Diatomite modified polyvinyl chloride synthetic leather and manufacturing method thereof

A technology of attapulgite and polyvinyl chloride, applied in chemical instruments and methods, synthetic resin layered products, dyed low-molecular organic compound treatment, etc., can solve product quality problems, residues, hydrolysis resistance, weather resistance, etc. problems, to achieve the effect of increasing flexibility, high bonding fastness, good vapor permeability and moisture absorption conductivity

Inactive Publication Date: 2014-12-10
HEFEI ANSHAN COATING FABRICS
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a large amount of DMF solvent with certain toxicity and volatility is used in its manufacturing process. Even after sufficient drying, there will be a large amount of DMF residue, which will become a source of excessive VOC pollution in indoor air; at the same time, polyurethane synthetic leather is resistant to hydrolysis, Insufficient weather resistance and other issues limit its further wide application
PVC synthetic leather modified by attapulgite and bentonite has excellent hydrolysis resistance, abrasion resistance, scratch resistance, flame retardancy, etc., but there are problems in product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] A polyvinyl chloride synthetic leather modified by attapulgite and bentonite, including a surface layer, a foam layer, an adhesive layer, and a raised cloth,

[0027] The surface layer is prepared from the following raw materials in parts by weight (kg):

[0028] SG-1 type PVC resin 40, SG-6 type PVC resin 70, propylene glycol sebacate polyester 15, acetyl triethyl citrate 10, dibutyl maleate 25, PVC color paste 6, bisthioglycolic acid Isooctyl di-n-octyl tin 2, dibasic lead phosphite 1, zinc stearate 1, nanometer calcium carbonate 10, modified attapulgite 15, carbon black N22015, fast extruded carbon black N66035, bis(dioctyl oxide base pyrophosphate) ethylene titanate 1, antioxidant 1680.5, 3-aminopropyltrimethoxysilane 2, crosslinking agent TAC0.5, silane coupling agent KH5502, protein powder 4;

[0029] The foam layer is made of the following raw materials in parts by weight (kg):

[0030] SG-1 type PVC resin 50, SG-4 type PVC resin 80, SG-7 type PVC resin 40, ace...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses diatomite modified polyvinyl chloride synthetic leather. The diatomite modified polyvinyl chloride synthetic leather comprises a surface layer, a foaming layer, a bonding layer and a brushing fabric and is characterized in that the surface layer is manufactured by blending the following raw materials in parts by weight into slurry: 40-50 parts of SG-1 type PVC (Polyvinyl Chloride) resin, 70-80 parts of SG-6 type PVC resin, 15-20 parts of sebacic acid propylene glycol polyester, 10-15 parts of acetyl triethyl citrate, 20-25 parts of di-n-butyl maleate, 5-6 parts of PVC color paste, 1-2 parts of imarcaptoacetate dioctyltin, 1-2 parts of dibasic lead phosphate, 1-2 parts of zinc stearate, 5-10 parts of nanometer calcium carbonate and 15-20 parts of modified attapulgite. Through an improvement of a formula and a technology, the flexibility of the synthetic leather is increased, and the diatomite modified polyvinyl chloride synthetic leather has the natural comfortable hand feel similar to that of natural leather and is not easily damaged or torn.

Description

technical field [0001] The invention belongs to the technical field of chemical synthetic leather fabric processing, in particular to a polyvinyl chloride synthetic leather modified by attapulgite and bentonite and a manufacturing method thereof. Background technique [0002] At present, polyurethane and polyvinyl chloride synthetic leather modified with attapulgite and bentonite are widely used in commercial furniture and household furniture. Polyurethane synthetic leather has the advantages of high imitation and good hand feeling, and has been widely favored by the market. However, a large amount of DMF solvent with certain toxicity and volatility is used in its manufacturing process. Even after sufficient drying, DMF will still have a large amount of residue, which will become a source of excessive VOC pollution in indoor air; at the same time, polyurethane synthetic leather is resistant to hydrolysis, Insufficient weather resistance and other problems limit its further ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More