Halogen-free filling flame-retardant nylon 6 composite material and preparation method thereof

A technology of flame-retardant nylon and composite materials, applied in the field of polymer flame-retardant materials preparation, can solve the problems of unpublished GWFI test and mechanical properties, non-environmentally friendly flame-retardant of flame-retardant filled nylon, unstable GWFI test, etc., and achieve excellent results Dimensional stability, enhanced flame retardancy, and good application prospects

Active Publication Date: 2013-04-03
SHANGHAI KINGFA SCI & TECH +1
View PDF8 Cites 56 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent 200710011841.2 provides a kind of mixing nylon 6, melamine cyanurate, antioxidant, triphenyl phosphate or zinc borate, and adopts reactive extrusion method to prepare melamine cyanurate / nylon 6 flame retardant material, flame retardant The performance can reach UL94V-0, but the data such as GWFI test and mechanical properties have not been disclosed
[0006] Existing flame-retardant filled nylon has problems such as non-environmentally friendly flame-retardant, low flame-retardant grade, and unstable GWFI test.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free filling flame-retardant nylon 6 composite material and preparation method thereof
  • Halogen-free filling flame-retardant nylon 6 composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-11

[0032] Among the raw materials used in Examples 1-11, nylon 6 is PA6M2400 (produced by Xinhui Meida); melamine cyanurate is a commercially available powder (produced by Sichuan Fine Chemical); Limestone is acicular silica lime with an aspect ratio of 15-20:1; the average diameter of spherical glass microspheres is about 15 μm; the size ratio of the main cross-sectional axis to the secondary cross-sectional axis of flat glass fibers is 2, and the length is 2 - 3 mm chopped fibers. The montmorillonite is sodium montmorillonite DK5 produced by Zhejiang Fenghong Clay Chemical; the zinc borate is ZB-2335 produced by Zibo Xubei Chemical; the phenoxy polyphosphazene is KP-735NA produced by Zibo Lanyin Chemical; Phenyl ester is produced by Changzhou Ke'an Chemical; the stabilizer is polycarbodiimide, which adopts STABAXOL-1 produced by German Rheinland Chemical; the antioxidant is N, N'-bis-(3-(3,5-di-tert-butyl Base-4-hydroxyphenyl) propionyl) hexamethylenediamine (Irganox 1098 of C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a halogen-free filling flame-retardant nylon 6 composite material and a preparation method thereof. The halogen-free filling flame-retardant nylon 6 composite material provided by the invention is characterized by being prepared from the following raw materials: 53-70 parts by weight of nylon 6 resin, 7-15 parts by weight of melamine cyanurate, 20-30 parts by weight of inorganic filling material, 0-5 parts by weight of synergistic flame retardant, and 1-5 parts by weight of processing agent. Compared with the prior art, the halogen-free filling flame-retardant nylon 6 composite material provided by the invention has the beneficial effects the halogen-free filling flame-retardant nylon 6 composite material is capable of passing the GWFI (Glow Wire Flammability Index) test at 960 DEG C, also has the characteristics of being low in cost, high in modulus and strength, excellent size stability, environment-friendly, flame-retardant and the like, and has good application prospect.

Description

technical field [0001] The invention relates to the field of preparation methods of polymer flame-retardant materials, in particular to a halogen-free filled flame-retardant nylon 6 material and a preparation method thereof. Background technique [0002] With the development of the electronic and electrical industry, the demand for flame-retardant nylon materials keeps growing rapidly. Although halogen-containing flame retardants have good flame retardant effects, they generate a large amount of smoke when burned, and produce toxic gases to cause secondary pollution. Melamine cyanurate, referred to as MCA, is a nitrogen-containing compound formed by the polymerization of melamine and cyanuric acid. As a nitrogen-based flame retardant, compared with halogen-based flame retardants, it has lower toxicity and has excellent comprehensive flame-retardant properties. Nylon 6 is an important engineering plastic with good toughness, excellent electrical properties, oil resistance, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08K13/02C08K13/04C08K5/3492C08K3/34C08K7/20C08K7/14C08K3/38C08K5/5399C08K5/523B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/875B29C48/92B29C2948/92704B29C2948/92895
Inventor 张现军田晋丽张永卢立波
Owner SHANGHAI KINGFA SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap