Wear-resistant reinforced pom and preparation method thereof

A technology of antioxidant and polyoxymethylene, applied in the field of wear-resistant reinforced POM and its preparation, can solve the problems of lack of reinforcement effect, difficulty in compatibility between resin and glass fiber, etc., and achieve good resistance to ultraviolet radiation and excellent mechanical properties , easy to promote the effect of the application

Active Publication Date: 2016-01-20
WUJIANG YINGLIDA PLASTIC PACKAGING
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for the reinforcement modification of POM, due to the high crystallinity of POM, it is difficult to achieve good compatibility between resin and glass fiber, so that no obvious reinforcement effect can be achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant reinforced pom and preparation method thereof
  • Wear-resistant reinforced pom and preparation method thereof
  • Wear-resistant reinforced pom and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Wear-resistant reinforced POM includes the following raw materials in parts by weight: 80 parts of polyoxymethylene, 12 parts of carbon fiber, 1 part of polytetrafluoroethylene, 2 parts of nano-montmorillonite, 0.2 parts of nano-zinc oxide, 2642 parts of antioxidants, Polypropylene grafted maleic anhydride 1 part, ethylene bis-stearamide 0.2 part, polycyanamide 0.5 part, titanate coupling agent 1 part, 2,4,6-tris(2'-hydroxy-4'- N-Butoxyphenyl)-1,3,5-triazine 0.5 parts.

[0017] The preparation method of the wear-resistant reinforced POM includes the following steps: grafting polyoxymethylene, polytetrafluoroethylene, nano-montmorillonite, nano-zinc oxide, antioxidant 264, polypropylene grafting maleic anhydride, and ethylene bis-stearamide , Polycyanamide, titanate coupling agent and 2,4,6-tris(2'-hydroxy-4'-n-butoxyphenyl)-1,3,5-triazine are placed in the mixer, The mixing is uniform, and the mixed materials are mixed and extruded by adding carbon fiber from the side und...

Embodiment 2

[0019] Wear-resistant reinforced POM, including the following raw materials in parts by weight: 100 parts of polyformaldehyde, 18 parts of carbon fiber, 5 parts of polytetrafluoroethylene, 5 parts of nano-montmorillonite, 0.5 parts of nano-zinc oxide, 2645 parts of antioxidants, 2 parts of polypropylene grafted maleic anhydride, 0.4 parts of ethylene bisstearamide, 1.2 parts of polycyanamide, 2 parts of titanate coupling agent, 2,4,6-tris(2'-hydroxy-4'- 1.2 parts of n-butoxyphenyl)-1,3,5-triazine.

[0020] The preparation method of the wear-resistant reinforced POM of this embodiment is the same as that of the first embodiment.

Embodiment 3

[0022] Wear-resistant reinforced POM includes the following raw materials in parts by weight: 90 parts of polyoxymethylene, 15 parts of carbon fiber, 3 parts of polytetrafluoroethylene, 4 parts of nano-montmorillonite, 0.3 parts of nano-zinc oxide, 2644 parts of antioxidants, Polypropylene grafted maleic anhydride 1.2 parts, ethylene bis-stearamide 0.3 parts, polycyanamide 0.8 parts, titanate coupling agent 1.5 parts, 2,4,6-tris(2'-hydroxy-4'- 0.9 parts of n-butoxyphenyl)-1,3,5-triazine.

[0023] The preparation method of the wear-resistant reinforced POM of this embodiment is the same as that of the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to wear-resistant reinforced POM (polyformaldehyde) and a preparation method thereof, and belongs to the technical field of a high polymer material. The wear-resistant reinforced POM comprises the following raw materials in part by weight: 80 to 100 parts of polyformaldehyde, 12 to 18 parts of carbon fibers, 1 to 5 parts of polytetrafluoroethylene, 2 to 5 parts of nano-montmorillonite, 0.2 to 0.5 part of nano zinc oxide, 2 to 5 parts of antioxidant, 1 to 2 parts of polypropylene maleic anhydride, 0.2 to 0.4 part of ethylene bis stearamide, 0.5 to 1.2 parts of formaldehyde absorbent, 1 to 2 parts of titanate coupling agent and 0.5 to 1.2 parts of 2,4,6-tri(2-hydroxy-4-butoxy-phenyl)-1,3,5-triazine. The preparation method disclosed by the invention is simple; the prepared wear-resistant reinforced POM has excellent mechanical performance, excellent wear resistance and excellent resistance to ultraviolet radiation, also has a certain antibacterial capacity and can be widely used in the fields of electronic and electrical engineering, machinery, instruments, daily light industry, automobile, building materials, agriculture and the like.

Description

Technical field [0001] The invention belongs to the technical field of polymer materials, and specifically relates to wear-resistant reinforced POM and a preparation method thereof. Background technique [0002] Polyoxymethylene, abbreviated as POM in English, is a kind of thermoplastic crystalline polymer, known as "super steel" or "sai steel", also known as polyoxymethylene. POM has the hardness, strength and rigidity similar to that of metal. It has good self-lubricity, good fatigue resistance and elasticity in a wide range of temperature and humidity. In addition, it has good chemical resistance. Quality, but it has the disadvantage of not being resistant to sunlight and ultraviolet radiation. [0003] At a lower cost than many other engineering plastics, POM is replacing some of the markets traditionally occupied by metals, such as replacing zinc, brass, aluminum and steel to make many parts. Since its inception, POM has been widely used in electronics, electrical, machinery ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L59/00C08L27/18C08L51/06C08K13/04C08K7/06C08K3/34C08K3/22C08K5/20C08K5/10C08K5/3492B29B9/06B29C47/92B29C48/92
CPCB29B7/90B29B9/14B29B2009/125B29C48/022B29C48/04B29C48/40
Inventor 倪迪
Owner WUJIANG YINGLIDA PLASTIC PACKAGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com