Ultra-durable self-cleaning reflective insulation simulation coating technical field

A self-cleaning, ultra-durable technology, applied in reflective/signal paints, coatings, etc., can solve the problems of heat reflection and heat insulation performance changes, unstable chemical properties, difficult to store for a long time, etc., to reduce air-conditioning costs and achieve excellent whiteness. , the effect of appearance improvement

Active Publication Date: 2013-04-24
江阴市天邦涂料股份有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional reflective insulation materials have certain toxicity, and are not stable in chemical properties, not

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] An ultra-durable self-cleaning reflective thermal insulation anti-counterfeiting paint, which contains the following components by weight percentage:

[0048] Water 11.5%

[0049] Propylene glycol 4%

[0050] Acrylic thickener CR 1%

[0051] Wetting agent TRITON X-100 1.5%

[0052] Dispersant TRITON CF-10 1.5%

[0053] Defoamer SN-154 1%

[0054] Multifunctional additives AMP95 0.5%

[0055] Fungicide ACTICIDE HF 1%

[0056] Film forming aid TEXANOL 2%

[0057] Dry film antifungal agent ACTICDE EPW 1%

[0058] Self-cleaning additive BYK-9131 0

[0059] Modified fluorocarbon emulsion 30%

[0060] Covering hollow microemulsion 15%

[0061] High-strength hollow glass beads 25%

[0062] Hollow ceramic powder 5%

[0063] The paint is used as a middle coat and has good heat insulation performance.

Embodiment 2

[0065] An ultra-durable self-cleaning reflective thermal insulation anti-counterfeiting paint, which contains the following components by weight percentage:

[0066] Water 10%

[0067] Propylene glycol 5%

[0068] Acrylic thickener CR 1%

[0069] Wetting agent TRITON X-100 1.5%

[0070] Dispersant TRITON CF-10 1%

[0071] Defoamer SN-154 1%

[0072] Multifunctional additives AMP95 0.5%

[0073] Fungicide ACTICIDE HF 1%

[0074] Rutile Titanium Dioxide R902+ 5%

[0075] Environmentally friendly color mixed phase inorganic pigment 5%

[0076] Film-forming aid TEXANOL Dodecyl alcohol 2%

[0077] Dry film antifungal agent ACTICDE EPW 1%

[0078] Self-cleaning additive BYK-9131 1%

[0079] Modified fluorocarbon emulsion 35%

[0080] Covering hollow microemulsion 10%

[0081] High-strength hollow glass beads 5%

[0082] Hollow ceramic powder 15%

[0083] The paint is used as a top coat, anti-counterfeiting, good reflection and heat insulation performance, good appearance, long-lasting self-cleaning.

Embodiment 3

[0085] An ultra-durable self-cleaning reflective thermal insulation anti-counterfeiting paint, which contains the following components by weight percentage:

[0086] Water 28%

[0087] Propylene glycol 5%

[0088] Acrylic thickener CR 5%

[0089] Wetting agent TRITON X-100 0.5%

[0090] Dispersant TRITON CF-10 0.5%

[0091] Defoamer SN-154 0.4%

[0092] Multifunctional additives AMP95 0.5%

[0093] Fungicide ACTICIDE HF 0.6%

[0094] Rutile Titanium Dioxide R902+ 9.5%

[0095] Environmentally friendly color mixed phase inorganic pigment 5%

[0096] Film-forming aid TEXANOL dodecyl alcohol 1%

[0097] Dry film antifungal agent ACTICDE EPW 1%

[0098] Self-cleaning additive BYK-9131 1%

[0099] Modified fluorocarbon emulsion 30%

[0100] Covering hollow microemulsion 5%

[0101] High-strength hollow glass beads 5%

[0102] Hollow ceramic powder 2%

[0103] The paint is used as a top coat, with good sealing performance, good appearance and long-lasting self-cleaning.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses an ultra-durable self-cleaning reflective insulation simulation coating. The ultra-durable self-cleaning reflective insulation simulation coating includes the following components: water, an antifreeze, a thickener, a wetting agent, a dispersing agent, an antifoaming agent, a multifunctional additive, a pH adjusting agent, a bactericide, rutile titanium dioxide, an environmentally-friendly colored mixed-phase inorganic pigment, a coalescing agent, a dry film fungicide, a self-cleaning additive, a modified fluorocarbon emulsion, a covering hollow micro-emulsion, high-strength hollow glass beads, and hollow ceramic micro powder. The environmentally-friendly colored mixed-phase inorganic pigment adopted in the coating has excellent durability, excellent infrared-reflection function, and excellent insulation and cooling, and environmental protection and energy saving effect; additionally, the pigment also has a function of simulating chlorophyll, so the coating can be used for simulation in national defense and military fields; and the coating of the present invention has excellent resistance to staining, yellowing, alkali, acid rain, and salt spray, and ultra-long weather resistance, ultra-long durability and self-cleaning function.

Description

[0001] The invention relates to the field of chemical coatings, in particular to an ultra-durable self-cleaning reflective heat-insulating anti-counterfeiting coating. Background technique [0002] As the temperature of the outer surface of the building exposed to the sun for a long time continues to rise, the outer surface of the building is cement, concrete, ceramic tile, metal, insulation brick and other building materials. The temperature of the outer surface of the building material can reach 40-50 ℃. The temperature can reach 60°C, reaching a scalding temperature. Under the high temperature of the outer surface of such a building, the temperature in the living room, workshop, etc. will inevitably rise, which will have a great impact on the safety of normal human living, material storage, and equipment, and may cause great safety hazards such as explosions. Hidden danger, if the temperature is too high, it needs to be cooled down, and at the same time it causes a great wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D127/12C09D5/33C09D7/12
Inventor 吴立新王国华梁勇吕君倪伟孔平刘欢刘魁魁
Owner 江阴市天邦涂料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap