Inorganic/organic composite porous lithium battery diaphragm and preparation method thereof

A lithium battery separator and porosity technology, which is applied in the field of inorganic/organic composite polypropylene (PP) non-woven fabric-based lithium battery separator and its preparation, can solve the trouble of making PE-PP sheath core composite fibers and is not suitable for lithium batteries Diaphragm, non-woven fabric with large pore size and other problems, to achieve the effects of excellent charge-discharge cycle performance, improved mechanical strength, and high liquid absorption rate

Active Publication Date: 2012-07-04
SUZHOU UNIV
View PDF5 Cites 46 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mechanical strength of PVdF-HFP containing nano-Al2O3 particles is low, and the application is affected by it
[0011](2) Japanese scientist Tae-Hyung Cho et al. made non-woven fabrics with nano-SiO2 and PE-PP sheath-core composite fibers Film and PAN nanofiber non-woven film, the composite film made by hot calendering method has excellent water absorption and ion conductivity, as well as good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic/organic composite porous lithium battery diaphragm and preparation method thereof
  • Inorganic/organic composite porous lithium battery diaphragm and preparation method thereof
  • Inorganic/organic composite porous lithium battery diaphragm and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 6

[0038] Embodiments one to six: SiO 2 Preparation of / PVdF-HFP / PP non-woven composite lithium battery separator

Embodiment 1

[0039] Example 1: Preparation of PVdF-HFP / PP non-woven composite diaphragm

[0040] Dry the reaction bottle and stirring bar in an oven at 120 °C for at least 6 hours, and dry polyvinylidene fluoride-hexafluoropropylene copolymer (PVdF-HFP, Solvay, trade name Solef 21216 / 1001) at 80 °C for at least 6 hours. Let dry for 6 hours. Cool to room temperature after taking it out, and weigh it immediately for use.

[0041] Weigh 4.000 grams of PVdF-HFP and 0.400 grams of hydrophilic agent F127, put them in a round bottom flask, then add 4.000 grams of DMF (N,N-dimethylformamide) and 36.000 grams of acetone, and stir at room temperature for 1 hour , and then heated to 60 ° C and continued to stir for 2 hours to obtain a uniform mixed solution, which was cooled to room temperature.

[0042] PP non-woven fabric of suitable size (approximately 9 mm x 12 mm in area) is placed on a dry PE board, pipette the mixed solution onto the non-woven fabric with a rubber dropper, and use an adjusta...

Embodiment 2

[0043] Example 2: SiO 2 / PVdF-HFP / PP non-woven fabric (PVdF-HFP:SiO 2 =100: 2) Preparation of composite separator

[0044] Dry the reaction bottle and stirrer in an oven at 120 °C for at least 6 hours in advance, PVdF-HFP and SiO with a particle size of 18nm 2 Dry at 80°C for at least 6 hours. Cool to room temperature after taking it out, and weigh it immediately for use.

[0045] Weigh 4.000 g of PVdF-HFP, 0.080 g of SiO 2 and 0.400 grams of F127 in a round-bottomed flask, then added 4.000 grams of DMF (N,N-dimethylformamide) and 36.000 grams of acetone, stirred at room temperature for 1 hour, then raised the temperature to 60°C and continued to stir for 2 hours. A homogeneous mixed solution was obtained and cooled to room temperature.

[0046] PP non-woven fabric of suitable size (approximately 9 mm x 12 mm in area) is placed on a dry PE board, pipette the mixed solution onto the non-woven fabric with a rubber dropper, and apply the solution with an adjustable film appl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of lithium batteries, and relates to an inorganic/organic composite porous lithium battery diaphragm and a preparation method thereof. The inorganic/organic composite porous lithium battery diaphragm comprises a base material layer and an inorganic/organic composite porous diaphragm layer arranged on the surface of the base material layer, wherein the base material layer adopts polypropylene non-woven fabrics; the inorganic/organic composite porous diaphragm layer adopts a polyvinylidene fluoride- hexafluoropropylene multipolymer containing inorganic nano grains and hydrophilizing agents; and the inorganic nano grains are silicon dioxide nano grains or coupling agent improved silicon dioxide nano grains. The inorganic/organic composite porous lithium battery diaphragm provided by the invention has the advantages that the production cost of the lithium battery diaphragm is lowered while high ion-conductivity, excellent electrochemical performance, high mechanical strength and low thermal shrinking percentage are ensured.

Description

technical field [0001] The invention belongs to the field of lithium batteries, and relates to an inorganic / organic composite polypropylene (PP) non-woven fabric-based lithium battery diaphragm and a preparation method thereof. Background technique [0002] The lithium-ion battery separator is one of the core components of the lithium battery. It is called the "third electrode" of the battery. It is an electrically insulating film with a porous structure. Its main function is to separate the positive and negative electrodes and prevent the battery from short-circuiting. , and at the same time allow the ion load body to pass quickly when the battery is connected to the circuit. The performance of the separator is a key factor affecting the performance of the battery, which requires the separator to have high ionic conductivity, good mechanical strength, appropriate pore size and porosity, and high temperature resistance. [0003] At present, the separators widely used in lit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/02B32B27/12B32B27/18B32B3/24H01M2/16
CPCY02E60/12Y02E60/10
Inventor 张明祖徐玲妍倪沛红何金林孟菊雯
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap