Preparation method and film-forming liquid for aluminum alloy high-performance trivalent chromium hybrid conversion film

A technology of film-forming liquid and aluminum alloy, which is applied in the coating process of metal materials, etc., can solve the problems of anti-corrosion performance, high cost, and large pollution, and achieve the effect of improving anti-corrosion performance, low cost, and low concentration

Inactive Publication Date: 2012-07-04
GUANGXI UNIV FOR NATITIES
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These preparation methods have high concentration, high cost, and large pollution, and their anti-corrosion performance needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and film-forming liquid for aluminum alloy high-performance trivalent chromium hybrid conversion film
  • Preparation method and film-forming liquid for aluminum alloy high-performance trivalent chromium hybrid conversion film
  • Preparation method and film-forming liquid for aluminum alloy high-performance trivalent chromium hybrid conversion film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1 Trivalent chromium chromization of 2024 aluminum alloy

[0019] A. Build a 450L degreasing bath: Please clean the container thoroughly before building the bath. For new containers or new production lines, first wash with 50L of 10% sulfuric acid solution, then wash with water twice, each time with 100L of water, and then add Henkel's degreasing agent 9KGRidoline212, and then diluted to 450L with deionized water, the pH is controlled within the range of 7 to 8, and mixed evenly.

[0020] B. Build a 450L activation bath: Please clean the container thoroughly before building the bath. For a new container or a new production line, first clean it with 10% sulfuric acid solution, then clean it with water, add the required 9KG of sodium hydroxide, Then dissolve it with deionized water and dilute it to 450L with deionized water, and stir evenly. The temperature was maintained at 30°C.

[0021] C. Build a 450L chromium bath: Please clean the container thoroughly befo...

Embodiment 2

[0026] Example 2 Trivalent chromium chromization of 3003 aluminum alloy

[0027] A. Build a 450L degreasing bath: Please clean the container thoroughly before building the bath. For new containers or new production lines, first wash with 50L of 10% sulfuric acid solution, then wash with water twice, each time with 100L of water, and then add Henkel's degreasing agent 8KGRidoline212, and then diluted to 450L with deionized water, the pH is controlled within the range of 7-8, and mixed evenly.

[0028] B. Building an activation bath: Please clean the container thoroughly before building the bath. For a new container or a new production line, first clean it with 10% sulfuric acid solution, then clean it with water, add the required 12KG of sodium hydroxide, and then Dissolve with deionized water and then dilute to 450L with deionized water, stir evenly. The temperature was maintained at 20°C.

[0029] C. Build a 450L chromium bath: Please clean the container thoroughly before b...

Embodiment 3

[0034] Example 3 Trivalent chromium chromization of 4032 aluminum alloy

[0035] A. Build a 450L degreasing bath: Please clean the container thoroughly before building the bath. For new containers or new production lines, first wash with 50L of 10% sulfuric acid solution, then wash with water twice, each time with 100L of water, and then add Henkel's degreaser 9KGRidoline212, then diluted to 450L with deionized water, PH control in the range of 7-8, mix well.

[0036] B. Build a 450L activation bath: Please clean the container thoroughly before building the bath. For a new container or a new production line, first clean it with 10% sulfuric acid solution, then clean it with water, add the required 15KG of sodium hydroxide, Then dissolve it with deionized water and dilute it to 450L with deionized water, and stir evenly. The temperature was maintained at 15°C.

[0037] C. Build a 450L chromium bath: Please clean the container thoroughly before building the bath. For new conta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method and film-forming liquid for an aluminum alloy high-performance trivalent chromium hybrid conversion film. The film-forming liquid is added with phosphotungstate serving as an inorganic corrosion inhibitor, and organophosphorus; and when an aluminum or aluminum alloy workpiece is treated by the film-forming liquid, a trivalent chromium, phosphotungstate and organophosphorus hybrid conversion film can be formed on the surface of an aluminum alloy. Compared with a single trivalent chromium conversion film, the hybrid conversion film can improve the corrosion resistance of the aluminum alloy and achieve the anti-corrosion effect of a hexavalent chromium chemical conversion film.

Description

technical field [0001] The invention relates to aluminum alloy surface treatment, in particular to a method for preparing an aluminum alloy high-performance trivalent chromium hybrid conversion film and a film-forming solution thereof. Background technique [0002] In order to improve the corrosion resistance of aluminum and other metals such as zinc and steel, the traditional method is to use hexavalent chromium conversion coating. However, hexavalent chromium is toxic. In the electrical and electronic industries, the EU RoHS regulations (Restriction of Hazardous Substances, "Instructions on Restricting the Use of Certain Hazardous Substances in Electrical and Electronic Equipment") prohibit the use of hexavalent chromium compounds. In order to meet the needs of environmentally friendly processes, various hexavalent chromium-free conversion coatings have been developed. Recent research involves new conversion coatings such as titanium, tungsten, tin, zinc and rare earth sa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/40
Inventor 余会成黄小小雷福厚谭学才韩燕燕韦冬萍
Owner GUANGXI UNIV FOR NATITIES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More