A kind of water-based flame retardant spray glue and its preparation process

A preparation process, water-based technology, applied in adhesives, natural rubber coatings, natural rubber adhesives, etc., to achieve excellent flame retardancy, save transportation costs, and simple process

Active Publication Date: 2015-10-28
东莞智炜新材料股份有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims at various problems existing in the production and use of glue spraying at present, and provides a water-based flame-retardant spray glue and its preparation process to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A water-based flame-retardant spray glue, the ratio of its components is embodied in the process of the present invention. The preparation process of the water-based flame-retardant spray glue in this embodiment includes the following process steps (measured by parts by mass):

[0019] (1) Put 80 parts of neoprene latex, 20 parts of small molecular weight acrylic latex, 30 parts of hydrogenated rosin emulsion, 20 parts of natural latex, 2 parts of fumed silica, and 0.2 part of BYK163 dispersant into a stainless steel reaction kettle and stir evenly ;

[0020] (2) Put 10 parts of halogen-free flame retardant into a high-level interlayer heating reactor with 30 parts of deionized water, start stirring and heat up to 50°C, and stir for 10 minutes until the crystalline flame retardant is completely dissolved, and the After reaching normal temperature, add the mixture in step 1 and stir, then add 2 parts of associative thickener, and pack it out to obtain the water-based fla...

Embodiment 2

[0022] A water-based flame-retardant spray glue, the ratio of its components is embodied in the process of the present invention. The preparation process of the water-based flame-retardant spray glue in this embodiment includes the following process steps (measured by parts by mass):

[0023] (1) Put 120 parts of neoprene latex, 40 parts of small molecular weight acrylic latex, 60 parts of hydrogenated rosin emulsion, 40 parts of natural latex, 4 parts of fumed silica, and 1 part of BYK163 dispersant into a stainless steel reaction kettle and stir evenly ;

[0024] (2) Put 30 parts of halogen-free flame retardant into a high-level interlayer heating reactor containing 50 parts of deionized water, start stirring and heat up to 90°C, and stir for 60 minutes until the crystalline flame retardant is completely dissolved, and the After reaching normal temperature, add the mixture in step 1 and stir, then add 4 parts of associative thickener, and pack it out to obtain the water-base...

Embodiment 3

[0026] A water-based flame-retardant spray glue, the ratio of its components is embodied in the process of the present invention. The preparation process of the water-based flame-retardant spray glue in this embodiment includes the following process steps (measured by parts by mass):

[0027] (1) Put 100 parts of neoprene latex, 30 parts of small molecular weight acrylic latex, 50 parts of hydrogenated rosin emulsion, 30 parts of natural latex, 3 parts of fumed silica, and 0.5 part of BYK163 dispersant into a stainless steel reaction kettle and stir evenly ;

[0028] (2) Put 20 parts of halogen-free flame retardant into a high-level interlayer heating reactor containing 40 parts of deionized water, start stirring and heat up to 80°C, and stir for 30 minutes until the crystalline flame retardant is completely dissolved. After reaching normal temperature, add the mixture in step 1 and stir, then add 3 parts of associative thickener, and pack it out to obtain the water-based flam...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical fields of chemical engineering materials and preparation technologies thereof, and especially relates to an aqueous flame retardant spray adhesive and a preparation technology thereof. The preparation technology needs a simple device and has a simple process. The aqueous flame retardant spray adhesive which treats water as a diluting agent has the characteristics of no organic matter discharge, no pollution to human bodies or the environment, difficult spray gun obstruction, and no production or use danger. An aqueous resin which is the aqueous flame retardant spray adhesive has a high solid content high to 60%, saves a traffic transportation cost and also saves the liquid adhesive application amount of unit area. The aqueous spray adhesive has the advantages of strong heat resistance, excellent flame retardation performance, avoiding of the appearance of a sprayed product fire, and reduction of the continued diffusion of the fire.

Description

Technical field: [0001] The invention relates to the technical field of chemical materials and their preparation, in particular to a water-based flame-retardant spray glue and a preparation process thereof. Background technique: [0002] Spraying glue is a kind of spraying on the surface of objects to achieve a certain surface effect or to bond objects; at present, spraying glue has the following defects: [0003] 1. Most of the low-viscosity spray adhesives currently used in sofas, mattresses, pillows and other household products are chemical formulas in which thermoplastic rubber is dissolved in organic solvents and tackified resins, containing organic solvents such as benzene or methylene chloride, organic solvents It is a flammable and explosive dangerous product. Its existence will bring safety hazards to the production of adhesives and the enterprises that use the products. In addition, the volatilization and inhalation of organic substances and contact with the human ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J111/02C09J133/00C09J193/04C09J107/02C09J11/04C09D111/02C09D133/00C09D193/04C09D107/02C09D7/12
Inventor 张安洪张君侠黄桂平
Owner 东莞智炜新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com