Metal protective paint and application thereof, and hot-dip metal material

A metal protective coating and raw material technology, applied in the field of hot-dip metal materials and metal protective coatings, can solve the problems of poor corrosion resistance, water resistance, heat resistance and fingerprint resistance of the protective film

Inactive Publication Date: 2013-10-23
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the defects of poor corrosion resistance, water resistance, heat resistance and fingerprint resistance of the protective film formed by the existing metal protective coating, and to provide a protective film capable of forming corrosion resistance, water resistance and heat resistance. Protective coating for metal with a protective film with good anti-fingerprint and anti-fingerprint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal protective paint and application thereof, and hot-dip metal material
  • Metal protective paint and application thereof, and hot-dip metal material
  • Metal protective paint and application thereof, and hot-dip metal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] With 1 weight part of water-soluble silicate (sodium silicate, purchased from Baoding Runfeng Industrial Co., Ltd.), 0.6 weight part of accelerator (pyrrolidone), 1.6 weight part of C 6 h 11 NHCH 2 CH 2 CH 2 Si(OCH 3 ) 3 (purchased from Hubei Limeida Silicon Fluoride Technology Co., Ltd., brand LMD-58), 0.72 parts by weight of silica filler (nano silica powder, purchased from GE Company of the United States, RNS-E, average particle size 20nm), 2.4 The water-soluble film-forming resin (water-soluble silicon-acrylic film-forming resin (Qingdao Xingguo Paint Company TC-05 type silicon-acrylic emulsion, solid content is 48% by weight)) of weight part (in solids) and the water of 28 weight parts, in Mix until uniform at a stirring speed of 1500 rpm to obtain the metal protective coating of this embodiment.

Embodiment 2

[0048] With 1 weight part of water-soluble silicate (potassium silicate, purchased from Baoding Runfeng Industrial Co., Ltd.), 0.5 weight part of accelerator (pyrrolidone), 1.4 weight part of C 6 h 11 NHCH 2 CH 2 CH 2 Si(OCH 3 ) 3 (purchased from Hubei Limeida Silicon Fluoride Technology Co., Ltd., brand LMD-58), 0.6 parts by weight of silica filler (nano silica, purchased from GE Company of the United States, RNS-E, average particle size 20nm), 2.1 parts by weight Parts (in solid terms) of water-soluble film-forming resin (water-soluble acrylic film-forming resin (acrylic resin purchased from Guangzhou Oupeng Chemical Industry's brand is A-3418)) and 25 parts by weight of water, at 1500 rpm Mix until uniform at a stirring speed to obtain the protective metal coating of this embodiment.

Embodiment 3

[0050] With 1 weight part of water-soluble silicate (sodium silicate, purchased from Baoding Runfeng Industrial Co., Ltd.), 0.7 weight part of accelerator (pyrrolidone), 1.8 weight part of C 6 h 11 NHCH 2 CH 2 CH 2 Si(OCH 3 ) 3 (purchased from Hubei Limeida Silicon Fluoride Technology Co., Ltd., brand LMD-58), 0.85 parts by weight of silica filler (30% by weight of silica sol, the usage amount is calculated as solid), 2.7 parts by weight (calculated as solid) Water-soluble film-forming resin (water-soluble polyurethane film-forming resin (purchased from Fujian Jinjiang Jianhua Company, the polyurethane resin of brand 812)) and the water of 40 parts by weight are mixed to uniform under the stirring speed of 1500 rev / mins, obtain this implementation Examples of metal protective coatings.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a metal protective paint which is prepared by uniformly mixing a raw material mixture, wherein the raw material mixture contains water-soluble silicate, silicon oxide filler, accelerator, water-soluble film-forming resin, C6H11NHCH2CH2CH2Si(OCH3)3 and water; and the accelerator is at least one of pyrrolidone, N-methylpyrrolidone and N-ethylpyrrolidone. The invention also discloses application of the metal protective paint in preparation of metal materials. The invention also provides a hot-dip metal material which comprises a hot-dip metal substrate and a coating attached to the hot-dip metal substrate, wherein the coating is the cured product of the metal protective paint. The protective film formed by the metal protective paint provided by the invention has very excellent corrosion resistance, water resistance, heat resistance and fingerprint resistance.

Description

technical field [0001] The invention relates to the field of metal protection, in particular to a metal protection coating, the application of the metal protection coating and a hot-dip metal material. Background technique [0002] Hot-dip metal materials, including hot-dip galvanized metal materials and hot-dip galvanized metal materials, in order to prevent corrosion, a layer of metal protective paint will be coated on the surface of the hot-dip metal materials to form a protective film. Therefore, the performance of metal protective coatings is very important for the anti-corrosion of hot-dip metal materials. [0003] For example, CN101608306A discloses a passivation solution, which also belongs to a metal protective coating, and is characterized in that the passivation solution is an aqueous solution containing a water-soluble molybdenum compound, boric acid, water-soluble organic matter and silica sol, wherein the water-soluble The organic compound is a mixture of alco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/08C09D7/12C09D167/00C09D125/14C09D163/00C09D175/04C09D133/04C09D133/00C09D127/12
Inventor 许哲峰梅东生陈永徐权郭太雄娄燕周一林
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com