Crucible and preparation method thereof
A technology of crucible and silicon monoxide, which is applied in glass manufacturing equipment, manufacturing tools, glass forming, etc., and can solve the problems of low crucible strength, variable crucibles, and easy breakage of crucibles, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0010] The method for preparing the crucible disclosed in the present invention includes mixing a raw material composition to obtain a slurry, then homogenizing, mixing, and shaping the slurry to obtain a green body, and drying and sintering the green body to obtain a crucible; wherein, the raw material composition It includes the first fused silica sand and deionized water; and, before the molding, it also includes adding silicon monoxide to the slurry.
[0011] According to the present invention, the first fused silica sand in the above-mentioned raw material composition is well-known in the art. In order to reduce the influence of impurities in the raw material on the product crucible, preferably, the SiO in the first fused silica sand 2 The content is above 99.95wt%.
[0012] For the above-mentioned first fused silica sand, preferably, the first fused silica sand includes fused silica sand A and fused silica sand B, and based on the total weight of the first fused silica sand, t...
Example Embodiment
[0030] Example 1
[0031] This embodiment is used to illustrate the method for preparing the crucible and the crucible disclosed in the present invention.
[0032] The raw materials used in this embodiment are as follows:
[0033] The first fused silica sand: the content of SiO2 is 99.95wt%, and the particle size composition of the first fused silica sand is 30wt% with a particle size of 5-20mm, and 70wt% with a particle size of 1-2mm.
[0034] 100 parts by weight of the first fused silica sand, 20 parts by weight of deionized water and 0.5 parts by weight of 99.0% silicon monoxide were added to the ball mill and ball milled for 10 hours, and the slurry obtained after ball milling was homogenized. Stir continuously at 20r / min. The total time of homogenization is 8 days. On the 7th day of homogenization, 0.6wt% gum arabic is added to account for the weight of the slurry, and the homogenized slurry is mixed with the second fused silica sand. Mix in a mixing box for 2 hours, where, ba...
Example Embodiment
[0035] Example 2
[0036] This embodiment is used to illustrate the method for preparing the crucible and the crucible disclosed in the present invention.
[0037] The raw materials used in this embodiment are as follows:
[0038] The first fused silica sand: the content of SiO2 is 99.99wt%, and the particle size composition of the first fused silica sand is: 20wt% with a particle size of 15-40mm, and 80wt% with a particle size of 2-4mm.
[0039] 100 parts by weight of fused silica, 36 parts by weight of deionized water and 2 parts by weight of silicon monoxide with a purity of 99.5% were added to the ball mill and ball milled for 12 hours. The slurry obtained after ball milling was homogenized, and the homogenization rate was 30r / Min continuous stirring, the total time of homogenization is 10 days. On the 9th day of homogenization, 0.1wt% of carboxymethyl cellulose is added to the slurry, and the homogenized slurry is combined with the second Fused silica sand was mixed in the mix...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap