Adhesive and method for preparing iron-based copper microelectrolytic sectional material

An adhesive and micro-electrolysis technology, applied in adhesives, inorganic adhesives, chemical instruments and methods, etc., can solve the problems of easy collapse of the electrochemical reaction bed, prolong the service life and time, solve the problem of hardening, The effect of suppressing collapse

Inactive Publication Date: 2013-01-02
WUHAN COMEON ENVIRONMENT ENG
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention effectively solves the problem that the electrochemical reaction bed with iron-based copper micro-base material is easy to collapse, and prolongs the service life of the iron-based copper micro-electrolysis profiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0032] Example: Preparation of adhesive and iron-based copper micro-electrolysis profiles

[0033] (1) Glue-like adhesive formula (mass ratio)

[0034] Light magnesium oxide (industrial grade) 15 kg

[0035] Magnesium chloride hexahydrate (industrial grade) 3.5 kg

[0036] Silica sol (industrial grade) 1 kg

[0037] Sodium hexametaphosphate 1.5 kg

[0038] Water (pH=5-7) 29 kg

[0039] (2) Preparation process of profiles

[0040] 1) Preparation of glue: Weigh light magnesia, magnesium chloride hexahydrate, silica sol and sodium hexametaphosphate according to the formula ratio, add in the quantitative water according to the formula ratio in turn, stir quickly until completely dissolved, and obtain a transparent glue .

[0041] 2) Preparation of the mold: the mold is rectangular, and its size is limited to facilitate operation and transportation. There are no special requirements for the materials of the panels around the mold, iron, plastic and wood can be used, and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an adhesive and a method for preparing an iron-based copper microelectrolytic sectional material. Based on requirements for sewage microelectrolytic treatment methods, silica sol and sodium hexametaphosphate are added to reach the purpose of modification of magnesium oxychloride cement. Through the cementation effect of products obtained by reactions among components, the iron-based copper particles are cemented, and a cementation skeleton of the iron-based copper particles is formed which has certain strength, can resist acidic water corrosion, and has certain conductivity; therefore, collapse of a bed layer is inhibited; the service life and time is prolonged; and the hardening problem is solved finally.

Description

[0001] technical field [0002] The invention belongs to the technical field of wastewater treatment, and in particular relates to an adhesive and a method for preparing iron-based copper micro-electrolysis profiles. [0003] Background technique [0004] In the electrochemical reaction bed (layer) of iron-based copper micro-base material, the cast iron particles that act as a supporting framework, during the process of treating sewage through micro-electrolysis, due to the continuous reaction and dissolution of iron particles, their support strength continues to decrease until they collapse. Formation of bed compaction. Hardening will block and seal a large number of pore throats that originally pass through the sewage with the help of dialysis and undergo micro-electrolysis, and finally force the water to pass through only a small number of larger fixed channels, which makes the sewage treatment capacity of the iron-based copper fixed reaction bed obvious. decline....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J1/00C02F1/461
Inventor 罗逸文志敏
Owner WUHAN COMEON ENVIRONMENT ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products