Copper plastic composite strap suitable for telecommunication cable and optical cable and preparation method of copper plastic composite strap

A copper-plastic composite tape and communication cable technology, which is applied in communication cables, cable/conductor manufacturing, insulated cables, etc., can solve the problems that polyethylene and ethylene copolymers cannot fully meet the actual needs, and achieve the improvement of cooling liquid cooling process, Improve workability and flattening of belts

Inactive Publication Date: 2015-05-20
JIUXING HLDG GRP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, polyethylene and ethylene copolymers cannot fully meet the actual needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Copper plastic composite strap suitable for telecommunication cable and optical cable and preparation method of copper plastic composite strap
  • Copper plastic composite strap suitable for telecommunication cable and optical cable and preparation method of copper plastic composite strap
  • Copper plastic composite strap suitable for telecommunication cable and optical cable and preparation method of copper plastic composite strap

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0078] Production process of ultra-thin copper layer:

[0079] Pre-finished product rolling: select T2 copper strip with a thickness of 0.12mm, and roll it to a pre-finished product with a thickness of 0.08mm at a rolling speed of 0.8m / s.

[0080] Softening: The pre-finished product is softened by continuous online annealing, the softening temperature is 680°C, and the softening speed is 15m / min.

[0081] Finished product rolling: The pre-finished product is rolled to a finished product with a thickness of 0.03mm by a small four-high rolling mill with a diameter of 60mm working roll and a diameter of 300mm supporting roll. The work roll adopts hollow water-cooled roll, and the work roll directly cools the copper strip and adds an air cooling system at the discharge end for enhanced cooling, and at the same time blows the copper strip to keep the surface of the copper strip free of impurities and clean.

[0082] Softening: The finished copper strip after rolling is softened by...

Embodiment 2

[0109] Production process of ultra-thin copper layer:

[0110] Pre-finished product rolling: select T2 copper strip with a thickness of 0.12mm, and roll it to a pre-finished product with a thickness of 0.06mm at a rolling speed of 1.0m / s.

[0111] Softening: The pre-finished product is softened by continuous online annealing, the softening temperature is 750°C, and the softening speed is 20m / min.

[0112] Finished product rolling: the pre-finished product is rolled to a finished product with a thickness of 0.03mm by a small four-high rolling mill with a diameter of 90mm working roll and a diameter of 300mm supporting roll. The work roll adopts hollow water-cooled roll, and the work roll directly cools the copper strip and adds an air cooling system at the discharge end for enhanced cooling, and at the same time blows the copper strip to keep the surface of the copper strip free of impurities and clean.

[0113] 4) Softening: the finished copper strip after rolling is softened...

Embodiment 3

[0137] Production process of ultra-thin copper layer:

[0138] Pre-finished product rolling: select T2 copper strip with a thickness of 0.10mm, and roll it to a pre-finished product with a thickness of 0.06mm at a rolling speed of 1.5m / s.

[0139] Softening: The pre-finished product is softened by continuous online annealing, the softening temperature is 800°C, and the softening speed is 25m / min.

[0140] Finished product rolling: the pre-finished product is rolled to a finished product with a thickness of 0.02mm by a small four-high rolling mill with a diameter of 90mm working roll and a diameter of 280mm supporting roll. The work roll adopts hollow water-cooled roll, and the work roll directly cools the copper strip and adds an air cooling system at the discharge end for enhanced cooling, and at the same time blows the copper strip to keep the surface of the copper strip free of impurities and clean.

[0141] Softening: The finished copper strip after rolling enters the con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of cable straps, in particular to a copper plastic composite strap suitable for a telecommunication cable and an optical cable and a copper plastic composite strap preparation method. The copper plastic composite strap is wrapped on the outer surface of the telecommunication cable or the optical cable. The copper plastic composite strap is provided with a red copper layer (1), an adhesive layer (2) and a polyester film layer (3) in sequence. The red copper layer (1), the adhesive layer (2) and the polyester film layer (3) are attached together through bonding and heating to form a composite structure. The tensile strength of the copper plastic composite strap is larger than or equal to 180 MPa. The breakage elongation of the copper plastic composite strap is larger than or equal to 15%. The interlaminar peeling strength between a copper strap and a plastic layer is larger than or equal to 15N / centimeter. The conductivity of the copper plastic composite strap is larger than or equal to 90% of international annealed copper standard (IACS). The breakdown phenomenon does not happen to the single-sided copper plastic composite strap 1kvd.c in one minute.

Description

technical field [0001] The invention relates to the field of cable tapes, in particular to a copper-plastic composite tape suitable for communication cables and optical cables and its preparation. Background technique [0002] Copper-plastic composite tape is a substitute for pure copper tape for cables. It is one of the important varieties of modern copper processing materials, and its application in the communication cable and communication optical cable industries is continuously increasing. At present, the production standard of copper-plastic composite tape generally refers to YD / T 723.4-2007, that is, pure copper strip is used as the base material, the thickness is above 0.1mm, and the plastic film is made of ethylene copolymer or polyethylene plastic film, and the thickness is above 0.05mm. The tensile strength of the plastic film is ≥15MPa. Further thinning the base material of the pure copper strip, thereby reducing the total thickness of the copper-plastic composi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B5/14H01B7/17H01B7/18H01B11/00H01B13/00G02B6/44B32B15/09B32B15/20B32B7/12B32B37/06B32B37/12B32B37/10
Inventor 李文君刘刚王瑛
Owner JIUXING HLDG GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com