Flame-retardant glass fiber-reinforced ABS material with high CTI value and high GWIT value

A technology of ABS material and glass fiber, which is applied in the field of high CTI value and high GWIT value flame-retardant glass fiber reinforced ABS material, which can solve the problems of low CTI value and GWIT value, unsuitable electricity environment, etc., to improve anti-oxidation performance, lower friction coefficient, and improve processing fluidity

Inactive Publication Date: 2013-04-03
SHANGHAI SUNNY
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some traditional methods are (GF+decabromodiphenylethane+antimony trioxide) compound system, (GF+brominated polystyrene+antimony trioxide) compound system, but the CTI value and GWIT of these compound systems The value is not high, not suitable for high-demand electricity environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant glass fiber-reinforced ABS material with high CTI value and high GWIT value
  • Flame-retardant glass fiber-reinforced ABS material with high CTI value and high GWIT value
  • Flame-retardant glass fiber-reinforced ABS material with high CTI value and high GWIT value

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0026] The flame retardant glass fiber reinforced ABS materials with high CTI value and high GWIT value of Examples 1 to 6, each component contained is shown in Table 1, wherein, ABS is commercially available acrylonitrile-butadiene-styrene, glass fiber It is the non-alkali glass fiber (specifically: the non-alkali glass fiber is added in the silane coupling agent to make its surface through the silane coupling agent treatment) through the surface treatment of silane coupling agent. The toughening agent is commercially available horse 180 powder, Composite flame retardant A is a mixture of three components, and its mass percentage is BPS (brominated polystyrene): 50%, magnesium hypophosphite: 25%, talcum powder: 25%, and compound flame retardant B It is a compound system of BPS, GF (non-reactive nitrogen and phosphorus flame retardant) and antimony trioxide with a mass ratio of 2:1:1, and the compound flame retardant C is a mass ratio of 2:1 :1 compound system of decabromodiph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retardant glass fiber-reinforced ABS material with a high CTI value and a high GWIT value. The ABS material comprises the following components: by weight, 45 to 68% of ABS, 6 to 20% of a compound fire retardant, 3 to 15% of antimonony oxide, 20 to 30% of a glass fiber, 2 to 10% of a compatilizer, 0.1 to 1% of an anti-oxidant and 0.1 to 1% of a metallic oxide. In preparation of the ABS material, all the components are added into a high-speed mixer for mixing for 2 to 5 min, and then discharging and extrusion granulation in a twin-screw extruder are carried out, wherein processing temperature of the twin-screw extruder is 200 to 230 DEG C and screw revolution is 30 to 40 Hz. Compared with the prior art, the ABS material prepared in the invention has the advantages of high glow wire temperature, a high tracking index, environment-friendliness, balanced comprehensive properties and the like through utilization of a novel flame-retardant compounded system in the invention.

Description

technical field [0001] The invention relates to an ABS material, in particular to a flame-retardant glass fiber-reinforced ABS material with high CTI value and high GWIT value. Background technique [0002] ABS resin features: The resin has good comprehensive performance. High impact strength, chemical stability, good electrical properties; good fusion with plexiglass, made of two-color plastic parts, and the surface can be chrome-plated and spray-painted; it has high impact resistance, high heat resistance, flame retardancy, reinforcement, and transparency The same level; fluidity is a little worse than HIPS, better than PMMA, PC, etc., and good flexibility. In the 21st century, electronic and electrical communication appliances, home appliances, and electrical equipment are developing towards high-performance miniaturization, and the requirements for flame-retardant ABS materials are getting higher and higher. , along with the mankind's understanding to environmental prot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L25/04C08K13/06C08K3/22C08K7/14C08K3/32C08K3/34
Inventor 郭建鹏苏吉英
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More