Comprehensive treatment agent and use method thereof

A comprehensive treatment agent and treatment agent technology, applied in the direction of metal material coating process, etc., can solve the problems of high maintenance cost, large equipment investment, large environmental pollution, etc., and achieve low treatment cost, good treatment effect and high corrosion resistance Effect

Inactive Publication Date: 2013-12-11
谢俊磊
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a comprehensive treatment agent and its use method to solve the problems of large equipment investment, high maintenance cost, cumbersome operation and problems caused by using different treatment agents for each different step in the prior art. The problem of high environmental pollution and low treatment efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Comprehensive treatment agent and use method thereof
  • Comprehensive treatment agent and use method thereof
  • Comprehensive treatment agent and use method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0072] Weigh the quantitative reagent according to the following formula ratio, phosphoric acid (27.5%), zinc oxide (2.0%), sodium molybdate (0.3%), zinc dihydrogen phosphate (5.5%), potassium chlorate (0.7%), OP-10 (0.2 %), TX-10 (0.2%), SDBS (0.4%), triethanolamine (1.3%), citric acid (1.2%), thiourea (0.15%), deionized water (60.55%). The treatment agent is prepared according to the preparation method of the multifunctional shell surface treatment agent. The shell cleaning operation is carried out by spraying method. The operating conditions are as follows: spraying pressure 0.12MPa, solution temperature 35°C, spraying time 2.5min, ambient temperature 20°C. The test results show that under the above operating conditions, the formula has a rust removal rate of 99.4%, an oil removal rate of 99.0%, and the quality of the phosphating film formed is 1.42g / m2. The phosphating film is uniform and dense, and has good corrosion resistance. The test time is 1.6min. The soaking oper...

Embodiment 3

[0074] Weigh the quantitative reagent according to the following formula ratio, phosphoric acid (30.0%), zinc oxide (2.0%), sodium molybdate (0.5%), zinc dihydrogen phosphate (4.0%), potassium chlorate (0.7%), OP-10 (0.3 %), TX-10 (0.2%), SDBS (0.4%), triethanolamine (1.3%), citric acid (1.2%), thiourea (0.15%), deionized water (59.25%). The treatment agent is prepared according to the preparation method of the multifunctional shell surface treatment agent. Use the spray method to clean the shells. The operating conditions are as follows: spray pressure 0.15MPa, solution temperature 40°C, spray time 3min, ambient temperature 20°C. Under the above operating conditions, the formula has a rust removal rate of 99.6% and an oil removal rate of 98.5%. The quality of the phosphating film formed is 1.37g / m2. The phosphating film is relatively uniform, has slight pores, and has good corrosion resistance. , CuSO4 drop test time is 1.4min. The soaking operation conditions are as follow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a comprehensive treatment agent, which comprises, by mass, 25.0-30.0% of phosphoric acid, 1.0-3.0% of zinc oxide, 0.1-0.5% of sodium molybdate, 4.0-7.0% of zinc dihydrogen phosphate, 0.3-1.2% of potassium chlorate, 0.3-1.2% of a surfactant, 0.0-2.3% of triethanolamine, 0.8-2.3% of citric acid, 0.1-0.3% of thiourea, and 58.0-62.6% of water. According to the present invention, the treatment agent can be recycled, a treatment cost is low, and pollution on the environment can not be generated.

Description

technical field [0001] The invention relates to the field of treatment agents, in particular to a comprehensive treatment agent and its application method. Background technique [0002] In the surface treatment of shells, the surface treatment of ammunition, mainly degreasing and phosphating, includes degreasing, rust removal, phosphating, and passivation. The oil on the surface of shells is mainly To protect macromolecular substances such as grease, the rust on the surface of the shell is mainly various oxides of iron. The phosphating of the surface of the shell is to cover the surface of the shell with a layer of phosphate to achieve the purpose of anti-corrosion. After phosphating, the surface of the shell needs to be treated Passivation treatment greatly reduces the chemical activity of the active metal or alloy, and becomes a noble metal state, and then undergoes subsequent treatment. The existing technology uses different treatment agents for each different step, resu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/42C23G1/02
Inventor 张怀智谢俊磊曹宏安钱芳黄鹏波刘鹏安
Owner 谢俊磊
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap