Anti-impact and wear-resistant mortar

A wear-resistant sand and Portland cement technology, which is applied in the field of mortar of hydropower engineering material technology, can solve the problems of poor crack resistance, high elastic modulus, prone to cracks, etc., and achieves low elastic modulus and crack resistance. The effect of excellent performance and steady increase in strength

Active Publication Date: 2012-09-19
POWERCHINA CHENGDU ENG +1
View PDF4 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the existing technology represented by the above-mentioned patent documents still has the technical problems of "the early strength development is too fast, the middle and late strength growth is small, the heat of hy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-impact and wear-resistant mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] Embodiment 1: The components and parts by weight of the anti-impact and wear-resistant mortar in this embodiment are: 47 parts of low-heat Portland cement, 50 parts of sand in basalt, 1.5 parts of redispersible latex powder, powdery polycarboxylate water-reducing 0.2 parts of antifoaming agent, 0.3 parts of polyether defoamer, nano-SiO 2 0.4 parts, nano CaCO 3 0.6 parts.

[0067] Preparation method: Weigh each component according to the above-mentioned parts by weight, mix in a mixer, and form a product after mixing evenly;

[0068] How to use: Add appropriate amount of water to the anti-scour and wear-resistant mortar to make the consistency meet the requirements of use; the conventional construction method of anti-scouring and wear-resistant materials is used for construction, and it is mainly used for repairing hydropower projects.

Embodiment 2

[0069] Embodiment 2: The components and parts by weight of the anti-impact and wear-resistant mortar in this embodiment are: 44 parts of low-heat Portland cement, 44 parts of sand in basalt, 1.0 part of redispersible latex powder, and powdery polycarboxylate water-reducing 0.10 parts of antifoaming agent, 0.20 parts of polyether defoamer, nano-SiO 2 0.7 parts, 5 parts of fly ash, 5 parts of slag.

[0070] The preparation method and usage method are the same as in Example 1.

Embodiment 3

[0071] Embodiment 3: The components and parts by weight of the anti-impact and wear-resistant mortar of this embodiment are: 40 parts of medium-heat Portland cement, 42 parts of quartz medium sand, 1.5 parts of redispersible latex powder, and powdery polycarboxylate 0.15 parts of water agent, 0.25 parts of polyether defoamer, nano-SiO 2 0.5 parts, 5 parts of fly ash, 10 parts of slag, 0.6 parts of sodium sulfate.

[0072] The preparation method and usage method are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-impact and wear-resistant mortar, belonging to the field of a repairing material in water-power engineering. The difficulty that the constructions in the conventional water-power engineering is difficult to repair after being damaged by rushing and abrading with water with sands and stones can be solved. The anti-impact and wear-resistant mortar comprises the following components in parts by weight: 39-48 parts of silicate cement, 45-50 parts of graded hard fine aggregate, 0.05-0.25 parts of water reducing agent, 0.05-0.3 parts of de-foaming agent and 0.05-1.5 parts of nanometer material. The anti-impact and wear-resistant mortar provided by the invention has the advantages of high anti-impact and wear-resistant strength, low elasticity modulus and good anti-crack property, and is a finished product material with a higher application value for repairing through irrigation works.

Description

technical field [0001] The invention relates to the technical field of mortar in hydropower engineering material technology. The mortar is mainly used for repairing water scoured parts, and can also be used as a pouring material for anti-scouring concrete. Background technique [0002] In hydraulic construction projects, the concrete on the overflow dam surface, water delivery tunnel, spillway or apron, etc., is often subjected to high-speed water flow or high-speed water flow carrying sand and stones, and is prone to damage such as wear and cavitation This phenomenon not only directly or indirectly affects the normal and safe operation of the project, but also requires huge maintenance and repair costs. [0003] Many problems have been exposed in the performance of existing anti-abrasion materials during the engineering construction process and in the later stages of the site. For example, the early strength development of the silica fume series anti-abrasion concrete i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B111/72
Inventor 杨代六曲良焕阳运霞吴勇田先忠黎茜杜青林
Owner POWERCHINA CHENGDU ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap