Modified ABS high temperature resistant high polymer material
A polymer material, high temperature resistant technology, applied in the field of modified ABS high temperature resistant polymer materials, can solve the problems of insufficiency, easy to be scratched, low surface hardness, etc., to achieve good economic benefits, wide application range, comprehensive Superior performance
Inactive Publication Date: 2013-08-07
青岛永卓真塑料制品有限公司
View PDF0 Cites 11 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] ABS is a copolymer of propylene ester, I diene and styrene, which has good comprehensive properties: good chemical corrosion resistance and processing fluidity, as well as high heat resistance, toughness, impact performance and rigidity, so it is widely used In addition, ABS is also widely used in the manufacture of panels of electronic and electrical products. In order to maintain a long-term aesthetic appearance, new requirements are put forward for its surface hardness, and the surface hardness of ABS is relatively high. Low, the product is easily scratched and cannot meet the requirements of some products
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0008] A modified ABS high temperature resistant polymer material, comprising the following parts by weight: 30-80 parts of ABS resin, 20-25 parts of glass fiber, 2-9 parts of compatibilizer, 10-20 parts of organic solvent, concentrated 10-30 parts of hydrochloric acid, 20-23 parts of curing agent, 10-20 parts of methylphenylsiloxane branched prepolymer, 10-15 parts of modifier, 10-19 parts of pigment, 10-25 parts of diluent 10-25 parts of toughening agent, 10-35 parts of active calcium, 20-35 parts of stearic acid, 21-23 parts of lithopone, 1-3 parts of carbon black, 1-9 parts of nano calcium carbonate, stearin 1-9 parts of acid, 1-8 parts of talcum powder, 2-9 parts of EPDM rubber, 3-6 parts of anti-impact agent.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a modified ABS (acrylonitrile butadiene styrene) high temperature resistant high polymer material, which comprises the following substances by weight: 30-80 parts of ABS resin, 20-25 parts of a glass fiber, 2-9 parts of a compatilizer, 10-20 parts of an organic solvent, 10-30 parts of concentrated hydrochloric acid, 20-23 parts of a curing agent, 10-20 parts of methylphenyl siloxane branched chain prepolymer, 10-15 parts of a modifier, 10-19 parts of a pigment, 10-25 parts of a diluent, 10-25 parts of a toughening agent, 10-35 parts of active calcium, 20-35 parts of stearic acid, 21-23 parts of lithopone, 1-3 parts of carbon black, 1-9 parts of nano-calcium carbonate, 1-9 parts of stearic acid, 1-8 parts of talcum powder, 2-9 parts of ethylene-propylene-diene monomer rubber, and 3-6 parts of an anti-impact agent. The modified ABS high temperature resistant high polymer material disclosed in the invention has superior comprehensive performance and a wide application range, thus having very good economic benefits.
Description
technical field [0001] The invention relates to a modified ABS high temperature resistant polymer material. Background technique [0002] ABS is a copolymer of propylene ester, I diene and styrene, which has good comprehensive properties: good chemical corrosion resistance and processing fluidity, as well as high heat resistance, toughness, impact performance and rigidity, so it is widely used In addition, ABS is also widely used in the manufacture of panels of electronic and electrical products. In order to maintain a long-term aesthetic appearance, new requirements are put forward for its surface hardness, and the surface hardness of ABS is relatively high. Low, the product is easily scratched, and cannot meet the requirements of some products. Contents of the invention [0003] The technical problem to be solved by the invention is to provide a modified ABS high temperature resistant polymer material. [0004] In order to solve the problems of the technologies describ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L23/16C08K13/04C08K7/14C08K5/09C08K3/04C08K3/26C08K3/34
Inventor 李耀东
Owner 青岛永卓真塑料制品有限公司