Chemical nitridation catalyst

A technology of infiltration catalyst and chemical infiltration, applied in metal material coating process, coating, solid diffusion coating and other directions, can solve the problems of workpiece rust, short duration of infiltration effect, etc., to save electricity, heat preservation, etc. Shortened time and good nitriding effect

Inactive Publication Date: 2012-09-26
远立贤
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although the above method has the effect of promoting infiltration, the phenomenon of furnace blockage is relative

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chemical nitridation catalyst
  • Chemical nitridation catalyst
  • Chemical nitridation catalyst

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example 1,

[0013] Take 5% calcium carbonate, 25% sodium carbonate, 3% calcium oxide, 17% calcium chloride, 30% ammonium chloride, 5% rare earth carbonate, 15% rare earth chloride in proportion, and mix the above seven compounds uniformly , Put it into a section of stainless steel tube, plug both ends with aluminum silicate fiber felt, and then spot weld both ends on the stainless steel tube with stainless steel discs, and divide them into 200g and 300g packages. Load the workpiece and tooling into the bottom of the 100kw nitriding furnace. After holding at 560-580°C for 12 hours, compare the depth of the infiltration layer and the structure and hardness of the infiltration layer between the test block and no accelerator. As a result, the depth of the permeation layer with the addition of permeation agent is obviously deeper than that without the permeation agent, which is equivalent to the depth of the permeation layer without adding permeation agent for 30 hours.

Example Embodiment

[0014] Example 2,

[0015] Take 10% calcium carbonate, 15% sodium carbonate, 5% calcium oxide, 15% calcium chloride, 35% ammonium chloride, 10% rare earth carbonate, 10% rare earth chloride in proportion, and mix the above seven compounds uniformly , Put it into a section of stainless steel tube, plug both ends with aluminum silicate fiber felt, and then spot weld both ends on the stainless steel tube with stainless steel discs, and divide them into 200g and 300g packages. The workpiece and tooling are also loaded into the bottom of the 100kw nitriding furnace, and after holding at 560-580°C for 12 hours, the depth of the infiltration layer and the structure and hardness of the infiltration layer are compared with the test block without the infiltration agent. As a result, the depth of the permeation layer with the addition of permeation agent is also significantly deeper than that without the permeation agent, which is equivalent to the depth of the permeation layer without addi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a chemical nitridation catalyst which comprises the following components in proportion: 5 to 15 percent of calcium carbonate, 12 to 25 percent of sodium carbonate, 3 to 5 percent of calcium oxide, 10 to 30 percent of calcium chloride, 15 to 38 percent of ammonium chloride, 5 to 10 percent of rare earth carbonate and 10 to 15 percent of rare earth chloride. The seven compounds are uniformly mixed and put into a stainless steel pipe; two ends are plugged and locked by aluminium silicate fiber felts and spot-welded on the stainless steel pipe by stainless steel wafers; and the chemical nitridation catalyst is packaged every 200 grams and 300 grams. Discharged waste gas is reduced by about more than 52.5 kilograms, so that the environment is improved. The chemical nitridation catalyst is short in nitridation time and good in nitridation effect; electric energy is saved; a nitridation layer tissue is relatively thinned and dispersed; and the brittleness level, the nitride level and the looseness level can be well controlled.

Description

technical field [0001] The invention relates to a chemical nitriding and permeating agent. Background technique [0002] Nitriding is a common chemical heat treatment method for the surface of metal workpieces. At a certain temperature, active nitrogen atoms are infiltrated into the surface of metal workpieces to form a compound layer, which changes the phase structure of the surface of metal workpieces, thereby improving the mechanical properties of the surface of metal workpieces, corrosion resistance, Obtain good wear resistance, fatigue resistance. The patent application number 201110097678.2 published by the Patent Office of the State Intellectual Property Office is an invention patent for "Solid Rare Earth Nitriding Catalyst", which is composed of the following ingredients uniformly mixed by weight percentage, 50-90% of rare earth chloride, -30% and urea 5-20%. The rare earth permeation agent is a paste solid, packed in a wax-sealed paper box with a plastic film, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C8/24
Inventor 远立贤闫牧夫张志军郎大伟高臣蒋绍楼
Owner 远立贤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap