A kind of oil-resistant and alkali-resistant metal antirust paint and preparation method thereof

A metal anti-rust and alkali-resistant technology, applied in the field of metal anti-rust paint, can solve problems such as easy to fall off, not suitable for complex, harsh environments, poor weather resistance of water-based anti-rust paint, etc., to achieve strong adhesion and high hardness Effect

Active Publication Date: 2016-01-20
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, water-based antirust paint generally has poor weather resistance, is easy to fall off, and is not suitable for complex and harsh environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] Oil-resistant and alkali-resistant metal antirust paint, made of the following raw material components in parts by weight (kg):

[0027] Raw material for pulping:

[0028] Aluminum powder 5, 2,2,4-trimethyl 1,3-pentanediol monoisobutyrate 8, anti-settling agent 3300S2, leveling agent BYK-3002, paraffin wax emulsion 8, magnesium hydroxide 12, diffusing agent MF2, LBCB-1 thixotropic lubricant 2, sodium bentonite 1, aluminum tripolyphosphate 2, modified nano sepiolite powder 6, modified water-soluble nano silica sol 6;

[0029] Raw materials for paint mixing:

[0030] Water-based polyurethane resin 25, water-based fluorocarbon resin 12, phytate 25, propylene glycol 55, dicyclopentenyl ethoxy methacrylate 5, heavy alkylbenzene sulfonate 4, carboxymethyl cellulose 12, 2-Amino-2-methyl-1-propanol 2.

[0031] Modified nano sepiolite powder is prepared by the following method:

[0032] (1) Add 0.8g / L potassium permanganate solution to the sepiolite powder and soak for 2 hou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses oil-resisting and alkali-resisting metal anti-rust paint and a preparation method thereof. The anti-rust paint is prepared from slurrying raw materials and paint mixing raw materials; a paint film formed by the anti-rust paint has high hardness, scratching resistance, strong adhesion, salt fog resistance, saline resistance, acid-base resistance, water resistance, and oil resistance; the paint can be used on the surface of an old paint film repeatedly; the damage to the paint film can be avoided; and super strong toughness of the paint film can be achieved. The service life of the paint film can reach 8 to 10 years generally.

Description

technical field [0001] The invention relates to a metal antirust paint, in particular to an oil-resistant and alkali-resistant metal antirust paint. Background technique [0002] All kinds of mechanical equipment need to be coated with a layer of metal paint, on the one hand to increase the appearance, and on the other hand to prevent dust, rust and corrosion; the anti-rust paint in the prior art contains a large amount of volatile organic solvents, which produces a large amount of toxic and harmful Volatile gases pollute the air and damage human health. Water-based antirust paint has attracted people's attention and welcome because of its low pollution. However, water-based antirust paint generally has poor weather resistance, is easy to fall off, and is not suitable for complex and harsh environments. Contents of the invention [0003] The invention provides an oil-resistant and alkali-resistant metal antirust paint and a preparation method thereof, which have good mec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D127/12C09D101/26C09D7/12C09D5/10
Inventor 刘春芳
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap