PET/PP alloy material and preparation method thereof

A technology of alloy material and compatibilizer, applied in the field of PET/PP alloy material and its preparation, can solve problems such as poor compatibility, and achieve the effects of good flame retardant effect, high impact strength and excellent comprehensive performance

Inactive Publication Date: 2014-04-09
QINGDAO XINZHAN PLASTIC
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PET is a polar polymer, and PP is a non-polar polymer, so the compatibility between the two is poor. Therefore, to improve the performance of the PET / PP alloy, the compatibility problem between the two must be solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A PET / PP alloy material, its components are proportioned by mass percentage: PET 35%, PP 20%, styrene-ethylene-butylene-styrene copolymer grafted maleic anhydride (SEBS-g-MAH) 5%, talcum powder 20%, compound flame retardant 18%, polysiloxane 1.5%, hindered phenol antioxidant 1010 and phosphite antioxidant 168 compound 0.5%, wherein, the The compound flame retardant is a ternary compound composed of 50wt% decabromodiphenyl ether (DBDPO), 25% polyphenylsulfone diphenyl phosphonate and 25% montmorillonite.

[0023] Preparation method: (1) Dry PET and PP at 130°C-150°C for 3-4 hours, and set aside; (2) Weigh 50wt% decabromodiphenyl ether (DBDPO), 25% polyphenylene diphenyl sulfone phosphonate and 25% montmorillonite to mix evenly to prepare a compound flame retardant, then dry at 80°C to 85°C for 30 to 45 minutes, and set aside; (3) Formulate by weight Weigh the dried PET, PC and composite flame retardant, add them into a high-speed mixer and mix them evenly, then add the ...

Embodiment 2

[0025] A PET / PP alloy material, its components are proportioned by mass percentage: PET 35%, PP 35%, polypropylene grafted maleic anhydride (PP-g-MAH) 4%, the surface is treated with silane coupling agent 10% of alkali-free glass fiber, 15% of compound flame retardant, 0.8% of calcium stearate, 0.2% of compound of hindered phenol antioxidant 1076 and phosphite antioxidant 168, wherein, the The compound flame retardant is a ternary compound composed of 50wt% decabromodiphenyl ether (DBDPO), 25% polyphenylsulfone diphenyl phosphonate and 25% montmorillonite.

[0026] Preparation method: (1) Dry PET and PP at 130°C-150°C for 3-4 hours, and set aside; (2) Weigh 50wt% decabromodiphenyl ether (DBDPO), 25% polyphenylene diphenyl sulfone phosphonate and 25% montmorillonite to mix evenly to prepare a compound flame retardant, then dry at 80°C to 85°C for 30 to 45 minutes, and set aside; (3) Formulate by weight Weigh the dried PET, PC and compound flame retardant, add them into the hig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a PET / PP alloy material and a preparation method thereof. The invention discloses a PET / PP alloy material, which is prepared from the following components according to the mass percentage proportions: 20-50% of PET, 20-50% of PP, 3-8% of compatibilizer, 10-30% of reinforcing agent, 15-20% of composite fire retardant, 0.5-2% of lubricant, and 0.1-1% of anti-oxidant. The beneficial effects reside in that: the PET / PP blending alloy material provided by the invention has both advantages of PET and PP, has excellent comprehensive properties; simultaneously, proper amounts of reinforcing agent and composite fire retardant are added, in order to effectively improve mechanical properties and flame retardation performance of the PET / PP alloy material, and make the PET / PP blending alloy material have advantages of high notch impact strength, excellent bendability, and good flame retardation effect; and the PET / PP blending alloy material is widely applied in the fields of automobile, household electrical appliance, toy and machinery, and has a wide application prospect.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PET / PP alloy material and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET) is mainly used in synthetic fibers, biaxially stretched films, and hollow containers. Due to PET's low price, excellent wear resistance, heat resistance, chemical resistance, electrical insulation, molding dimensional stability and high mechanical strength, PET was widely used as an engineering plastic in the 1960s. application. PET for engineering plastics has excellent comprehensive performance and low price, which is very competitive compared with other general engineering plastics. There are rigid groups on the main chain of PET molecules, so its heat resistance is very high, and its electrical properties are also excellent due to the high symmetry of the molecular chain. However, PET also has disadvantages such as slow crystallization speed, d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L23/12C08K13/02C08K3/34C08K3/22C08K13/06C08K9/06C08K7/14C08K5/06B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/911B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 不公告发明人
Owner QINGDAO XINZHAN PLASTIC
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com