Colouring solution used for stainless steel electrochemical colouring and stainless steel electrochemical colouring method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An electrochemical and coloring liquid technology, applied in the field of stainless steel surface treatment reagents, can solve the problems of difficult to control the content of sodium metavanadate, the color of the coloring layer has a great influence, and the treatment of coloring waste liquid is difficult, so as to improve the anti-discoloration ability and the anti-discoloration ability. Corrosion ability, improve the stability of the color film, the effect of color stability
Active Publication Date: 2013-05-22
湖南中皖骏环保科技有限公司
View PDF3 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0013] The coloring temperature of this coloring liquid is 80-140 °C, the temperature is relatively high, it needs to be heated, and the temperature has a great influence on the color of the coloring layer. Oxidation corrosion, resulting in rough surface and poor gloss
In addition, a large amount of sulfuric acid is required in the coloring liquid, and the coloring cost is relatively high. The presence of sulfuric acid also makes it difficult to dispose of the coloring waste liquid.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] The coloring solution for electrochemical coloring of stainless steel is a solution, and the solvent is water. The solution mainly includes:
[0026]
[0027]
[0028] According to the coloring method, the stainless steel product is colored, the coloring voltage is 1.7V, the coloring current is 4A / dm2, and the coloring time is 5 minutes.
Embodiment 2
[0030] The coloring solution for electrochemical coloring of stainless steel is a solution, and the solvent is water. The solution mainly includes:
[0031]
[0032] According to the coloring method, the stainless steel product is colored, the coloring voltage is 1.9V, the coloring current is 20A / dm2, and the coloring time is 2 minutes.
Embodiment 3
[0034] The coloring solution for electrochemical coloring of stainless steel is a solution, and the solvent is water. The solution mainly includes:
[0035]
[0036] According to the coloring method, the stainless steel product is colored, the coloring voltage is 2.0V, the coloring current is 16A / dm2 and the coloring time is 4 minutes.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a stainless steel surface treatment reagent, in particular to a stainless steel surface colouring method. According to the invention, with water as a solvent, each litre of solution contains 30-80g of molybdate, 10-18g of boric acid, 2-5g of zinc sulphate, 0.5-5g of manganese sulphate, 2-15g of antimony nitrite, 0.2-2g of lanthanum nitrite and 0.1-10g of sodium malonate. The stainless steel surface colouring method comprises the following basic flow: oil removing, electrolytic polishing, cleaning, colouring, cleaning and drying and obtaining the finished product, wherein an anode is a workpiece to be coloured, a cathode is a lead plate, a colouring current is controlled to be 0.1-5A / dm<2>, voltage is 1.5-2.5V, a colouring temperature is room temperature, colouring time is 0.1-30 minutes, cleaning and drying are carried out after colouring, and the surface of the obtained sample is uniform and bright. The stainless steel electrochemical colouring process provided by the invention needs simple equipment, is easy to operate, contains no toxic substance and is beneficial to environmental protection; and colouring is stable, and a high-quality colour stainless steel product can be produced by adopting the stainless steel electrochemical colouring process.
Description
technical field [0001] The invention relates to a stainless steel surface treatment reagent, in particular to a coloring method for the stainless steel surface. Background technique [0002] Stainless steel has excellent corrosion resistance and wear resistance. With the improvement of people's living standards, stainless steel products continue to develop into decorative aspects, so the color requirements for stainless steel surfaces are also increasing. [0003] Coloring stainless steel is to form color on the surface of stainless steel, thus becoming colored stainless steel. The industrial production of colored stainless steel originated from the British INC0 company in 1973. The INCO method is to immerse the stainless steel workpiece in a mixed solution containing high concentrations of chromic acid and sulfuric acid at 80 ° C. By controlling the length of immersion, translucent surfaces of different thicknesses are formed on the surface chromium oxide film. Due to th...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more