A foamed relief wall base cloth of nano-bamboo charcoal and diatom mud and its preparation process

A nano-bamboo charcoal and preparation process technology, applied in the field of decoration and decoration materials, can solve the problems of small vertical and horizontal tensile force, monotonous weaving of textile patterns, loss in the event of fire, small difference in vertical and horizontal strength, overcoming weak relief feeling, and repeated use. long life effect

Active Publication Date: 2016-01-06
青岛润东新型建筑材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Since the main component of the paper base of the wallpaper is wood pulp, its composition determines that the vertical and horizontal tensile force is small, it is easy to deform after being wet, it is not suitable for repair, the content of organic matter is high, it is not anti-aging, low strength, poor stability, and not resistant to acid and alkali; The environment with high humidity and the wall are prone to mildew, moth and rot. At the same time, it is not resistant to high temperature, poor in flame retardancy, and will suffer heavy losses in case of fire.
The main component of the traditional wall base cloth is made of glass fiber yarn through weaving, which has the advantages of high temperature resistance, good flame retardancy, strong vertical and horizontal tensile force, not easy to deform, and long service life, but its disadvantage is that the weaving pattern is monotonous, The three-dimensional effect is not strong, the decorative performance is poor, and it cannot purify the air

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Preparation of nano-bamboo charcoal diatom mud foam slurry

[0034] Prepare the nano bamboo charcoal diatom mud foaming slurry according to the weight percentage of the following raw materials: 25% of nano bamboo charcoal powder, 25% of acrylic emulsion, 20% of titanium dioxide, 15% of diatom mud, 10% of azodicarbonamide foaming agent, Purified water 10%, mineral oil defoamer 0.2%, wetting agent P-40 0.3%, hydroxyethyl cellulose 0.1%, acrylic dispersant 0.2%, alcohol ester twelve film-forming aid 0.1%, CMIT fungicide 0.2%, flame retardant tetrabromobisphenol A 1.0%;

[0035] Among them, the nano-bamboo charcoal powder is 3000 mesh, the solid content of the acrylic emulsion is 50%, the titanium dioxide is 800 mesh, and the diatom mud is 1000 mesh;

[0036] The density of the prepared nano-bamboo charcoal diatom mud foaming slurry is 1.45-1.88g / cm 3 , the decomposition and foaming temperature in air is 130-150°C, and the foaming amount is 200-260ml / g;

[0037] (2) ...

Embodiment 2

[0047] (1) Preparation of nano-bamboo charcoal and diatom mud foam slurry

[0048] Prepare the nano bamboo charcoal diatom mud foaming slurry according to the weight percentage of the following raw materials: 35% of nano bamboo charcoal powder, 35% of acrylic acid emulsion, 30% of titanium dioxide, 25% of diatom mud, 20% of azodicarbonamide foaming agent, Purified water 20%, mineral oil defoamer 0.5%, wetting agent P-40 0.9%, hydroxyethyl cellulose 0.3%, acrylic dispersant 0.4%, alcohol ester twelve film-forming aid 0.4%, CMIT fungicide 0.6%, flame retardant tetrabromobisphenol A 1.5%;

[0049] Among them, the nano-bamboo charcoal powder is 3000 mesh, the solid content of the acrylic emulsion is 50%, the titanium dioxide is 1000 mesh, and the diatom mud is 1000 mesh;

[0050] The density of the prepared nano-bamboo charcoal diatom mud foaming slurry is 1.45-1.88g / cm 3 , the decomposition and foaming temperature in air is 130-150°C, and the foaming amount is 200-260ml / g;

[...

Embodiment 3

[0060] (1) Preparation of nano-bamboo charcoal and diatom mud foam slurry

[0061] Prepare the nano bamboo charcoal diatom mud foaming slurry according to the weight percentage of the following raw materials: 30% of nano bamboo charcoal powder, 30% of acrylic emulsion, 25% of titanium dioxide, 20% of diatom mud, 15% of azodicarbonamide foaming agent, Purified water 15%, mineral oil defoamer 0.5%, wetting agent P-40 0.9%, hydroxyethyl cellulose 0.3%, acrylic dispersant 0.4%, alcohol ester twelve film-forming aid 0.4%, CMIT fungicide 0.6%, flame retardant tetrabromobisphenol A 1.5%;

[0062] Among them, the nano-bamboo charcoal powder is 3000 mesh, the solid content of the acrylic emulsion is 50%, the titanium dioxide is 900 mesh, and the diatom mud is 1000 mesh;

[0063] The density of the prepared nano-bamboo charcoal diatom mud foaming slurry is 1.45-1.88g / cm 3 , the decomposition and foaming temperature in air is 130-150°C, and the foaming amount is 200-260ml / g;

[0064] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
heightaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses foaming relief wall base cloth made of nano bamboo charcoal diatom mud and a production process thereof. The production process comprises respectively utilizing polyester non-woven fabrics, nylon non-woven fabrics or quartz fabrics as base materials; utilizing the nano bamboo charcoal diatom mud to foam slurry; performing printing and drying through a mould gravure mixing wallpaper production line or a bedplate printing machine; performing foaming through a tunnel furnace and performing slitting after cooling; and performing sorting and packaging to obtain finished products of the foaming relief wall base cloth made of the nano bamboo charcoal diatom mud. The foaming relief wall base cloth made of the nano bamboo charcoal diatom mud has the advantages of being strong in humidifying capability, harmful gas absorption capability and antibacterial capability, strong in decorative three-dimensional sense, attractive in appearance and elegant, good in permeability, stable in performance, ageing resistant, acid and alkali resistant, non-toxic, mould proof and moth proof at the same time, enabling people to decorate the beautiful home life and easily enjoy the fresh and healthy quality life with families brought by the foaming relief wall base cloth made of the nano bamboo charcoal diatom mud at the same time and the like.

Description

technical field [0001] The invention belongs to the technical field of decoration materials, and in particular relates to a foamed relief wall base cloth of nano-bamboo charcoal and diatom mud and a preparation process thereof. Background technique [0002] Wallpaper and wall base cloth are widely used wall decoration materials in the modern decoration industry. [0003] Since the main component of the paper base of the wallpaper is wood pulp, its composition determines that the vertical and horizontal tensile force is small, it is easy to deform after being wet, and it is not suitable for repair. The environment with high humidity and the wall are prone to mildew, insects and rot. At the same time, it is not resistant to high temperature, has poor flame retardancy, and will suffer heavy losses in case of fire. The main component of the traditional wall base cloth is made of glass fiber yarn through weaving, which has the advantages of high temperature resistance, good flam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/075D06P5/00
Inventor 王贵琦
Owner 青岛润东新型建筑材料科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com