Modified urea-formaldehyde resin adhesive and preparation technology thereof
A urea-formaldehyde resin and adhesive technology, applied in the direction of adhesives, aldehyde/ketone condensation polymer adhesives, adhesive types, etc., can solve the problems of increased gas generation, poor heat resistance of resins, decreased strength, etc., and achieve prolonged activity. effect of improving heat resistance and stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment
[0020] Urea 20-30
[0021] Formaldehyde (37%) 70-80
[0022] Nitric acid 1.5-2.5
[0023] Calcium hydroxide (15%-30%) 0.5-1
[0024] Sodium bicarbonate 2.5-3.5
[0025] Furfuryl alcohol 25-30
[0026] Appropriate amount of water.
[0027] Add formaldehyde and sodium bicarbonate aqueous solution in the stirred tank, after stirring evenly, add calcium hydroxide solution, adjust reactant pH value to be 7-8;
[0028] Add urea and nitric acid, raise the reaction temperature to 90-95°C, and react for about 1 hour. The urea first undergoes an addition reaction with formaldehyde, and then further undergoes a polycondensation reaction to form a resin;
[0029] Take 15 parts of the above-prepared resin and 85 parts of furfuryl alcohol, put the two liquids into another reaction kettle, stir well, adjust the pH value to 5-6 with nitric acid, and cool down to 70°C after reacting for 1 hour;
[0030] Connect the vacuum system, close the reflux condenser, and contro...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap