A water-based polyurethane and ultra-fine fiber technology, which is applied in the field of polyurethane synthetic leather to achieve the effect of purifying the decorative space

Inactive Publication Date: 2013-04-03
福建可利得皮革纤维有限公司
View PDF5 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To match with the paint, that is to paint the surface of the wallpaper with a high-grade satin finish paint, the color can be matched with the co

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0060] Example 1:

[0061] 1) In parts by mass, 40 parts of water-soluble polyurethane with a solid content of 55%, 2 parts of wood powder loaded with nano-silver peroxide, 1 part of wood powder loaded with nano-titanium dioxide, and 5 parts of diatoms with a fineness of more than 400 mesh Soil, 3 parts of bayberry extract, 2 parts of foaming agent sodium dodecylbenzene sulfonate and 1 part of industrialized water-based resin colorant are added to a batch or continuous foam coating foaming machine under stirring Carry out 5~45 minutes to make fine foam slurry;

[0062] Wherein, loaded nanometer silver peroxide wood powder, is to be carrier with lignocellulose powder, after the nano silver peroxide after adsorption dispersion, the powder that obtains after drying and pulverizing, the amount of adsorption nano silver peroxide is 10% of wood powder weight %;

[0063] The loaded nano-titanium dioxide wood powder is a powder obtained by using lignocellulose powder as a carrier, a...

Example Embodiment

[0066] Example 2:

[0067] 1) In parts by mass, 50 parts of water-emulsion polyurethane with a solid content of 70%, 1 part of wood powder loaded with nano-silver peroxide, 3 parts of wood powder loaded with nano-titanium dioxide, and 8 parts of silicon dioxide with a fineness of more than 400 mesh Alginate earth, 5 parts of larch extract, 4 parts of foaming agent sodium lauryl sulfate and 3 parts of industrialized water-based resin colorant are added to a batch or continuous foam coating foaming machine under stirring Carry out 5~45 minutes to make fine foam slurry;

[0068] Wherein, the loaded nanometer silver peroxide wood powder is to use lignocellulose powder as a carrier, after absorbing and dispersing the nano silver peroxide, the powder obtained after drying and pulverizing, the amount of adsorbing nano silver peroxide is 8% of the wood powder weight %;

[0069] The loaded nano-titanium dioxide wood powder is a powder obtained after absorbing and dispersing nano-tita...

Example Embodiment

[0072] Example 3:

[0073] 1) In parts by mass, 70 parts of water-dispersed polyurethane with a solid content of 60%, 3 parts of wood powder loaded with nano silver peroxide, 0.3 parts of wood powder loaded with nano titanium dioxide, and 3 parts of silicon dioxide with a fineness of more than 400 mesh Alginate earth, 1 part of Vitex bark extract, 7 parts of foaming agent sodium stearate and 5 parts of industrialized water-based resin colorant are added to a batch or continuous foam coating foaming machine under stirring 5-45 minutes to make fine foam slurry;

[0074] Wherein, loaded nano-silver peroxide wood powder is to take lignocellulose powder as carrier, after absorbing and dispersing nano-silver peroxide, the powder obtained after drying and pulverizing, the amount of adsorbing nano-silver peroxide is 12% of wood powder weight %;

[0075] The loaded nano-titanium dioxide wood powder is a powder obtained by using lignocellulose powder as a carrier, absorbing and disper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for producing multifunctional waterborne polyurethane superfine fiber decorative leather. According to the method, superfine fiber non-woven cloth is used as a base material, and the method comprises the following steps of: firstly, preparing mixed slurry containing the components of waterborne polyurethane, wood powder loaded with nano silver oxide and the like into superfine foam slurry by adopting a physical and mechanical stirring method; secondly, forming a functional coating on release paper by adopting a knife coating method, closely integrating the release paper with the base material, and drying, cooling and stripping to obtain superfine fiber non-woven cloth provided with the functional coating; and finally, performing various beautification processes on the superfine fiber non-woven cloth to obtain the multifunctional waterborne polyurethane superfine fiber decorative leather which has a variety of functions of decorating, purifying air, removing formaldehyde, deodorizing, sterilizing, adjusting moisture and the like and has a through microcellular structure. The multifunctional waterborne polyurethane superfine fiber decorative leather can be widely used in a variety of fields such as house wall decoration, hotel decoration, furniture soft package, automobile interior trim, jewelry package and the like.

Description

technical field [0001] The invention relates to the technical field of polyurethane synthetic leather, in particular to a production method of multifunctional water-based polyurethane superfine fiber decorative leather. Background technique [0002] 1. Technical progress of wallpaper [0003] The birthplace of wallpaper is Europe, and now it is the most popular in developed countries in northern Europe, with the best environmental protection and quality, followed by Southeast Asian countries, and the penetration rate of wallpaper in Japan and South Korea is as high as nearly 90%. No matter in terms of production technology, process, or use, compared with other building materials, it can be said that wallpaper is the least toxic. The main raw materials of modern new wallpaper are made of bark and chemically synthesized pulp, which is very natural. It will not emit ingredients harmful to human health. [0004] According to market research, most of the environmentally friendl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/12B32B37/02B32B37/15B32B37/26B32B38/16B32B27/06B32B9/00
Inventor 施凌山马兴元牛建民张晓镭
Owner 福建可利得皮革纤维有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap