Polyester film with adhesion resisting function and preparation method of polyester film

A polyester film, anti-blocking technology, applied in chemical instruments and methods, layered products, synthetic resin layered products, etc., can solve the problems of high added value, less deep-processing products, unfavorable industry development, etc., and achieve good thermal stability. the effect of reducing environmental pollution

Active Publication Date: 2012-10-24
JIANGSU SHUANGXING COLOR PLASTIC NEW MATERIALS
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the above two methods use ordinary polyester film, and there are few high-value-added and deep-processed products.
On the one hand, this situation has limited the domestic polyester industry to low-level vicious competi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Polyester chips for ordinary films containing 35% general anti-adhesive agent and polyester chips for functional films containing 15% high-performance anti-adhesive agent, 5% anti-adhesive masterbatch and 50% general anti-adhesive The ordinary film of the binder uses polyester chips as raw materials, and the weight ratio of raw and auxiliary materials for each layer is A layer: 65% polyester for ordinary film, 35% general anti-adhesive agent; B layer: masterbatch polyester for functional film Chip 80%, anti-adhesion masterbatch 5%, high-performance anti-adhesive agent 15%; C layer: ordinary film polyester 50%, general anti-adhesive agent 50%.

[0054] 1. Slicing:

[0055] Polyester slices for ordinary films containing general anti-adhesive agents: Put high-purity terephthalic acid and ethylene glycol into the reactor at a ratio of 1:1mol to carry out esterification reaction. At the end stage, nano-scale SiO 2 The ethylene glycol dispersion and magnesium acetate ethyle...

Embodiment 2

[0078] Polyester chips for ordinary films containing 20% ​​general anti-adhesive agent and polyester chips for functional films containing 12% high-performance anti-adhesive agent, 3% anti-adhesive masterbatch and 35% general anti-adhesive The ordinary film of the binder uses polyester chips as raw materials, and the weight ratio of raw and auxiliary materials for each layer is A layer: 80% polyester for ordinary film, 20% general anti-adhesive agent; B layer: masterbatch polyester for functional film Chip 85%, anti-adhesion masterbatch 3%, high-performance anti-adhesive agent 12%; C layer: polyester for ordinary film 65%, general anti-adhesive agent 35%.

[0079] 1. Slicing:

[0080] Polyester slices for ordinary films containing general anti-adhesive agents: Put high-purity terephthalic acid and ethylene glycol into the reactor at a ratio of 1:1mol to carry out esterification reaction. At the end stage, nano-sized SiO 2 The ethylene glycol dispersion and magnesium acetate e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Stretch temperatureaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyester film with an adhesion resisting function. The polyester film is of a structure comprising a layer A, a layer B and a layer C, wherein the layer A and the layer C are surface layers; the layer B is a core layer; the layer A comprises the components of 65-80 percent of polyester slice for a general film and 20-30 percent of general adhesion resisting agent; the layer B comprises the components of 80-85 percent of master batch polyester slice for a functional film, 3-5 percent of general adhesion resisting master batch and 12-15 percent of high-performance adhesion resisting agent; and the layer C comprises the components of 50-65 percent of polyester slice for the general film and 35-50 percent of general adhesion resisting agent. The high heat resistance and excellent adhesion resistance are achieved by the steps of slicing, mixing, melting co-extrusion, longitudinal drawing, transverse drawing, drawing and trimming, coiling, splitting and forming a finished product. The products prepared by the preparation method disclosed by the invention is environment-friendly and can be directly recycled, so that the pollution to the environment is reduced; and the polyester film can be widely applied to packaging of cakes, seasonings, fast foods and candies and packaging of medical products.

Description

technical field [0001] The invention relates to a three-layer co-extruded biaxially stretched PET film and a preparation method thereof, in particular to an anti-blocking functional polyester film and a preparation method thereof. Background technique [0002] As a new type of industrial material, polyester film continues to expand its application fields. my country's polyester film industry follows the pace of developed countries and combines independent innovation to make full use of the good performance of polyester film materials and the characteristics of meeting environmental protection requirements, vigorously promote and guide consumption, and promote the application of polyester film to a wider range. The market demand is increasing year by year. [0003] Chinese patent application 201019026142.4 discloses an anti-blocking masterbatch for light-diffusing polyester base film and its film preparation method. The film uses the anti-blocking agent masterbatch as an addi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/18B32B27/36C08L67/00C08K9/00C08K3/22C08K3/36C08K3/26C08K3/32C08K3/30C08K3/34C08K5/098C08J3/22C08G63/183B29C69/02B29C55/14B29C47/92B29C47/06B29C48/08B29C48/92
CPCB29C48/08
Inventor 吴培服
Owner JIANGSU SHUANGXING COLOR PLASTIC NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap