Modified polypropylene resin composition and solar energy rear panel made of the same
A solar backsheet and polypropylene resin technology, applied in photovoltaic power generation, electrical components, circuits, etc., can solve the problems of brittleness, poor cold resistance, and inability to meet low-temperature impact resistance, etc., and achieve low cost and simple and easy preparation method Good, excellent interlayer peeling effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0061] A modified polypropylene resin composition, its preparation method is as follows:
[0062] (1) Preparation of grafted polyethylene PE-MA
[0063] 100 parts (parts by mass) of LLDPE7042 (Beijing Yanshan Petrochemical Company), 1 part of maleic anhydride (chemical reagent, analytical grade), and 0.05 parts of DCP initiator (Tianjin Aksu Company) were measured and added to the mixer for mixing and homogenization. After homogenizing for two hours, put it into a twin-screw extruder for melt extrusion and granulation; cool and granulate to obtain granular grafted polyethylene PE-MA, and its melt flow rate at 190°C / 2.16kg is 0.5g / 10min. The diameter of the screw is 75mm, the aspect ratio is 33, the temperature of the screw is controlled at 160-220°C, the rotational speed of the screw is controlled at 100 rpm, and the residence time of the material in the screw is 2-4 minutes.
[0064] The LLDPE7042 (Beijing Yanshan Petrochemical Company) is a linear low-density polyethylene w...
Embodiment 2
[0068] A modified polypropylene resin composition, its preparation method is as follows:
[0069] (1) Preparation of grafted polyethylene PE-MA: see Example 1
[0070] (2) Preparation of modified polypropylene resin composition: 75 parts of block copolymerized polypropylene K8303, 25 parts of grafted polyethylene PE-MA, 50 parts of rutile titanium dioxide R960, 0.25 parts of antioxidant tetra[?- (3',5'-di-tert-butyl-4'-hydroxyphenyl) propionate] pentaerythritol ester, 0.2 part of UV absorber 2-hydroxy-4-n-octyloxybenzophenone, 0.1 part of light stabilizer The agent bis(2,2,6,6-tetramethyl-4-piperidinyl) sebacate is mixed evenly according to the metering ratio, and then put into the twin-screw extruder for melt extrusion (the twin-screw adopts the exhaust screw, The diameter of the screw is 75 mm, the ratio of length to diameter is 33, the temperature of the screw is controlled at 180-240 ° C, the speed of the screw is controlled at 100 rpm, and the residence time of the mater...
Embodiment 3
[0072] A modified polypropylene resin composition, its preparation method is as follows:
[0073] (1) Preparation of grafted polyethylene PE-MA: see Example 1
[0074] (2) Preparation of modified polypropylene resin composition: 96 parts of polypropylene 1300 and 4 parts of grafted polyethylene PE-MA, 40 parts of rutile titanium dioxide R960, 0.2 parts of antioxidant tetrakis[?-(3' , 5'-di-tert-butyl-4'-hydroxyphenyl) propionate] pentaerythritol ester, 0.25 parts of UV absorber 2-hydroxy-4-n-octyloxybenzophenone, 0.15 parts of light stabilizer bis( 2,2,6,6-tetramethyl-4-piperidinyl) sebacate is mixed evenly and put into a twin-screw extruder for melt extrusion (the twin-screw adopts an exhaust screw, and the diameter of the screw is 75 mm. The aspect ratio is 33, the screw temperature is controlled at 180-240°C, the screw speed is controlled at 100 rpm, and the residence time of the material in the screw is 2-4 minutes); the material is cooled, granulated and dried to become ...
PUM
Property | Measurement | Unit |
---|---|---|
melting point | aaaaa | aaaaa |
melt flow index | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com