Medium-heat anti-cracking portland cement

A technology of portland cement and cement, which is applied in the field of cement, can solve problems such as concrete cracking, and achieve the effects of increasing cement toughness, flexural strength, and volume stability

Inactive Publication Date: 2013-06-12
CHINA THREE GORGES CORPORATION
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the cracking problem of concrete in the prior art, the present invention provides a medium-heat crack-resistant Portland cement for hydraulic concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A medium-heat crack-resistant Portland cement, the mineral composition of the cement clinker is: tricalcium silicate: 51.8%, dicalcium silicate: 23.6%, tricalcium aluminate: 2.9%, tetracalcium aluminoferrite : 21.1%, free calcium oxide: 0.6%; the content of magnesium oxide in the cement is 4.0%, the alkali content is 0.5%, and the sulfur trioxide is adjusted to 3.0%, and the above percentages are percentages by weight.

[0019] The technical indicators of the medium-heat crack-resistant Portland cement are: loss on ignition: 2wt%, specific surface area: 310m 2 / kg, initial setting time: 85min, final setting time: 10h, stability: qualified, 7-day compressive strength: 24MPa, 28-day compressive strength: 49MPa, 7-day flexural strength: 5MPa, 28-day Flexural strength: 8MPa, 3-day heat of hydration: 233KJ / kg, 7-day compressive strength: 267KJ / kg.

[0020] When the medium-heat crack-resistant Portland cement is transported to the construction site in bulk, the tank entry te...

Embodiment 2

[0022] A medium-heat crack-resistant Portland cement, the mineral composition of the cement clinker is: tricalcium silicate: 35%, dicalcium silicate: 15%, tricalcium aluminate: 1%, tetracalcium aluminoferrite : 15%, free calcium oxide: 0.1%; the content of magnesium oxide in cement is 3.5%, the content of alkali is 0, and the content of sulfur trioxide is 1%. The above percentages are percentages by weight.

[0023] The technical indicators of the medium-heat crack-resistant Portland cement are: loss on ignition: 1wt%, specific surface area: 100m 2 / kg, initial setting time: 60min, final setting time: 8h, stability: qualified, no requirement for 3-day compressive strength, 7-day compressive strength: 22MPa, 28-day compressive strength: 42.5MPa, 3 days No requirements for the flexural strength, 7-day flexural strength: 4.0MPa, 28-day flexural strength: 7.5MPa, 3-day heat of hydration 241KJ / kg, 7-day compressive strength 283KJ / kg.

[0024] When the medium-heat crack-resistant P...

Embodiment 3

[0026] A medium-heat crack-resistant Portland cement, the mineral composition of the cement clinker is: tricalcium silicate: 55%, dicalcium silicate: 35%, tricalcium aluminate: 4%, tetracalcium aluminoferrite : 30%, free calcium oxide: 0.8%; magnesium oxide in cement: 5.0%, alkali content: 0.55, sulfur trioxide content: 3.5%, the above percentages are percentages by weight.

[0027] The technical indicators of the medium-heat crack-resistant Portland cement are: loss on ignition: 3wt%, specific surface area: 320m 2 / kg, initial setting time 100min, final setting time: 12h, stability: qualified, no requirement for 3-day compressive strength, 7-day compressive strength: 30MPa, 28-day compressive strength: 52.5MPa, 3-day compressive strength No requirement for flexural strength, 7-day flexural strength: ≥4.0MPa, 28-day flexural strength: 9MPa, 3-day heat of hydration 220KJ / kg, 7-day compressive strength ≤245KJ / kg.

[0028] When the medium-heat crack-resistant Portland cement is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
curing timeaaaaaaaaaa
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses low-heat anti-cracking Portland cement. The cement clinker of the cement consists of the following minerals in percentage by weight: 35 to 55 percent of tricalcium silicate, 15 to 35 percent of dicalcium silicate, 1 to 4 percent of tricalcium aluminate, 15 to 30 percent of tetra calcium aluminoferrite, and 0.1 to 0.8 percent of free calcium oxide, wherein the content of magnesium oxide in the cement is between 3.5 percent and 5.0 percent, the content of alkali is not more than 0.55 percent, and the content of sulfur trioxide is not more than 3.5 percent. The cement has the main technical indexes that the ignition loss is less than or equal to 3wt%, the specific area is less than or equal to 320m<2> / kg, the stability is qualified, 3-day tensile strength is not required, the 7-day tensile strength is more than or equal to 22MPa, the 28-day tensile strength is between 42.5MPa and 52.5MPa, the 3-day breaking strength is not required, the 7-day breaking strength is more than or equal to 3.5MPa, the 28-day breaking strength is more than or equal to 7.5MPa, the 3-day hydration heat is less than or equal to 241KJ / kg, and the 7-day tensile strength is less than or equal to 283KJ / kg. The cement can be used for remarkably improving the cracking resistance of hydraulic concrete.

Description

technical field [0001] The invention relates to a cement, in particular to a medium-heat crack-resistant Portland cement used for hydraulic concrete. Background technique [0002] In recent years, the speed of dam construction in my country has been accelerating, but the problem of concrete cracking has not been well resolved. As far as materials are concerned, cement is one of the most critical factors affecting concrete cracking. [0003] Hydraulic concrete (except concrete for flood discharge and energy dissipation buildings) has the characteristics of large volume, long design age, and generally low strength. It has high requirements for concrete crack resistance and durability. Therefore, cement is required to have low and slow heat of hydration. 1. It has a certain function of compensating for shrinkage. In special cases, it should also have the effect of preventing alkali aggregate reaction and sulfate erosion. Contents of the invention [0004] In order to solve t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B22/08
Inventor 李文伟
Owner CHINA THREE GORGES CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com