A kind of alumina, high-purity technology, applied in the field of preparation of high-purity alumina, can solve the problems of low content, high price, environmental pollution, etc., and achieve the effect of high purity and less impurities
Inactive Publication Date: 2013-09-11
RUGAO CITY LEHENG CHEM COMPANY
View PDF0 Cites 7 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, for alumina used in phosphor powder, coatings, gemstones, high-pressure sodium lamp tubes, glass additives, electronic ceramics, catalyst carriers, etc., the impurity requirements are more stringent, and ordinary metallurgical-grade alumina cannot meet the use requirements, while traditional Industrialized alumina produced by Bayer method, soda lime sintering method or a combination of the two methods can only obtain Al due to raw material and process reasons. 2 o 3 Low content, impurity SiO 2 、Na 2 Ordinary alumina with high O content
[0003] At present, the main methods for preparing high-purity alumina powder are: improved Bayer method, ammonium alum decomposition method and its improved ammonium aluminum carbonate thermal decomposition method, organic aluminum decomposition method, aluminum powder water discharge method, and some of these methods are cheap But the performance is poor, some have good performance but the price is high, the process is complicated, and some also cause pollution to the environment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] 1) Add industrial 500gAl to the reaction tank 2 (SO 4 ) 3 18H 2 O was dissolved in 750ml of water and heated to boiling, adding 110g (NH 4 ) 2 SO 4 Stir to dissolve the solid, select a high-molecular PE microporous tube for ultra-fine microporous filtration, cool to room temperature under constant stirring, a large number of white crystals precipitate, filter the crystals with suction, rinse with a small amount of water once, and drain to obtain a crystallization;
[0019] 2) In the crystallization tank, add 500g of primary crystallized ammonium aluminum sulfate into 500ml of water, heat to dissolve, then cool to room temperature under stirring, filter and crystallize with suction to obtain a white crystal wet product, dry the wet product in an oven at 90°C Obtain aluminum ammonium sulfate crystals;
[0020] 3) Add 10% ammonia water to the obtained aluminum ammonium sulfate crystals to obtain aluminum hydroxide gel, add deionized water to wash, and use ion exchang...
Embodiment 2
[0023] 1) Add industrial 500gAl to the reaction tank 2 (SO 4 ) 3 18H 2 O was dissolved in 750ml of water and heated to boiling, adding 110g (NH 4 ) 2 SO 4 Stir to dissolve the solid, select a high-molecular PE microporous tube for ultra-fine microporous filtration, cool to room temperature under constant stirring, a large number of white crystals precipitate, filter the crystals with suction, rinse with a small amount of water once, and drain to obtain a crystallization;
[0024] 2) In the crystallization tank, add 500g of primary crystallized ammonium aluminum sulfate to 500ml of water,
[0025] Heat to dissolve, then cool to room temperature under stirring, suction filter and crystallize to obtain a white crystal wet product, dry the wet product in an oven at 90°C to obtain aluminum ammonium sulfate crystals;
[0026] 3) Add 10% ammonia water to the obtained aluminum ammonium sulfate crystals to obtain aluminum hydroxide gel, add deionized water to wash, and use ion ex...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a preparation method of high-purity aluminum oxide. The preparation method comprises the following steps of: with industrial Al2(SO4)3.18H2O and (NH4)2SO4 solids as raw materials, preparing an aluminum ammonium sulfate crystal by utilizing a recrystallization method; adding ammonia water to the obtained aluminum ammonium sulfate crystal to obtain an aluminum hydroxide gel; purifying with an aluminum-type mixed resin to obtain a high-purity aluminum hydroxide gel; distilling the obtained aluminum hydroxide gel at reduced pressure to obtain aluminum hydroxide colloidal particles; roasting the aluminum hydroxide colloidal particles for 1 to 2 hours at 1,000 to 1,200 DEG C through a muffle so as to obtain aluminum oxide powder. According to the preparation method, the aluminum ammonium sulfate crystal is prepared by utilizing the recrystallization method, so that the crystal has less impurity; and the prepared aluminum hydroxide sol is purified by the ion exchange resin to obtain the high-purity aluminum hydroxide gel, and then the high-purity aluminum hydroxide gel is roasted to obtain the aluminum oxide which is high in purity.
Description
technical field [0001] The invention relates to a method for preparing high-purity alumina. Background technique [0002] Alumina has a wide range of industrial uses. Commonly used metallurgical grade alumina is mainly suitable for the production of aluminum metal by dissolved salt electrolysis, and is also suitable for the production of corundum, ceramics, refractory materials and other alumina chemicals. However, for alumina used in phosphor powder, coatings, gemstones, high-pressure sodium lamp tubes, glass additives, electronic ceramics, catalyst carriers, etc., the impurity requirements are more stringent, and ordinary metallurgical-grade alumina cannot meet the use requirements, while traditional Industrialized alumina produced by Bayer method, soda lime sintering method or a combination of the two methods can only obtain Al due to raw material and process reasons. 2 o 3 Low content, impurity SiO 2 、Na 2 Ordinary alumina with high O content. [0003] At present, t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more