Method for preparing activated carbon by utilizing camellia oleifera shells

A technology for preparing activated carbon and camellia husk, which is applied in chemical instruments and methods, inorganic chemistry, non-metallic elements, etc., to achieve the effects of developed pore structure, sufficient raw materials and low price

Inactive Publication Date: 2013-04-03
HUNAN AMAZING GRACE BIOTECH
6 Cites 32 Cited by

AI-Extracted Technical Summary

Problems solved by technology

[0004] In recent years, many patents related to the development and utilization of Camellia oleifera husks have been focused on the application of new materials. For example, patent application No. 201210027121.6 relates to a method for preparing a special slow-release fertilizer for Camellia oleifera by using Camellia oleifera husk; patent application No. 201010243982.9 discloses a The preparation method of biosorbent prepared from camellia ...
View more

Abstract

The invention discloses a method for preparing activated carbon by utilizing camellia oleifera shells. The method comprises the following steps: screening the camellia oleifera shells to remove impurities; mixing and soaking the shell particles and a certain proportion of activated agent; then firstly carbonizing, activating through secondary heating; and sequentially scouring, washing, drying and pelletizing the activated materials to obtain activated carbon. The activated carbon is prepared by the camellia oleifera shells which are obtained from leftovers in processing of camellia oleifera, thus source is sufficient; and the activated carbon is prepared by taking the camellia oleifera shells as raw materials and combining physical and chemical methods, is simple in process, good in stability, less in pollution, easy to regenerate, low in production cost, large in specific surface area and good in adsorptive property.

Application Domain

Carbon compounds

Technology Topic

Activated carbonPollution +4

Examples

  • Experimental program(2)

Example Embodiment

[0013] Example 1.
[0014] Select the oil-tea camellia husk and place it in a constant temperature electric heating drying box to reduce the dry moisture content to 6%. The pretreated husk is further crushed to 60 mesh, and the oil-tea husk powder and 80% phosphoric acid solution are in a weight ratio of 1:2.5. Stir and mix evenly After standing for 24 hours, the acid-leached camellia husks were heated and carbonized in a 250°C dry box for 80 minutes; the carbonized camellia husks were placed in a resistance furnace and the temperature was increased to 550°C for 60 minutes; after cooling, the activated carbon Take it out, add clean water and wash repeatedly, make the pH value 7 and dry it in a drying box at 100°C to make the activated carbon have a moisture content of 3%. After crushing and sieving, the finished product of the camellia husk activated carbon is obtained.
[0015] According to the national standard GB/T 12496.10-1999 and GB/T 12496.8-1999, the iodine adsorption value of camellia shell activated carbon can reach 1683mg/g and the methylene blue adsorption value can reach 187mg/g, which fully meets the national standard of first-class activated carbon Adsorption performance index. The specific surface area of ​​the prepared activated carbon from camellia shell was 962m by using an automatic specific surface analyzer. 2 /g, the scanning electron microscope observation results show that the activated carbon from camellia shell has developed pore structure and rich mesopores.

Example Embodiment

[0016] Example 2.
[0017] Select the oil-tea camellia husk and place it in a constant temperature electric heating drying box to reduce the dry moisture content to 5%. The pre-treated husk is further crushed to 80 mesh, and the oil-tea husk powder and 60% phosphoric acid solution are in a weight ratio of 1:3.5. Stir and mix well After standing for 48 hours, the acid-leached camellia husks were heated and carbonized in a drying oven at 150°C for 120 minutes; the carbonized camellia husks were placed in a resistance furnace and the temperature was increased to 650°C for activation for 120 minutes; after cooling, the activated carbon Take it out, add clean water and repeatedly wash, make the pH value 5 and dry in a 120°C drying box to make the activated carbon have a moisture content of 5%. After crushing and sieving, the finished product of camellia husk activated carbon is obtained.
[0018] According to national standards GB/T 12496.10-1999 and GB/T 12496.8-1999, the iodine adsorption value of camellia shell activated carbon can reach 1534mg/g and the methylene blue adsorption value can reach 177mg/g, which fully meets the national standard of first-class activated carbon. Adsorption performance index. The specific surface area of ​​the prepared activated carbon from camellia shell was 949m measured by the automatic specific surface analyzer. 2 /g, the scanning electron microscope observation results show that the activated carbon from camellia shell has developed pore structure and rich mesopores.

PUM

PropertyMeasurementUnit
Iodine adsorption value1683.0mg/g
Adsorption value of methylene blue187.0mg/g
Specific surface area962.0m²/g

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.

Similar technology patents

Chinese patent medicine for treating herpes zostor

InactiveCN103463278ANo side effectsSufficient raw materials
Owner:徐茂恺

Music instrument made up of marine biota shells

InactiveCN1397928ASufficient raw materialsThe production process is simple
Owner:于泉林

Mixing method of fructus phyllanthi coarse cereal powder in tea therapy

PendingCN113907249ASufficient raw materialsRaw materials are easy to get
Owner:普红天下(广东)茶业科技有限公司

Laser roughening method for diamond

InactiveCN109570746Alow costSufficient raw materials
Owner:ZHENGZHOU INSOLL TOOLS TECH CO LTD

Traditional Chinese medicine composition for treating trigeminal neuralgia and preparation method thereof

InactiveCN108379429Asimple recipeSufficient raw materials
Owner:重庆跃龙生物制药有限公司

Classification and recommendation of technical efficacy words

  • Sufficient raw materials
  • low price

Anode material for lithium-ion battery and preparation method of anode material

InactiveCN104577081Alow priceSufficient raw materials
Owner:SOUTH CHINA UNIV OF TECH

Production method of camellia oleifera meal protein adhesive

InactiveCN102295902Alow costSufficient raw materials
Owner:ZHEJIANG FORESTRY UNIVERSITY

Process for making hot-melt pressure sensitive adhesive type fabric base adhesive tape

ActiveCN1844285ASufficient raw materialsfair price
Owner:SHANGHAI YONGGUAN ADHESIVE PROD CORP LTD

Dephosphorizing agent for hematite separation and preparation method thereof

InactiveCN101078048ASufficient raw materialsreduce manufacturing cost
Owner:HUBEI YICHANG LINSEN INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products