Fireproof plaster board and production method thereof

A paper-faced gypsum board and gypsum technology, which is applied in the field of building materials, can solve the problems of poor adsorption of harmful gases, low impact strength, and poor fire resistance, and achieve good market prospects, strong fire resistance, and improved performance parameters.

Inactive Publication Date: 2014-01-29
海门市创豪工业设计有限公司
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to overcome the disadvantages of poor fire resistance, low flexural strength and impact strength, easy to be affected by moisture, and poor ability to absorb harmful gases in the existing technology of paper-faced gypsum boards, the present invention provides a paper-faced gypsum board with high performance parameters in all aspects. Surface gypsum board, which is far superior to general products in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A fire-resistant paper-faced gypsum board, which is composed of a middle gypsum matrix and face-protecting papers on the upper and lower sides (the upper and lower sides are the same face-protecting paper); the gypsum base and the face-protecting paper are bonded by bonding materials made;

[0022] The gypsum matrix is ​​prepared as follows:

[0023] Take the following raw materials by weight: 100 parts of gypsum powder, 30 parts of diatomite, 20 parts of pyrite powder, 15 parts of dolomite powder, 10 parts of talcum powder, 10 parts of chitin, 8 parts of glass fiber, 8 parts of borax, 8 parts of polyvinyl alcohol, 6 parts of starch ether, 6 parts of hydroxyethyl cellulose, 2 parts of phenolic resin, 1 part of sodium succinate and 50 parts of water; mix the above raw materials evenly, then put them into a mortar mixer, and stir evenly to obtain Mix the slurry, then inject the mixed slurry into the mold and cast it into a plate, demould after the plate is solidified, an...

Embodiment 2

[0032] A fire-resistant paper-faced gypsum board, which is composed of a middle gypsum matrix and face-protecting papers on the upper and lower sides (the upper and lower sides are the same face-protecting paper); the gypsum base and the face-protecting paper are bonded by bonding materials made;

[0033] The gypsum matrix is ​​prepared as follows:

[0034] Take the following raw materials by weight: 120 parts of gypsum powder, 40 parts of diatomite, 30 parts of pyrite powder, 20 parts of dolomite powder, 10 parts of talcum powder, 10 parts of chitin, 8 parts of glass fiber, 8 parts of borax, 8 parts of polyvinyl alcohol, 6 parts of starch ether, 6 parts of hydroxyethyl cellulose, 2 parts of phenolic resin, 1 part of sodium succinate and 50 parts of water; mix the above raw materials evenly, then put them into a mortar mixer, and stir evenly to obtain Mix the slurry, then inject the mixed slurry into the mold and cast it into a plate, demould after the plate is solidified, an...

Embodiment 3

[0043] Charcoal environmental protection paper surface gypsum board performance parameter test detection:

[0044] Comparative test 1: Gypsum board prepared according to the patent method (CN200710139236); gypsum board prepared in Example 1, the results are shown in Table 1.

[0045] Table 1

[0046] group Maximum operating temperature °C Compressive strengthkpa Thermal conductivity W / (m.K) 2h water absorption thickness expansion rate% Flexural modulus of elasticity mpa Comparative test 1 600 178 0.068 0.82 3547 Embodiment 1 of the present invention 1000 309 0.027 0.21 7431

[0047]After testing, the flame retardant performance of the plasterboard prepared by the present invention is A1 grade, and the fire stability time is more than 70 minutes (refer to GB / T9775-2008 standard); the removal rate of free formaldehyde in the living room can reach more than 48%. , The removal rate of ammonia is more than 30%, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of build environment-friendly materials and discloses a fireproof plaster board. The fireproof plaster board is formed by a plaster base body and protective paper; the plaster base body is arranged in the middle; the protective paper is arranged on the upper side and the lower side; binding materials are bound between the plaster base body and the protective paper. The produced fireproof plaster board has the advantages of being good in fire resistance, environmentally friendly and free of pollution, greatly improving the mechanical performance such as the compressive and bending strength and being good in market prospect.

Description

[0001] technical field [0002] The invention belongs to the field of building materials, and in particular relates to a fire-resistant paper-faced gypsum board and a preparation method thereof. Background technique [0003] Fire refers to the disaster caused by burning out of control in time and space. Among various disasters, fire is one of the main disasters that most frequently and commonly threaten public safety and social development. Human beings can use and control fire, which is an important symbol of civilization progress. Therefore, the history of human use of fire and the history of fighting against fire go hand in hand. While using fire, people constantly summarize the law of fire occurrence and minimize fire and its harm to human beings. At present, common fires are building fires, which seriously endanger human life safety and property safety. How to provide the fire performance of building materials is a problem that needs to be solved. [0004] Gypsum bo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/077C04B28/14D21H27/00C09J123/08C09J131/02C09J189/00C04B111/28
Inventor 王开学
Owner 海门市创豪工业设计有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap