the glass filter was dissolved in chloroform and subjected to liquid separation with cold water until the system became neutral. The organic phase was separated and dried over anhydrous sodium sulfate. After removing anhydrous sodium sulfate by filtration, chloroform was removed by evaporation, and the residue was further dried under reduced pressure to obtain glucose pentaacetate (58.8 g, 150 mmol, yield: 90.9%). In this regard, the aforementioned monocarboxylic acids ca...

Embodiment 1

[0402] [Preparation of optical film]

[0403] Coating liquids for forming the respective layers were formulated to form the respective layers shown below, whereby Optical Film Samples 1-13 were prepared.

[0404] (preparation of coating solution for hard coat)

[0405] The following composition was put into the mixing tank, stirred, and filtered through a filter made of polypropylene having a pore size of 0.4 μm, thereby preparing a coating solution A-1 for a hard coat layer (solid concentration: 58% by mass).

[0406]

[0407] In a similar manner to the coating liquid A-1 of the hard coat layer, as shown in Table 1 below, the components were mixed and dissolved in a solvent so as to have the ratios shown in Table 1, thereby preparing a hard coat layer Coating solutions A-2 to A-14.

[0408]

[0409]

[0410] Each compound used is shown below.

[0411] Leveling agent (SP-13):

[0412]

[0413] PET30: a mixture of compounds having the following structure produce...

Embodiment 2

[0478] Substrates 1-3 were prepared using dopes B-1 and B-2 shown in Table 3 below in the manner described in paragraphs 41-42 of this specification, respectively.

[0479] table 3

[0480]

[0481] Table 3 (continued)

[0482]

[0483] Optical Films 14 to 18 were prepared in the same manner as Film Sample 1 except for using each of the base materials and coating liquids of the hard coat layer shown in Table 4 below, and in the same manner as those in Table 2, Evaluations were made in terms of interference unevenness and pencil hardness. Here, the base material used in Sample 16 was ZRD60SL (cellulose acylate film having an acetyl substitution degree of 2.86 and a film thickness of 60 μm) produced by Fujifilm Corporation.

[0484] Table 4

[0485]

[0486] As shown in Table 4, even in the case of using a thin base material of 40 μm or 60 μm, the optical film of the present invention had high hardness, suppressed interference unevenness, and exhibited excellent perfor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

An optical film contains a transparent base material having thereon a hard coat layer formed of a hard coat layer forming composition containing the specific components, wherein a refractive index of the hard coat layer is 1.45 or more and not more than 1.55; and in the hard coat layer forming composition, a content of the component (a) is a content of the component (b) or more.

Description

technical field [0001] The invention relates to an optical film, a polarizer, an image display device and a method for making the optical film. Background technique [0002] In image display devices such as cathode ray tube display (CRT), plasma display (PDP), electroluminescence display (ELD), vacuum fluorescent display (VFD), field emission display (FED) and liquid crystal display (LCD) Among them, in order to prevent abrasion of the display surface, it is suitable to provide a hard coat film with a hard coat layer on a transparent base material. [0003] In addition, in the case of high-definition and advanced image display devices such as recent LCDs, in addition to the above-mentioned prevention of display surface wear, in order to prevent contrast reduction or image glare due to reflection of external light on the display surface, An antireflection layer or an optical film with an antireflection layer is provided on the hard coat layer. [0004] In such an optical fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G02B1/10G02B5/30G02F1/1335G09F9/30C09D4/02B32B7/02B32B23/08G02B1/111G02B1/14H01L51/50H05B33/02H05B33/14
CPCG02F1/133502G02B1/111G02B5/285Y10T428/31551
Inventor 太田绚子铃木贵登
Owner FUJIFILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap