Preparation method of super-hydrophilic oleophobic net film and application thereof in oil water separation

A super-hydrophilic and omentum technology, which is applied in the fields of chemistry, chemical engineering and functional materials, can solve the problems of complex preparation process, easy pollution and separation omentum, complex process, etc., and achieve simple preparation process, good application prospect and good separation effect Effect

Inactive Publication Date: 2014-02-19
TIANJIN UNIVERSITY OF TECHNOLOGY
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese invention patents CN101708384A, CN101518695, CN1721030A, etc. have reported the oil-water separation omentum with superhydrophobic and super lipophilic functions, but the above-mentioned omentum is not suitable for the separation of oil-water mixture of a small amount of oil in a large amount of water, and it is easy to pollute the separation omentum, etc.
[0004] Chinese invention patents CN102350094A, CN103316507A etc. report a kind of oil-water separator with superhydrophilicity and underwater superoleophobicity, but the process is complic...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of super-hydrophilic oleophobic net film and application thereof in oil water separation
  • Preparation method of super-hydrophilic oleophobic net film and application thereof in oil water separation
  • Preparation method of super-hydrophilic oleophobic net film and application thereof in oil water separation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for preparing a superhydrophilic and oleophobic mesh, using a brass mesh as a base, constructing a micro-nano structure by a simple solution soaking method, and using polydimethyldiallylammonium chloride-sodium perfluorooctanoate / silica (PDDA-PFO / SiO 2 ) complex for surface modification, the steps are as follows:

[0028] 1) Clean the brass mesh with a pore size of 180 mesh with washing powder, ethanol solution with a concentration of 50 w%, and deionized water for 10 minutes, and dry it in an electric blast drying oven for 1 hour;

[0029] 2) Weigh 0.849 g AgNO under dark conditions 3 Put the powder into 250ml of deionized water, and then ultrasonically oscillate in the ultrasonic tank until it is completely dissolved; use a pipette to take 0.08ml of ammonia water with a concentration of 27w%, and add it dropwise to the AgNO 3 solution, to get AgNO 3 Ammonia solution;

[0030] 3) Put the brass mesh treated in step 1) into the solution for 60s, take it out,...

Embodiment 2

[0041] A preparation method of superhydrophilic and oleophobic omentum, the steps are as follows:

[0042] 1) Clean the brass mesh with a pore size of 180 mesh with washing powder, ethanol solution with a concentration of 50 w%, and deionized water for 5 minutes, and dry it in an electric blast drying oven for 2 hours

[0043] 2) Weigh 0.849 g AgNO under dark conditions 3 Put the powder into 250ml of deionized water, and then ultrasonically oscillate in the ultrasonic tank until it is completely dissolved; use a pipette to take 0.08ml of ammonia water with a concentration of 27w%, and add it dropwise to the AgNO 3 solution, to get AgNO 3 Ammonia solution;

[0044] 3) Put the brass mesh treated in step 1) into the solution for 60s, take it out, and then put it in a 90°C drying oven to dry for 3 hours. 3 It is easy to decompose when exposed to light, so the experiment process should be completely protected from light;

[0045] 4) Add 0.9 g of nano-SiO 2 Particles were ultraso...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Apertureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a super-hydrophilic oleophobic net film. A silver micro-nanometer branch type structure is constructed through a simple solution dipping method with a brass net as a substrate; a poly-dimethyl diallyl ammonium chloride-perfluoro sodium caprylate/silicon dioxide compound is used for modifying the surface to prepare the super-hydrophilic oleophobic net film; the super-hydrophilic oleophobic net film is used for oil water separation. The preparation method of the super-hydrophilic oleophobic net film is simple, and is suitable for industrial production; the super-hydrophilic oleophobic net film is applied in the oil water separation to realize the effect of water penetrating the net film and oil not penetrating the net film, and has a better separation effect on vegetable oil and gasoline; the oil water separation net film has the advantages of easy cleaning, recycling property, good stability and excellent application foreground in the oil water separation.

Description

technical field [0001] The invention belongs to the technical fields of chemistry, chemical engineering and functional materials, in particular to a preparation method of a superhydrophilic and oleophobic omentum and its application in oil-water separation. Background technique [0002] Due to the increasing amount of industrial oily sewage and frequent oil spill accidents, how to efficiently separate oil from water has become an increasingly urgent problem in modern industrial processes and environmental protection. [0003] Based on the wettability of materials, superhydrophobic and superoleophilic films have been successfully prepared. Chinese invention patents CN101708384A, CN101518695, CN1721030A, etc. have reported the oil-water separation omentum with superhydrophobic and super lipophilic functions, but the above-mentioned omentum is not suitable for the separation of oil-water mixture of a small amount of oil in a large amount of water, and it is easy to pollute the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D17/022
Inventor 袁志好姬悄悄杜学丽
Owner TIANJIN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap